A method for analyzing the effect of ultrasonic impact treatment on residual stress of metal components formed by laser selective melting

A technology of laser selective melting and ultrasonic impact, which is applied in the field of additive manufacturing, can solve problems such as initial stress and deformation, and achieve the effect of optimizing impact process parameters

Active Publication Date: 2022-08-02
HARBIN ENG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current simulation analysis generally does not consider the influence of initial stress and deformation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for analyzing the effect of ultrasonic impact treatment on residual stress of metal components formed by laser selective melting
  • A method for analyzing the effect of ultrasonic impact treatment on residual stress of metal components formed by laser selective melting
  • A method for analyzing the effect of ultrasonic impact treatment on residual stress of metal components formed by laser selective melting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The present invention will be further described below with reference to the accompanying drawings.

[0027] figure 1 is the finite element mesh division diagram of the impacted member; figure 2 Overall assembly drawing of punch, impact pin and impacted components after meshing; image 3 is the displacement load curve loaded on the punch; Figure 4 The displacement diagram in the transverse direction is cut along the longitudinal section of the center line for the component after laser selective melting and forming; Figure 5 It is the transverse stress distribution after the component is cut along the longitudinal section of the center line after laser selective melting and forming; Image 6 It is the transverse stress distribution after the member is cut along the longitudinal section of the center line after impact treatment; Figure 7 It is the lateral displacement distribution of the member after the impact treatment is cut along the longitudinal section of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of additive manufacturing, and in particular relates to a method for analyzing the influence of ultrasonic impact treatment on residual stress of metal components formed by laser selective melting. First, the finite element software Simufact.Additive is used to simulate the laser selective melting and forming process of an aluminum alloy sheet, and Cool in Simufact.Forming to obtain the distribution of manufacturing residual stress and deformation, and then use Msc.Marc to input the stress and deformation mesh to simulate the ultrasonic impact process on the basis of the residual stress and deformation generated in the laser selective melting forming process. Calculated to analyze the physical process of the effect of the entire ultrasonic impact on the laser selective melting and forming of metal components. The invention uses the Msc.Marc dynamic transient module to simulate the ultrasonic impact, takes the laser selective melting and forming stress field as the initial condition, and the calculation results and the residual stress tester measurement results are in good agreement in terms of numerical value and change trend. In order to optimize the impact process parameters and explore the purpose of its action mechanism.

Description

technical field [0001] The invention belongs to the field of additive manufacturing, and particularly relates to a method for analyzing the influence of ultrasonic impact treatment on residual stress of a metal component formed by laser selective melting. Background technique [0002] Aluminum alloys have good mechanical properties and processing properties, and have the advantages of low density, good corrosion resistance and wear resistance, high strength and stiffness, and strong impact resistance. They are widely used in aerospace, automobile manufacturing, shipbuilding and marine engineering equipment. Applications. The laser selective melting forming processing method can produce components of any shape without being limited by the complexity of the part structure. In recent years, the laser selective melting forming technology of aluminum alloy parts has been more and more applied. [0003] Due to the characteristics of continuous rapid melting and solidification in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G06F30/23G06F111/10G06F119/14G06F113/10
CPCG06F30/23
Inventor 邢晓冬段晓明姜风春周长平王振李鹏苏艳蒋婷婷
Owner HARBIN ENG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap