A technology of colored asphalt and composition, applied in the direction of building structure, building components, building insulation materials, etc., can solve the problems of polluting energy consumption, failure to solve the environment, etc., to reduce emissions, solve environmental pollution, service performance and service life improved effect

Inactive Publication Date: 2019-03-22
WUHAN HANYANG MUNICIPAL CONSTR GRP CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is still the problem of segregation between inorganic pigments and asphalt, and the problems of environmental pollution and high energy consumption have not been solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color asphalt composition capsule and preparation method thereof
  • Color asphalt composition capsule and preparation method thereof
  • Color asphalt composition capsule and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A colored asphalt composition capsule is prepared according to the following process steps:

[0025] 1) In terms of parts by mass, weigh 15 parts of inorganic pigments, 50 parts of decolorized pitch, 28.45 parts of slaked lime, 6 parts of organic montmorillonite modified by octadecyl trimethyl quaternary ammonium salt, 0.5 parts of zeolite, and 0.05 parts of water share;

[0026] 2) After heating the decolorized asphalt to a molten state, put it into a container, add inorganic pigments and organic montmorillonite at a temperature of 145°C, and then place it in a high-speed shearing instrument with a rotation speed of 5000r / min. Cut for 45 minutes to obtain the mixture A of "bleached asphalt-inorganic pigment-organic montmorillonite mixed system";

[0027] 3) After adding zeolite and water to the mixture A, place it on a high-speed mixer with a rotating speed of 800r / min, stir for 3min, and obtain the blending system of "decolorized asphalt-inorganic pigment-organic mon...

Embodiment 2

[0046] A colored asphalt composition capsule is prepared according to the following process steps:

[0047]1) In terms of parts by mass, weigh 10 parts of inorganic pigments, 60 parts of decolorized pitch, 25.45 parts of slaked lime, 4 parts of organic montmorillonite modified by octadecyl trimethyl quaternary ammonium salt, 0.5 parts of zeolite, and 0.05 parts of water. share;

[0048] 2) After heating the decolorized asphalt to a molten state, put it into a container, add inorganic pigments and organic montmorillonite at a temperature of 145°C, and then place it in a high-speed shearing instrument with a rotation speed of 5000r / min. Cut for 45 minutes to obtain the mixture A of "bleached asphalt-inorganic pigment-organic montmorillonite mixed system";

[0049] 3) After adding zeolite and water to the mixture A, place it on a high-speed mixer with a rotating speed of 800r / min, stir for 3min, and obtain the blending system of "decolorized asphalt-inorganic pigment-organic mon...

Embodiment 3

[0069] A colored asphalt composition capsule is prepared according to the following process steps:

[0070] 1) In terms of parts by mass, weigh 20 parts of inorganic pigments, 40 parts of decolorized pitch, 31.45 parts of slaked lime, 8 parts of organic montmorillonite modified by octadecyl trimethyl quaternary ammonium salt, 0.5 parts of zeolite, and 0.05 parts of water. share;

[0071] 2) After heating the decolorized asphalt to a molten state, put it into a container, add inorganic pigments and organic montmorillonite at a temperature of 145°C, and then place it in a high-speed shearing instrument with a rotation speed of 5000r / min. Cut for 45 minutes to obtain the mixture A of "bleached asphalt-inorganic pigment-organic montmorillonite mixed system";

[0072] 3) After adding zeolite and water to the mixture A, place it on a high-speed mixer with a rotating speed of 800r / min, stir for 3min, and obtain the blending system of "decolorized asphalt-inorganic pigment-organic mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a color asphalt composition capsule and a preparation method thereof, and belongs to the technical field of a road material. The composition capsule is prepared from the following raw materials in parts by mass through mixing: 10 to 20 parts of inorganic pigment, 40 to 60 parts of decolorized asphalt, 20 to 35 parts of hydrated lime, 4 to 10 parts of organic montmorillonite, 0.5 to 1 part of zeolite and 0.04 to 0.06 part of water, wherein the organic montmorillonite is long-chain quaternary ammonium salt modified organic montmorillonite. Through the compounding of the inorganic pigment, the decolorized asphalt, the hydrated lime, the organic montmorillonite, the zeolite and the water, a color asphalt cementing material product of a capsule structure is prepared; thedifficult problem that the inorganic pigment and the asphalt can easily generate separation is effectively solved; the thermal oxidative aging resistant and ultraviolet aging resistant performance ofthe color asphalt is improved; meanwhile, the release of volatile organic compounds can be inhibited; the problem of environment pollution of the existing color asphalt cementing material is solved;in addition, the liquid state of the color asphalt cementing material can be effectively maintained without energy consumption, so that the energy source consumption in the transportation process is reduced.

Description

technical field [0001] The invention belongs to the technical field of road materials, in particular to a colored asphalt composition capsule and a preparation method thereof Background technique [0002] Colored asphalt pavement refers to the color asphalt concrete pavement with certain strength and function that is formed by mixing and mixing materials such as decolorized asphalt, stones, pigments and additives at a specific temperature to prepare colored asphalt concrete, and then paving and rolling. . In terms of traffic management, colored asphalt pavement can induce traffic and make traffic management more intuitive. Using color to indicate and distinguish road sections or lanes with different functions can improve the driver's alertness and recognition effect, increase road capacity and traffic. Safety. Therefore, colored asphalt pavement can play a greater role in promoting road traffic safety and beautifying the road space environment than ordinary asphalt concret...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08K7/26C08K3/22C08K9/04C08K3/34
CPCC08K3/22C08K3/346C08K7/26C08K9/04C08K2003/2206C08L95/00
Inventor 李立平秦琛易国锋胡颖张裕王林立严涵陈琴
Owner WUHAN HANYANG MUNICIPAL CONSTR GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap