Microalloying wear resisting ball and preparation method and preparation system thereof

A technology of microalloying and preparation system, which is applied in the field of metallurgy, can solve the problems of poor production process and unstable hardness of grinding balls, and achieve the effects of good and stable product quality, enhanced wear resistance, and short production cycle

Active Publication Date: 2018-09-28
ZHONGBEI UNIV
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to propose a micro-alloyed wear-resistant ball for the problems of poor production process and unstable hardness of the current grinding ball. The micro-alloyed wear-resistant ball has high strength, high toughness, simple production process and low price. Affordable advantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microalloying wear resisting ball and preparation method and preparation system thereof
  • Microalloying wear resisting ball and preparation method and preparation system thereof
  • Microalloying wear resisting ball and preparation method and preparation system thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] This embodiment discloses a microalloyed wear-resistant ball, and its main chemical composition (mass fraction %) is shown in Table 1.

[0048] Table 1 Chemical composition of microalloyed wear-resistant balls

[0049] C

Si

mn

Cr

B

N

Mg

Ca

P

S

Fe

0.8

0.2

0.68

0.43

0.08

0.02

0.12

0.1

≤0.010

≤0.010

margin

[0050] This embodiment discloses a microalloyed wear-resistant ball preparation system, its structure is as follows Figure 1-2 The shown includes: sequentially connected smelting device, continuous casting and rolling device, induction heating device 2 (intermediate frequency induction heating device), steel ball rolling mill 4, ball sieving device 5 and heat treatment device. The end of the reaction heating section of the induction heating device 2 is provided with an infrared temperature measuring device 3, and the preparation system of the micro-alloyed wear-resistant ball also incl...

Embodiment 2

[0059] This embodiment discloses a microalloyed wear-resistant ball, and its main chemical composition (mass fraction %) is shown in Table 2.

[0060] Table 2 Chemical composition of microalloyed wear-resistant balls

[0061] C

Si

mn

Cr

B

N

Mg

Ca

P

S

Fe

0.75

0.3

0.7

0.45

0.1

0.02

0.12

0.1

≤0.010

≤0.010

margin

[0062] This embodiment discloses a microalloyed wear-resistant ball preparation system, its structure is as follows Figure 1-2 The shown includes: sequentially connected smelting device, continuous casting and rolling device, induction heating device 2 (intermediate frequency induction heating device), steel ball rolling mill 4, ball sieving device 5 and heat treatment device. The end of the reaction heating section of the induction heating device 2 is provided with an infrared temperature measuring device 3, and the preparation system of the micro-alloyed wear-resistant ball also inc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a microalloying wear resisting ball and a preparation method and a preparation system thereof. The microalloying wear resisting ball comprises the following components in percentage by weight: 0.75-0.85% of C, 0.15-0.35% of Si, 0.65-0.75% of Mn, 0.4-0.5% of Cr, 0.05-0.1% of B, 0.01-0.05% of N, 0.01-0.015% of Mg, 0.05-0.15% of Ca, S not more than 0.010%, P not more than 0.015%, and the balance of Fe. The invention further discloses the preparation method of the microalloying wear resisting ball; and the preparation method comprises the steps of induction smelting-continuous casting and rolling of rods-medium-frequency induction heating-inclined rolling and rotary cutting of balls-heat treatment process (quenching+tempering). The microalloying wear resisting ball has the advantages of high strength, high toughness, simple production process and low cost.

Description

technical field [0001] The invention relates to metallurgical technology, in particular to a microalloyed wear-resistant ball, a preparation method and a preparation system thereof. Background technique [0002] With the rapid development of society, natural resources such as energy ores are becoming less and less, the mining environment is getting more and more difficult, and the mining costs are getting higher and higher. How to reduce the consumption and cost of energy mining has become a key point of my country's energy strategy. research focus. In the industrial production of mineral resources, as the abrasive medium of the ball mill, the grinding ball plays a role in crushing and grinding the material in the production process, and its quality and performance directly affect the working efficiency and powder quality of the ball mill. Therefore, the development of high-quality grinding balls is of great significance for improving mining efficiency and reducing mining co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/32C21D1/18C21D9/36B21H1/14B02C17/20
CPCB02C17/20B21H1/14C21D1/18C21D9/36C21D2211/001C21D2211/002C21D2211/004C21D2211/008C22C38/001C22C38/002C22C38/02C22C38/04C22C38/32
Inventor 顾涛赵宇宏徐凤强侯华闫锋徐小龙裴海祥
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap