A special continuous casting mold mold powder for csp medium carbon low alloy and its application

A continuous casting mold and low alloy technology, which is applied in the field of continuous casting mold mold powder for medium carbon and low alloy in CSP, can solve the problem of high crack sensitivity of billet

Active Publication Date: 2021-10-22
XIXIA LONGCHENG METALLURGICAL MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of CSP medium-carbon low-alloy continuous casting mold mold powder and its application, which solves the problem of the high sensitivity of casting slab cracks in the existing multi-element alloy steel, especially for CSP continuous casting. The casting speed is 4-5m / min, which not only requires continuous casting to quickly form the billet shell, but also requires the billet shell not to form cracks. The above-mentioned mold flux provided by the present invention has excellent properties, and can control the heat transfer capacity just right, so that the high-speed medium carbon Continuous casting of low alloy steel proceeds smoothly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A CSP medium-carbon and low-alloy continuous casting mold powder, which includes the following components: CaO, SiO 2 、Al 2 o 3 , Fe 2 o 3 , MgO, Na 2 O, MnO 2 , F - , C, the weight percentages of the above components are respectively: 30.2 parts, 34.4 parts, 2.5 parts, 0.8 parts, 2.0 parts, 7.8 parts, 2.6 parts, 7.1 parts and 5.6 parts.

[0027] The raw materials for the preparation of the above-mentioned CSP medium-carbon and low-alloy continuous casting mold powder include: glass powder, fluorite powder, cement clinker, industrial soda ash, Degussa carbon black, flake graphite powder, wollastonite powder, bentonite, calcite, Magnesia, manganese carbonate, bauxite, binder, the corresponding weight percentages of each raw material are respectively: 9.0 parts, 6.6 parts, 8.2 parts, 5.1 parts, 2 parts, 2.5 parts, 50 parts, 1.5 parts, 3.1 parts, 1.6 copies, 4 copies, 2.9 copies, and 2 copies.

[0028] The binary basicity (CaO / SiO 2 The mass percentage) is 0.88, a...

Embodiment 2

[0032] A CSP medium-carbon and low-alloy continuous casting mold powder, which includes the following components: CaO, SiO 2 、Al 2 o 3 , Fe 2 o 3 , MgO, Na 2 O, MnO 2 , F - , C, the weight percentages of the above components are respectively: 32.1 parts, 33.5 parts, 3.3 parts, 0.9 parts, 1.7 parts, 8.5 parts, 2.6 parts, 7.5 parts and 5.4 parts.

[0033] The raw materials for the preparation of the above-mentioned CSP medium-carbon and low-alloy continuous casting mold powder include: glass powder, fluorite powder, cement clinker, industrial soda ash, Degussa carbon black, flake graphite powder, wollastonite powder, bentonite, calcite, Magnesia, manganese carbonate, bauxite, binder, the weight percentages corresponding to each raw material are respectively: 8.5 parts, 7.1 parts, 8.6 parts, 5.4 parts, 2 parts, 2.5 parts, 48.5 parts, 1.4 parts, 3.6 parts, 1.4 copies, 4 copies, 3.7 copies, and 2 copies.

[0034] The binary basicity (CaO / SiO 2 The mass percentage) is 0.96,...

Embodiment 3

[0038] A CSP medium-carbon and low-alloy continuous casting mold powder, which includes the following components: CaO, SiO 2 、Al 2 o 3 , Fe 2 o 3 , MgO, Na 2 O, MnO 2 , F - , C, the weight percentages are 33.5 parts, 32.5 parts, 4.2 parts, 1.2 parts, 2.4 parts, 10.0 parts, 2.6 parts, 8.1 parts and 5.6 parts respectively.

[0039] The raw materials for the preparation of the above-mentioned CSP medium-carbon and low-alloy continuous casting mold powder include: glass powder, fluorite powder, cement clinker, industrial soda ash, Degussa carbon black, flake graphite powder, wollastonite powder, bentonite, calcite, Magnesia, manganese carbonate, bauxite, binder, the weight percentages corresponding to each raw material are respectively 5.9 parts, 4.6 parts, 9.5 parts, 6.3 parts, 2 parts, 2.4 parts, 47 parts, 1.7 parts, 4.4 parts, 1.5 parts parts, 4 parts, 3.9 parts and 2 parts.

[0040] The binary basicity (CaO / SiO 2 The mass percentage) is 1.03, and the physical indicato...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a special continuous casting mold mold flux for medium-carbon and low-alloy CSP and its application, which comprises the following components in parts by mass: CaO: 29.5-34.5 parts, SiO 2 : 30.5-35 parts, Al 2 o 3 : 2.5‑4.5 parts, Fe 2 o 3 : 0.5‑2.0 parts, MgO: 1.2‑3.5 parts, Na 2 O: 7.5‑11.5 parts, MnO 2 : 1.5‑3.0 parts, F ‑ : 6.5-10 copies, C: 4-7 copies. The above-mentioned mold flux is suitable for CSP continuous casting at a casting speed of 4-5m / min, which not only can realize continuous casting to quickly form a billet shell, but also prevent the billet shell from forming cracks, so that the continuous casting of high-speed medium-carbon and low-alloy steel can proceed smoothly.

Description

technical field [0001] The invention relates to the technical field of mold slag, and in particular to a special continuous casting mold mold slag for medium-carbon and low-alloy CSP and its application. Background technique [0002] At present, the binary alkalinity of mold flux for carbon steel continuous casting mold in conventional CSP is between 1.16-1.22, the melting point is controlled at 1050-1090°C, and the viscosity is controlled at 0.08-0.11Pa.S at 1300°C. The corresponding chemical Component weight percent is CaO: 31.5-35.5 parts, SiO 2 : 26.5-31.5 parts, Al 2 o 3 : 3.0-5.5 parts, Fe 2 o 3 : 0.5-2.2 parts, MgO: 1.0-3.5 parts, Na 2 O: 8.5-12.0 parts, F - : 8.0-11.5 parts, C: 4-6.5 parts. During the use of medium-carbon low-alloy steel, this formula has high crystallization rate, good heat transfer ability, and can effectively solve the problem of cracks on the surface of the slab. However, in medium-carbon low-alloy steel, the liquid steel contains many inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 梁冠冬徐金岩秦教武彭会志赵春宝马帅王希彬
Owner XIXIA LONGCHENG METALLURGICAL MATERIALS CO LTD