Environment-friendly durable building material

A kind of building material and durable technology, applied in the field of building materials, can solve the problems of insufficient impermeability and frost resistance, and achieve the effect of improving impermeability, compact structure and stable structure

Active Publication Date: 2019-04-05
宁波盈峰新型建材有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to solve the technical problem of insufficient impermeability and frost resistance of building materials in the prior art, and then propose an environmentally friendly and durable building material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly durable building material
  • Environment-friendly durable building material
  • Environment-friendly durable building material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An environmentally friendly and durable building material proposed by the present invention comprises the following raw materials in parts by weight: 100 parts of Portland cement, 30 parts of pozzolan, 300 parts of sand, 5 parts of aggregate, 10 parts of antifreeze, 15 parts of xanthan gum, 2 parts of water reducer, 30 parts of water;

[0027] Described antifreeze is made of antifreeze component A and sodium nitrite, wherein, the mass ratio of antifreeze component A and sodium nitrite in antifreeze is 1:3, and the structural formula of antifreeze component A is as follows:

[0028]

[0029] The mass ratio of the volcanic ash to the xanthan gum is 2:1.

[0030] Its preparation method comprises the following steps:

[0031] S1. Preparation of antifreeze: mix antifreeze component A and sodium nitrite in proportion, and mechanically stir until uniform to obtain antifreeze;

[0032] S2. Prepare raw materials: Weigh each raw material according to 100 parts of Portland ce...

Embodiment 2

[0035] An environmentally friendly and durable building material proposed by the present invention comprises the following raw materials in parts by weight: 100 parts of Portland cement, 36 parts of pozzolan, 350 parts of sand, 8 parts of aggregate, 13 parts of antifreeze, 18 parts of xanthan gum, 3 parts of water reducer, 40 parts of water;

[0036] Described antifreeze is made of antifreeze component A and sodium nitrite, wherein, the mass ratio of antifreeze component A and sodium nitrite in antifreeze is 1:3, and the structural formula of antifreeze component A is as follows:

[0037]

[0038] The mass ratio of the volcanic ash to the xanthan gum is 2:1.

[0039] Its preparation method comprises the following steps:

[0040] S1. Preparation of antifreeze: mix antifreeze component A and sodium nitrite in proportion, and mechanically stir until uniform to obtain antifreeze;

[0041] S2. Prepare raw materials: Weigh each raw material according to 100 parts of Portland ce...

Embodiment 3

[0044] An environmentally friendly and durable building material proposed by the present invention includes the following raw materials in parts by weight: 100 parts of Portland cement, 40 parts of pozzolan, 400 parts of sand, 10 parts of aggregate, 15 parts of antifreeze, 20 parts of xanthan gum, 4 parts of water reducer, 50 parts of water;

[0045] Described antifreeze is made of antifreeze component A and sodium nitrite, wherein, the mass ratio of antifreeze component A and sodium nitrite in antifreeze is 1:3, and the structural formula of antifreeze component A is as follows:

[0046]

[0047] The mass ratio of the volcanic ash to the xanthan gum is 2:1.

[0048] Its preparation method comprises the following steps:

[0049] S1. Preparation of antifreeze: mix antifreeze component A and sodium nitrite in proportion, and mechanically stir until uniform to obtain antifreeze;

[0050] S2. Prepare raw materials: Weigh each raw material according to 100 parts of Portland ce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an environment-friendly durable building material. The environment-friendly durable building material is prepared from the following raw materials in parts by weight: 100 partsof silicate cement, 30 to 40 parts of volcanic ash, 300 to 400 parts of sand grains, 5 to 10 parts of aggregates, 10 to 15 parts of antifreezing agent, 15 to 20 parts of xanthan gum, 2 to 4 parts ofwater reduction agent, and 30 to 50 parts of water. The preparation method comprises the following steps: S1, preparing an antifreezing agent; S2, preparing a raw material; and S3, preparing a building material. The building material provided by the invention is durable, environment-friendly, high in strength, good in anti-seepage performance, high in cohesive force, long in service life, easy intransportation and construction, and short in construction period.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an environmentally friendly and durable building material. Background technique [0002] Building materials refer to the general designation of engineering composite materials that aggregate aggregates into a whole by cementitious materials, and are one of the most frequently used materials in engineering construction. At present, the building materials we use mainly use cement as the cementitious material, add sand and stone as the aggregate, and add a certain proportion of water to stir it. The performance of building materials will directly affect the firmness of buildings, especially the frost resistance and impermeability of building materials. Therefore, the development of building materials is gradually moving towards environmentally friendly and durable mixed concrete. [0003] CN201811243132 proposes a graphite tailings concrete mixture and a preparation meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/04C04B111/76
CPCC04B28/04C04B40/0039C04B2111/76C04B2201/50C04B14/14C04B14/06C04B24/38C04B2103/302C04B2103/601C04B14/02C04B24/04C04B22/085
Inventor 李承坤
Owner 宁波盈峰新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap