Transmission electron microscope technology for in-situ study of three-dimensional distribution structure of nanoparticles

A technology of nanoparticle and three-dimensional distribution, which is applied in individual particle analysis, particle and sedimentation analysis, and preparation of test samples. It can solve problems such as poor dispersion, large particle size of metal catalysts, and difficult size control, and achieve high performance. , to avoid the effect of oxidation

Active Publication Date: 2019-09-06
ZHEJIANG UNIV
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the methods for preparing supported catalysts mainly include impregnation-liquid phase reduction method, gas phase reduction method, electrochemical deposition method, gel-sol method, etc. Disadvantages such as poor sex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transmission electron microscope technology for in-situ study of three-dimensional distribution structure of nanoparticles
  • Transmission electron microscope technology for in-situ study of three-dimensional distribution structure of nanoparticles
  • Transmission electron microscope technology for in-situ study of three-dimensional distribution structure of nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] The method for in-situ researching the sintering phenomenon and the three-dimensional distribution of the multi-component alloy nanoparticles loaded on the carbon nanofiber under the action of the electric field under the transmission electron microscope comprises the following steps:

[0064] 1. In order to obtain carbon nanofibers, we use the method of electrospinning. in accordance with figure 1 The schematic diagram of electrospinning shown in the figure shows that before spinning, polyacrylonitrile (PAN) and dimethylformamide (DMF) are mixed according to a certain ratio to form a polymer solution and then loaded into the injector. Then place a substrate for carrying carbon nanofibers at a suitable position on the receiving screen directly opposite the injection port. Choose copper foil or carbon paper as the substrate, but according to experimental experience, due to the relatively high strength of copper foil compared with carbon paper, and weaker bonding with ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a transmission electron microscope technology for in-situ study of a three-dimensional distribution structure of nanoparticles. The transmission electron microscope technologyis characterized by comprising the steps of: acquiring carbon nanofibers after carbonization treatment by adopting an electrospinning technique and thermal treatment; loading precursor salt of alloy on the carbon nanofibers; assembling a metal needle tip into a sample rod fixing end of a transmission electron microscope, the carbon nanofibers are loaded with a gold needle platform, and a gold needle is arranged on the movable end of a sample rod; the sample rod loaded with the metal needle tip and the gold needle is inserted into the transmission electron microscope, the height and position ofthe gold needle at the movable end of the sample rod are adjusted, such that the carbon nanofibers on the gold needle platform are in contact with the metal needle tip, a certain voltage is applied within certain instantaneous time, so that the precursor salt loaded on the carbon nanofibers on gold needle platform undergoes an instantaneous carbothermic reaction to form alloy nanoparticles, and the distribution variations and sintering situations of the alloy nanoparticles under the action of a current field are observed; and two-dimensional projection transmission electron microscope pictures are photographed, the electron microscope pictures are subjected to alignment, three-dimensional reconstruction and visualization by means of software.

Description

technical field [0001] The invention relates to a transmission electron microscope technology, in particular to a method for in-situ research on the three-dimensional distribution of multi-component alloy nanoparticles under the action of an electric field under the transmission electron microscope. [0002] technical background [0003] Fossil energy has always been the basis for human survival and supports the rapid development of modern society. But as we all know, fossil energy is a non-renewable energy. With the increasing demand for energy in human society, the international energy situation is becoming increasingly severe. The exhaustion of energy and the environmental pollution caused by the use of fossil energy have attracted widespread attention from all over the world. In order to solve the dual problems of non-renewability and environmental pollution brought about by traditional fossil energy, human demand for new energy is increasing. For example, renewable and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N15/10G01N1/28
CPCG01N1/28G01N15/10
Inventor 王宏涛梁春园褚雯张奕志刘嘉斌
Owner ZHEJIANG UNIV
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com