Flexible anti-cracking putty composition and application thereof

An anti-cracking putty and composition technology, applied in the direction of filling slurry, etc., can solve the problems of application performance limitation, inability to improve indoor environment, and insufficient functionality, and achieve good low-temperature storage stability, reduce radiation hazards, adjust strong wet performance

Inactive Publication Date: 2018-11-27
HEFEI SHANGHAN DECORATION ENG CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of interior wall putty has good physical properties, good flexibility and adhesion to the wall, but its functionality is insufficient, it does not have the ability to improve the indoor environment, and its application performance is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible anti-cracking putty composition and application thereof
  • Flexible anti-cracking putty composition and application thereof
  • Flexible anti-cracking putty composition and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] This embodiment relates to a flexible anti-cracking putty composition and a preparation method thereof, the putty is composed of the following raw materials in parts by weight:

[0058] 24 parts of 325 white cement;

[0059] 20 parts of perovskite tailings powder;

[0060] Coumarone resin 14 parts;

[0061] 10 servings of banana juice;

[0062] 8 parts of bismuth vitrinate powder;

[0063] 16 parts of sea pumice powder;

[0064] 15 parts of mordenite powder;

[0065] 1.5 parts of 2-ethyl-4 methylimidazole;

[0066] 2 parts of tributoxyethyl phosphate;

[0067] 4 parts toughening agent;

[0068] 2 parts of compound coupling agent;

[0069] 1.5 parts of compound water repellent;

[0070] 12 parts of compound rubber powder;

[0071] 30 parts of magnetized water.

[0072] The selection and preparation of the toughening agent, compounded coupling agent, compounded hydrophobic agent and compounded rubber powder in this example are shown in Table 1 below:

[0073] Ta...

Embodiment 2

[0081] This embodiment relates to a flexible anti-cracking putty composition and a preparation method thereof, the putty is composed of the following raw materials in parts by weight:

[0082] Label 325 white cement 26 parts;

[0083] 22 parts of perovskite tailings powder;

[0084] Coumarone resin 16 parts;

[0085] 12 parts of plantain juice;

[0086] 9 parts of bismuth vitrinate powder;

[0087] 18 parts of sea pumice powder;

[0088] 19 parts of mordenite powder;

[0089] 2 parts of 2-ethyl-4 methylimidazole;

[0090] 2.4 parts of tributoxyethyl phosphate;

[0091] 4.5 parts of toughening agent;

[0092] 2.5 parts of compound coupling agent;

[0093] 1.8 parts of compound water repellent;

[0094] 13 parts of compound rubber powder;

[0095] 32 parts of magnetized water.

[0096] The selection and preparation of the toughening agent, compounded coupling agent, compounded hydrophobic agent and compounded rubber powder in this example are shown in Table 2 below: ...

Embodiment 3

[0105] This embodiment relates to a flexible anti-cracking putty composition and a preparation method thereof, the putty is composed of the following raw materials in parts by weight:

[0106] Label 325 white cement 28 parts;

[0107] 23 parts of perovskite tailings powder;

[0108] Coumarone resin 18 parts;

[0109] 13 servings of plantain juice;

[0110] 10 parts of bismuth vitrinate powder;

[0111] 20 parts of sea pumice powder;

[0112] 21 parts of mordenite powder;

[0113] 2.2 parts of 2-ethyl-4 methylimidazole;

[0114] 2.5 parts of tributoxyethyl phosphate;

[0115] 5 parts of toughening agent;

[0116] 2.7 parts of compound coupling agent;

[0117] 2 parts of compound water repellent;

[0118] 14 parts of compound rubber powder;

[0119] 34 parts of magnetized water.

[0120] The selection and preparation of the toughening agent, compounded coupling agent, compounded hydrophobic agent and compounded rubber powder in this example are shown in Table 3 below:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flexible anti-cracking putty composition and application thereof, and relates to the technical field of putty materials. The flexible anti-cracking putty composition comprises white cement with the label of 325, coumarone resin, perovskite tailing powder, bismuth alum acid powder, bryozoatum powder, mordenite powder, banana juice, 2-ethyl-4-methylimidazole, tri-butoxyl ethyl phosphate ester, toughening agents, complex coupling agents, complex water repellents, complex gum powder and magnetized water. The flexible anti-cracking putty composition and the application have the advantages that interior wall putty of the flexible anti-cracking putty composition is obviously enhanced in the aspects of mechanical strength, hydrophobicity, flexibility, purification and humidification capacity, antibacterial property, heat insulation, electromagnetic radiation absorbing ability and the like, accordingly, the flexible anti-cracking putty composition is excellent in integral performance and good in applicability, and the service life can be effectively guaranteed.

Description

technical field [0001] The invention relates to the technical field of interior wall putty, in particular to a flexible anti-crack putty composition. Background technique [0002] Putty is the most commonly used kind of building decoration materials. The main components of traditional putty are talcum powder and glue. Putty, to take a step further, is a kind of base material for leveling the wall, which lays a good foundation for future decoration (painting and wallpaper). Putty is divided into two kinds: putty inside wall and putty on exterior wall. External wall putty can resist wind and sun, so it has good gelation, high strength and low environmental index. The comprehensive index of putty in the inner wall is good, and it is hygienic and environmentally friendly. Therefore, the inner wall is not for external use and the outer wall is not for internal use. Putties are usually based on gypsum or cement, so rough surfaces are easier to bond firmly. However, during const...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 俞克波
Owner HEFEI SHANGHAN DECORATION ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com