Aerogel heat insulation sheet

A technology of aerogel and heat insulation sheet, applied in the direction of adhesives, film/sheet adhesives, adhesive additives, etc., can solve the problem of damage to the system, pollution of automobile products, erosion of powder on the surface of products, etc. problem, to achieve the effect of excellent thermal insulation performance, good adhesion and high strength

Inactive Publication Date: 2018-09-28
王宏宁 +3
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Airgel materials are now widely used in the field of new energy vehicles. The heat insulation sheet made of airgel materials is used as the heat insulation material between batteries, but the existing airgel materials have powder erosion on the surface of the product. In the case of dropping, there is a risk of contamination and system damage to automotive products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aerogel heat insulation sheet
  • Aerogel heat insulation sheet
  • Aerogel heat insulation sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An aerogel heat insulation sheet, comprising an aerogel layer and a glue layer coated on the outer surface of the aerogel layer, the glue layer covering the entire outer surface of the aerogel layer, wherein the aerogel layer The thickness is 0.1mm. The thickness of the glue layer is 0.01 mm. The material of the aerogel layer is silica aerogel. The glue layer is mainly made of the following raw material components in parts by weight: 0.03 part of carbon powder, 0.5 part of glass fiber powder, 0.2 part of tributyl phosphate (flame retardant), and α-cyanoacrylate instant adhesive ( structural adhesive) 4 parts.

[0028] The aerogel insulation sheet is prepared by the following method:

[0029] Step S1, at a temperature of 40 ° C, the following raw material components by weight: 0.03 part of carbon powder, 0.5 part of glass fiber powder, 0.2 part of tributyl phosphate, and 4 parts of α-cyanoacrylate instant adhesive, Add into the reaction kettle and mix and stir evenly...

Embodiment 2

[0036] An aerogel heat insulation sheet, comprising an aerogel layer and a glue layer coated on the outer surface of the aerogel layer, the glue layer covering the entire outer surface of the aerogel layer, wherein the aerogel layer The thickness is 5mm. The thickness of the glue layer is 0.3 mm. The material of the aerogel layer is aluminum oxide aerogel. The glue layer is mainly made of the following raw material components by weight: 0.2 part of carbon powder, 1 part of glass fiber powder, 1 part of tris(dibromopropyl) phosphate (flame retardant), and epoxy acrylate glue (Structural glue) 19 parts.

[0037] The aerogel insulation sheet is prepared by the following method:

[0038] Step S1, at a temperature of 50 ° C, the following raw material components by weight: 0.2 parts of carbon powder, 1 part of glass fiber powder, 1 part of tris(dibromopropyl) phosphate, and 19 parts of epoxy acrylate glue , add it into the reaction kettle and mix and stir evenly to make a mixed...

Embodiment 3

[0045] An aerogel heat insulation sheet, comprising an aerogel layer and a glue layer coated on the outer surface of the aerogel layer, the glue layer covering the entire outer surface of the aerogel layer, wherein the aerogel layer The thickness is 10mm. The thickness of the glue layer is 0.5mm. The material of the aerogel layer is silica aerogel. The glue layer is mainly made of the following raw material components by weight: 0.5 parts of carbon powder, 2 parts of glass fiber powder, 2 parts of magnesium hydroxide (flame retardant), and 20 parts of ethyl acrylate adhesive (structural glue) .

[0046] The aerogel insulation sheet is prepared by the following method:

[0047] Step S1, at a temperature of 50 ° C, the following raw material components in parts by weight: 0.5 parts of carbon powder, 2 parts of glass fiber powder, 2 parts of magnesium hydroxide, and 20 parts of ethyl acrylate adhesive are added to the reaction kettle and mixed. , stir evenly to make mixed glu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an aerogel heat insulation sheet which comprises an aerogel layer and a glue layer coating the outer surface of the aerogel layer; the glue layer covers the whole outer surfaceof the aerogel layer and is prepared from the following raw material components in part by weight: 0.03-1.5 parts of carbon powder, 0.5-5 parts of glass fiber powder, 0.2-5 parts of a flame retardantand 4-35 parts of a structural adhesive. The aerogel heat insulation sheet provided by the invention has the benefits that as the glue layer covers the whole outer surface of the aerogel layer, powderon the surface of an aerogel material is fixed in the glue layer, so that the problem of falling-off of the powder on the surface of the aerogel material is solved. Therefore, the aerogel heat insulation sheet can be applied to the automobile field, and is used as a heat insulation material for an automobile battery, and the problems of pollution and damage to an automobile product due to powderdrop of the aerogel material are effectively solved.

Description

technical field [0001] The invention relates to the technical field of heat insulation, in particular to an aerogel heat insulation sheet. Background technique [0002] Aerogel insulation felt is a material with very good thermal insulation performance at present, which provides new ideas and possibilities for many technical solutions that cannot be achieved by the original traditional thermal insulation materials. Aerogel materials are now widely used in the field of new energy vehicles. The thermal insulation sheets made of aerogel materials are used as thermal insulation materials between batteries. However, the existing aerogel materials have powder erosion on the surface of the product. Drop situation, there is a risk of contamination to automotive products and damage to the system. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to solve the above-mentioned problems, and to provide an aerogel heat insulation sheet, which can effectively sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/30C09J7/20C09J4/02C09J11/04C09J11/06C09J163/10
CPCC09J7/30C09J4/00C09J7/20C09J11/04C09J11/06C09J163/10C09J2400/10C08K3/04C08K7/14C08K5/521
Inventor 王宏宁王贝尔王荣海
Owner 王宏宁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap