Ceramic tile binder, preparation method and using method

A ceramic tile adhesive and timely technology, applied in the direction of construction and building structure, can solve the problems of easy peeling, poor durability, weak adhesion, etc., and achieve the effect of saving material consumption, lasting performance and high construction efficiency

Inactive Publication Date: 2019-07-26
曹磊
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this mortar are weak adhesion, poor durability, and easy peeling off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic tile binder, preparation method and using method
  • Ceramic tile binder, preparation method and using method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A ceramic tile adhesive comprises the following raw materials in parts by weight: 30 parts of high-quality cement, 65 parts of filler, 0.15 part of cellulose ether, and 0.5 part of redispersible rubber powder.

[0030] Further: the filler is quartz sand.

[0031] A preparation method of tile adhesive, the steps are as follows:

[0032] S1. Prepare various raw materials and preparation tools in advance according to the formula, turn on the tank agitator, then prepare according to the formula requirements, and fill in the preparation records in time;

[0033] S2. The order and quantity of chemical raw materials added must be strictly in accordance with the process formula, and should not be changed arbitrarily, and the remaining raw materials in the raw material barrel must be thoroughly cleaned;

[0034] S3. Neatly place it in the designated area. After stirring the binder, notify the quality inspection department to test its solid content;

[0035] S4. During the prep...

Embodiment 2

[0047] A ceramic tile adhesive comprises the following raw materials in parts by weight: 32 parts of high-quality cement, 68 parts of filler, 0.25 part of cellulose ether, and 0.7 part of redispersible rubber powder.

[0048] Further, the filler is river sand.

[0049] A preparation method of tile adhesive, the steps are as follows:

[0050] S1. Prepare various raw materials and preparation tools in advance according to the formula, turn on the tank agitator, then prepare according to the formula requirements, and fill in the preparation records in time;

[0051] S2. The order and quantity of chemical raw materials added must be strictly in accordance with the process formula, and should not be changed arbitrarily, and the remaining raw materials in the raw material barrel must be thoroughly cleaned;

[0052] S3. Neatly place it in the designated area. After stirring the binder, notify the quality inspection department to test its solid content;

[0053] S4. During the prepa...

Embodiment 3

[0065] A ceramic tile adhesive comprises the following raw materials in parts by weight: 35 parts of high-quality cement, 70 parts of filler, 0.35 part of cellulose ether, and 1 part of redispersible rubber powder.

[0066] Further: the filler is any combination of quartz sand, river sand and limestone.

[0067] A preparation method of tile adhesive, the steps are as follows:

[0068] S1. Prepare various raw materials and preparation tools in advance according to the formula, turn on the tank agitator, then prepare according to the formula requirements, and fill in the preparation records in time;

[0069] S2. The order and quantity of chemical raw materials added must be strictly in accordance with the process formula, and should not be changed arbitrarily, and the remaining raw materials in the raw material barrel must be thoroughly cleaned;

[0070] S3. Neatly place it in the designated area. After stirring the binder, notify the quality inspection department to test its s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic tile binder which comprises, by weight, 30-35 parts of high-quality cement, 65-70 parts of filler, 0.15-0.35 part of cellulose ether and 0.5-1 part of redispersible adhesive powder. The ceramic tile binder is a nontoxic, odorless, pollution-free and environment-friendly product which emerges as development of building ceramic tiles require, and has the characteristics of being ultrastrong in binding, high in universality and flexibility, lasting in performance, supportive of fa ade construction, needless to fix, supportive of premixing and environment-friendlyin use; the ceramic tile binder has the advantages of being high in binding strength and construction efficiency and saving in material consumption when in use, and the defects of weak binding force,poor durability, easiness in falling and high construction material consumption when cement is directly used for binding are overcome thoroughly.

Description

technical field [0001] The invention relates to the technical field of tile pasting, in particular to a tile adhesive, a preparation method and a use method. Background technique [0002] The rapid development of architectural ceramics has made a significant contribution to the beautification of cities and home environments. The traditional tile paste method mostly uses cement mortar, which is to mix sand and cement on site to make simple cement mortar, apply this mortar on the back of pre-soaked or pre-wetted tiles, and press the mortar-coated tiles onto the pre-wetted surface on the tile, then tap the tile to ensure a consistent flatness of the tile. The main purpose of this process is to compact the mortar so that the cement particles get inside the porous backing of the tile and into the porous substrate. The disadvantages of this kind of mortar are weak adhesion, poor durability, and easy peeling off. Contents of the invention [0003] The object of the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00E04F21/02
CPCC04B28/00C04B2111/00637E04F21/023C04B14/06C04B24/383C04B2103/0057C04B14/068C04B14/28
Inventor 曹磊
Owner 曹磊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com