Method for making brick powder concrete from waste sintered shale brick powder

A technology of concrete and shale bricks, applied in the field of concrete, can solve problems such as increasing jobs, and achieve the effects of saving resources, improving performance, and reducing environmental pollution

Active Publication Date: 2019-08-23
GUANGXI UNIVERSITY OF TECHNOLOGY +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention can effectively recycle and utilize waste sintered shale brick powder to replace part of cement to produce brick powder concrete. After comparing with ordinary concrete, it is found that the overall performance of brick powder concrete is significantly improved, so as to achieve the purpose of improving its engineering quality and reduce the damage caused by cement. The problem of environmental pollution caused...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making brick powder concrete from waste sintered shale brick powder
  • Method for making brick powder concrete from waste sintered shale brick powder
  • Method for making brick powder concrete from waste sintered shale brick powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The method for making brick powder concrete by using waste sintered shale brick powder comprises the following steps:

[0045] (1) Recycling waste sintered shale bricks, using manual hammering, preliminary crushing, and sorting to remove impurities from waste sintered shale bricks;

[0046] (2) Use a jaw crusher to crush the waste sintered shale bricks after removal of impurities, and dry them after crushing;

[0047] (3) Finely grind the broken waste sintered shale bricks, sieve with a vibrating sieve machine, and dry them in an oven to obtain waste sintered shale brick powder. The fineness of the waste sintered shale brick powder is 0.08 mm;

[0048] (4) In parts by weight, the raw materials used are as follows: 359 parts by weight of cement, 600 parts by weight of medium sand, 1100 parts by weight of stones with a particle size of 18 mm, 190 parts by weight of water, 246 parts by weight of waste sintered shale brick powder 3 parts by weight, 3 parts by weight of ma...

Embodiment 2

[0053] The method for making brick powder concrete by using waste sintered shale brick powder comprises the following steps:

[0054] (1) Recycling waste sintered shale bricks, using manual hammering, preliminary crushing, and sorting to remove impurities from waste sintered shale bricks;

[0055] (2) Use a jaw crusher to crush the waste sintered shale bricks after removal of impurities, and dry them after crushing;

[0056] (3) Finely grind the broken waste sintered shale bricks, sieve with a vibrating sieve machine, and dry them in an oven to obtain waste sintered shale brick powder. The fineness of the waste sintered shale brick powder is 0.10 mm;

[0057] (4) In terms of parts by weight, the raw materials used are as follows: 400 parts by weight of cement, 610 parts by weight of medium sand, 1135 parts by weight of stones with a particle size of 20mm, 200 parts by weight of water, 48 parts by weight of waste sintered shale brick powder Part, 4 parts by weight of magnesiu...

Embodiment 3

[0062] The method for making brick powder concrete by using waste sintered shale brick powder is characterized in that it comprises the following steps:

[0063] (1) Recycling waste sintered shale bricks, using manual hammering, preliminary crushing, and sorting to remove impurities from waste sintered shale bricks;

[0064] (2) Use a jaw crusher to crush the waste sintered shale bricks after removal of impurities, and dry them after crushing;

[0065] (3) Finely grind the broken waste sintered shale bricks, sieve with a vibrating sieve machine, and dry them in an oven to obtain waste sintered shale brick powder. The fineness of the waste sintered shale brick powder is 0.15 mm;

[0066] (4) In parts by weight, the raw materials used are as follows: 445 parts by weight of cement, 620 parts by weight of medium sand, 1185 parts by weight of stones with a particle size of 22mm, 210 parts by weight of water, 96 parts by weight of waste sintered shale brick powder Part, 5 parts by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

A method for making brick powder concrete from waste sintered shale brick powder comprises the following steps: (1) impurity removal; (2) crushing and drying treatment; (3) grinding, sieving and drying treatment for obtaining the waste sintered shale brick powder; (4) weighing of the following raw materials: cement, medium sands, cobblestones, water, the waste sintered shale brick powder, magnesium borate, zirconia, hydroxypropyl methylcellulose, bentonite and mica according to corresponding parts by weight; (5) oscillation stirring of the raw materials with 100-200 Hz ultrasonic waves to obtain a mixed slurry; and (6) molding of the mixed slurry. Sintered shale bricks which are wastes are processed to form the powder, and the powder is used for partially replacing the cement to produce the brick powder concrete, and the integral performances of the brick powder concrete are effectively better than those of ordinary concrete.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a method for making brick powder concrete by using waste sintered shale brick powder. Background technique [0002] Concrete is one of the fundamental materials widely used in the civil engineering industry. According to the statistics of the National Bureau of Statistics, my country's commercial concrete output in 2016 reached 1,792 million cubic meters, an increase of 7.4%, and an increase of 5.4 percentage points year-on-year. With the rapid economic development, the application of concrete is more and more extensive. Every day in our country, old buildings are demolished and new ones rise. As a result, a large amount of construction waste will be generated every day. Abandoned sintered shale bricks account for a large part of construction waste. At the same time, shale brick manufacturers also produce a large number of discarded bricks. These bricks have no reasonable tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B18/16
CPCC04B28/04C04B2201/50C04B18/165C04B14/06C04B14/02C04B14/383C04B24/383C04B14/104C04B14/20Y02W30/91
Inventor 黄榜彪刘灏黄秉章李晓谢伟标王俊云
Owner GUANGXI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap