Transparent intumescent-type aqueous flame-retardant paint, and preparation method and applications thereof

A kind of flame retardant coating and expansion type technology, applied in the field of environmentally friendly flame retardant coating and its preparation, can solve the problems of limited use range of non-transparent coatings, poor flame retardant effect, etc., achieve obvious internal foam structure, continuous hard charcoal layer , The effect of dense carbon layer structure

Active Publication Date: 2018-11-30
广州诺一新材料有限公司
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems of the release of harmful organic volatiles containing halogen and the high temperature of the dehydration catalyst resulting in poor flame retardant effect and limited application range of non-transparent coatings during the use of existing flame retardant coatings. Provided is a transparent intumescent water-based flame-retardant coating and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent intumescent-type aqueous flame-retardant paint, and preparation method and applications thereof
  • Transparent intumescent-type aqueous flame-retardant paint, and preparation method and applications thereof
  • Transparent intumescent-type aqueous flame-retardant paint, and preparation method and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0037] Specific embodiment 1: The transparent intumescent water-based flame retardant coating of this embodiment is composed of component A, component B and coating additives, and the component A is composed of 12 to 24 parts by weight of carbon forming agent, 20 to 20 parts by weight. It consists of 50 parts of dehydration catalyst, 0-5 parts of melamine, 0-2 parts of glass microspheres and 40-120 parts of water, and component B is amino resin.

specific Embodiment approach 2

[0038] Embodiment 2: This embodiment is different from Embodiment 1 in that the char-forming agent is one or a combination of pentaerythritol, dipentaerythritol, and tripentaerythritol. Other steps and parameters are the same as those in the first embodiment.

specific Embodiment approach 3

[0039] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that the dehydration catalyst is one or a combination of phosphoric acid amidinourea, phosphoric acid amidinourea methylolated derivatives, and phosphoric acid . Other steps and parameters are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-protection transparent intumescent-type aqueous flame-retardant paint, and a preparation method and applications thereof, and belongs to the field of paint. Thepreparation method is used for solving problems in the prior art, that in using process of conventional flame retardant paint, halogen containing toxic organic volatile matters are released, flame retardant effect is poor because of the high dehydration catalyst temperature, and nontransparent paint using range is limited. The environment-protection transparent intumescent-type aqueous flame-retardant paint is composed of a component A, a component B, and a paint auxiliary agent. The preparation method comprises following steps: the component A is prepared; the component B is prepared from melamine formaldehyde resin and / or melamine modified urea-formaldehyde resin; the component A and the component B are mixed, the paint auxiliary agent is added, and an obtained mixture is stirred to be uniform so as to obtain the environment-protection transparent intumescent-type aqueous flame-retardant paint. The environment-protection transparent intumescent-type aqueous flame-retardant paint usedfor flame retardant protection of indoor timber structure materials, wood plastic composite materials, steel structure materials, or concrete structures.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to the technical field of an environmentally friendly flame-retardant coating and its preparation method and application. Background technique [0002] With the improvement of people's living standards and the rapid development of the construction industry, wood and a large number of flammable materials are used in building materials, interior decoration and even wooden house construction, which poses a huge fire safety hazard. The preparation of high-efficiency new non-combustible, flame-retardant, low-toxic and environmentally friendly decorative materials is one of the trends in material development in the future. The flame-retardant coating coated on the surface of the base material can effectively prevent the occurrence and spread of fire, and can significantly reduce the loss caused by fire. It has the advantages of low cost, complex variable use and wide application. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/30C09D5/18C09D7/61
CPCC08K5/06C08K5/34922C08K7/20C09D5/185C09D161/30
Inventor 王奉强李佳朋王清文肖泽芳谢延军张志军刘仕廉
Owner 广州诺一新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com