Wood-plastic composite material added with Chinese fan palm leaf fiber and application thereof

A technology of wood-plastic composite materials and palm leaves, which is applied in the field of wood-plastic profiles, can solve problems such as limitations in applicability, and achieve the effects of wide source of raw materials, low cost, and simple and convenient preparation

Inactive Publication Date: 2019-01-11
HEFEI LONGYANG AGRI TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of wood-plastic composite material has good degradability, lo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wood-plastic composite material added with Chinese fan palm leaf fiber and application thereof
  • Wood-plastic composite material added with Chinese fan palm leaf fiber and application thereof
  • Wood-plastic composite material added with Chinese fan palm leaf fiber and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment relates to a wood-plastic composite material added with palmetto leaf fibers and a preparation method thereof. The wood-plastic composite material is composed of the following raw materials in parts by weight:

[0046] Polyvinyl chloride resin powder SG-472 parts;

[0047] 12 parts of hydroxypropyl methacrylate;

[0048] 34 parts palm leaf fiber;

[0049] 10 parts of niobium yttrium tailings powder;

[0050] 3 parts of nanometer bismuth vanate powders;

[0051] 2 parts of JYM-087B rubber powder;

[0052] 1.5 parts of tributoxyethyl phosphate;

[0053] 1 part of compound dispersant:

[0054] 1 part of compound coupling agent;

[0055] 2 parts of compound foaming agent;

[0056] 1.5 parts of antioxidant antioxidant.

[0057] The selection and preparation of the compound dispersant, compound coupling agent, compound foaming agent and antioxidant anti-aging agent in this embodiment are shown in Table 1 below:

[0058] Table 1

[0059]

[0060] The...

Embodiment 2

[0065] This embodiment relates to a wood-plastic composite material added with palmetto leaf fibers and a preparation method thereof. The wood-plastic composite material is composed of the following raw materials in parts by weight:

[0066] Polyvinyl chloride resin powder SG-476 parts;

[0067] 13 parts of hydroxypropyl methacrylate;

[0068] 36 parts palm leaf fiber;

[0069] 12 parts of niobium yttrium tailings powder;

[0070] 3.5 parts of nanometer bismuth vanate powder;

[0071] JYM-087B rubber powder 2.3 parts;

[0072] 1.7 parts of tributoxyethyl phosphate;

[0073] 1.2 parts of compound dispersant:

[0074] 1.4 parts of compound coupling agent;

[0075] 2.5 parts of compound blowing agent;

[0076] Antioxidant antiaging agent 2 parts.

[0077] The selection and preparation of compound dispersant, compound coupling agent, compound foaming agent and anti-oxidant anti-aging agent in this embodiment are shown in Table 2 below:

[0078] Table 2

[0079]

[008...

Embodiment 3

[0085] This embodiment relates to a wood-plastic composite material added with palmetto leaf fibers and a preparation method thereof. The wood-plastic composite material is composed of the following raw materials in parts by weight:

[0086] Polyvinyl chloride resin powder SG-479 parts;

[0087] 14 parts of hydroxypropyl methacrylate;

[0088] 38 parts palm leaf fiber;

[0089] 13 parts of niobium yttrium tailings powder;

[0090] 4 parts of nanometer bismuth vanate powders;

[0091] JYM-087B rubber powder 2.5 parts;

[0092] 2 parts of tributoxyethyl phosphate;

[0093] 1.6 parts of compound dispersant:

[0094] 1.5 parts of compound coupling agent;

[0095] 2.8 parts of compound blowing agent;

[0096] 2.3 parts of antioxidant antioxidant.

[0097] The selection and preparation of compound dispersant, compound coupling agent, compound foaming agent and anti-oxidant anti-aging agent in this embodiment are shown in Table 3 below:

[0098] table 3

[0099]

[0100]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wood-plastic composite material added with sunflower leaf fiber and an application thereof and relates to the technical field of wood-plastic profiles. The material containsthe following raw materials: polyvinyl chloride resin powder SG-4, hydroxypropyl methacrylate, the Chinese fan palm leaf fiber, niobium yttrium tailing powder, nano bismuth vanadate powder, JYM-087B rubber powder, tributoxyethyl phosphate, compound dispersant, a compound coupling agent, a compound foaming agent and an anti-oxygen anti-aging agent. The wood-plastic composite material disclosed by the invention has the advantages that the mechanical strength, the physical stability, the purification ability, the antibacterial property, the shielding property and the like are remarkably improved;the overall performance is more excellent; the applicability is better; and the service life is more guaranteed.

Description

technical field [0001] The invention relates to the technical field of wood-plastic profiles, in particular to a wood-plastic composite material added with palmetto leaf fibers and an application thereof. Background technique [0002] Wood-plastic profiles, also known as wood-plastic composite materials, are made of wood powder, agricultural straw powder and other plant fibers and plastics as the main raw materials, processed by advanced technology, and the products can be recycled and reused repeatedly. In recent years, with the depletion of global resources, social awareness of environmental protection is increasing. As a brand-new green environmental protection product, wood-plastic composite material is an ecologically clean composite material. Its production raw materials can use various waste plastics, waste wood and agricultural and forestry residues. It helps to slow down the pollution of plastic waste, and also helps to reduce the environmental pollution caused by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L99/00C08K13/02C08K3/24C08K5/5419C08K5/10C08K5/3437C08K5/18C08J9/10C08J9/04
CPCC08J9/0023C08J9/0028C08J9/0042C08J9/0061C08J9/0071C08J9/0085C08J9/0095C08J9/04C08J9/103C08J2203/18C08J2327/06C08J2499/00
Inventor 沈涛
Owner HEFEI LONGYANG AGRI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap