Pearl frosted glaze ceramic prepared from waste ceramics and preparation process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of waste ceramics and manufacturing process, which is applied in the field of ceramic manufacturing to achieve unique artistic effects, positive development and high gloss
Active Publication Date: 2019-04-09
FUJIAN QUANZHOU SHUNMEI GROUP
View PDF11 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, there are few reports on the technology of using waste ceramics to make glazes. Therefore, if waste ceramics can be used to prepare glazes with unique effects, it will provide a new application field for the use of waste ceramics.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment 1
[0028] A pearl frosted glaze ceramic prepared from waste ceramics, including a ceramic body and a pearl frosted glaze, the raw materials of the pearl frosted glaze are as follows in parts by weight:
[0030] The pearl frosted glaze prepared by the above-mentioned waste ceramics, the specific steps are as follows:
[0031] Step 1, making a blank, preparing a ceramic blank, trimming and molding the prepared ceramic blank;
[0032]Step 2, making the glaze, crushing the waste ceramics, passing through a 60-mesh sieve, and calcining at 400°C to obtain waste ce...
specific Embodiment 2
[0036] A pearl frosted glaze ceramic prepared from waste ceramics, including a ceramic body and a pearl frosted glaze, the raw materials of the pearl frosted glaze are as follows in parts by weight:
[0037] 21 parts of waste ceramics, 20 parts of low-temperature titanium glaze frit, 16 parts of dolomite, 15 parts of potassiumfeldspar, 7 parts of kaolin, 12 parts of quartz, 2 parts of stalactite, 4 parts of copperoxide, 2 parts of zircon, tricalcium phosphate 1 part; wherein the chemical compositionmass percent of the low-temperature titanium glaze frit is as follows: R 2 O3%, CaO2%, ZnO2%, PbO3%, Al 2 o 3 12%, B 2 o 3 18%, SiO 2 48%, ZrO 2 9%, TiO 2 3%.
[0038] A kind of manufacturing process of pearl frosted glaze ceramics prepared by waste ceramics, making the above pearl frosted glazes prepared by waste ceramics, the specific steps are as follows:
[0039] Step 1, making a blank, preparing a ceramic blank, trimming and molding the prepared ceramic blank;
...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to the technical field of production of ceramics and particularly relates to pearl frosted glazeceramic prepared from waste ceramics and a preparation process thereof. The pearlfrosted glazeceramic prepared from waste ceramics comprises a ceramic blank body and pearl frosted glaze. According to the pearl frosted glaze prepared from the waste ceramics, the raw materials such as the waste ceramics and low-temperature titanium glaze frits are introduced and are used as glaze materials; one-time glazing and one-time firing and molding are achieved; the process problems ofrepeated glazing and repeated firing of the conventional frosted glaze are solved; after the ceramics are fired and molded, the formed bulges are high in frosted texture, high in glaze surface glossiness and special in artistic effect; the pearl frosted glaze is low-temperature fired glaze ceramic; a low-temperature rapid firing process is used; the low-temperature titanium glaze frits are introduced into the glaze materials, the glaze surface is high in glossiness and has pearly glossiness. The pearl frosted glaze ceramic provides a novel field of application of the waste ceramics, has positive significance to promotion of development of ceramic products, and has positive economic benefits.
Description
technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to pearl frosted glaze ceramics prepared from waste ceramics and a manufacturing process thereof. Background technique [0002] With the rapid development of the social economy and the ceramic industry, the output of ceramics has increased significantly. The main raw materials of traditional ceramics are non-renewable natural mineral raw materials. The total amount of natural minerals such as clay, feldspar, and quartz consumed by my country's ceramic industry has reached more than 130 million tons every year, and it is increasing year by year. While the output is soaring, the generation of ceramic waste is also increasing. Because the whole process from raw materialprocessing, mixing, ball milling to green body preparation, forming, drying, etc. will generate waste, including green body waste, waste glaze, semi-finished waste, firing waste, waste gypsum, waste sagge...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More