PVC artificial leather and preparation method thereof as well as car seat containing PVC artificial leather

An artificial leather and temperature control technology, applied in the field of automotive interior materials, can solve the problems of wear resistance, poor air permeability, easy wear and tear, and achieve the effect of high strength residual, environmental protection, and wear resistance.

Inactive Publication Date: 2019-10-25
DONGFENG MOTOR CORP HUBEI
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing automotive interior material market, PVC artificial leather is only widely used in the epidermis of seat accessories due to poor wear res

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC artificial leather and preparation method thereof as well as car seat containing PVC artificial leather
  • PVC artificial leather and preparation method thereof as well as car seat containing PVC artificial leather
  • PVC artificial leather and preparation method thereof as well as car seat containing PVC artificial leather

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Example 1:

[0039] The PVC artificial leather of this embodiment includes a base cloth layer 1, a PVC adhesive layer 2, a PVC foam layer 3, a PVC dense layer 4, and a surface layer 5 arranged from bottom to top. The above-mentioned preparation method of PVC artificial leather includes The following steps:

[0040] 1) Material preparation: configure PVC adhesive layer slurry, PVC foam layer slurry, PVC dense layer slurry, adhesive layer slurry, and surface coating slurry according to the formula, select the base cloth and release paper according to the product needs, and use the base cloth 3D high-density base fabric with an areal density of 280g / m 2 , Two-way breaking strength≥900N / 5cm, breaking elongation≥120%;

[0041] The preparation method of the PVC adhesive layer slurry is specifically: weighing 100 parts of polyvinyl chloride (K value 55), 55 parts of plasticizer (plasticizer 911), and 1 part of calcium zinc stabilizer in parts by weight. , 1 part of AC foaming agent...

Example Embodiment

[0066] Example 2:

[0067] The PVC artificial leather of this embodiment includes a base cloth layer 1, a PVC adhesive layer 2, a PVC foam layer 3, a PVC dense layer 4, and a surface layer 5 arranged from bottom to top. The above-mentioned preparation method of PVC artificial leather includes The following steps:

[0068] 1) Material preparation: configure PVC adhesive layer slurry, PVC foam layer slurry, PVC dense layer slurry, adhesive layer slurry, and surface coating slurry according to the formula, select the base cloth and release paper according to the product needs, and use the base cloth 3D high-density base fabric with an areal density of 340g / m 2 , Two-way breaking strength≥900N / 5cm, breaking elongation≥120%;

[0069] The preparation method of the PVC adhesive layer slurry is specifically: weighing 100 parts of polyvinyl chloride (K value 65), 75 parts of plasticizer (plasticizer 911), 2.5 parts of calcium zinc stabilizer in parts by weight , 2 parts of AC foaming agent,...

Example Embodiment

[0095] Example 3:

[0096] The PVC artificial leather of this embodiment includes a base cloth layer 1, a PVC adhesive layer 2, a PVC foam layer 3, a PVC dense layer 4, and a surface layer 5 arranged from bottom to top. The above-mentioned preparation method of PVC artificial leather includes The following steps:

[0097] 1) Material preparation: configure PVC adhesive layer slurry, PVC foam layer slurry, PVC dense layer slurry, adhesive layer slurry, and surface coating slurry according to the formula, select the base cloth and release paper according to the product needs, and use the base cloth 3D high-density base fabric with an areal density of 400g / m 2 , Two-way breaking strength≥900N / 5cm, breaking elongation≥120%;

[0098] The preparation method of the PVC adhesive layer slurry is specifically as follows: weigh 100 parts of polyvinyl chloride (K value 75), 90 parts of plasticizer (plasticizer DPHP), and 5 parts of calcium zinc stabilizer in parts by weight. , 3 parts of AC fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Areal densityaaaaaaaaaa
Areal densityaaaaaaaaaa
Areal densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses PVC artificial leather and a preparation method thereof as well as a car seat containing the PVC artificial leather. The PVC artificial leather comprises a base fabric layer, aPVC adhesive layer, a PVC foaming layer, a PVC dense layer and a surface layer which are arranged in order from bottom to top; the PVC adhesive layer is prepared from the following raw materials in parts by weight: 100 parts of polyvinyl chloride, 55-90 parts of a plasticizer, 1-5 parts of a calcium-zinc stabilizer and 1-3 parts of an AC foaming agent. The PVC artificial leather provided by the invention not only meets the technical standards of ordinary PVC leather, but also has the advantages of high wear resistance, environmental protection, and relatively high residual strength after punching, and meets the increasingly stringent requirements of the industry environmental protection regulations.

Description

technical field [0001] The invention relates to the technical field of automobile interior materials, in particular to a PVC artificial leather, a preparation method thereof, and an automobile seat containing the PVC artificial leather. Background technique [0002] At present, with the development of the economy, the demand for automobiles has further expanded, and at the same time, most consumers have further improved requirements for automobile quality and cost performance. Therefore, the competition among major OEMs is becoming more and more fierce, and the pressure to reduce costs is increasing. It has become a trend to use high-performance PVC leather to replace genuine leather on the A side of the seat, and to use microfiber materials to reduce costs. As an important visual part of the car, the car seat covered with PVC artificial leather is widely concerned by consumers for its mechanical properties, environmental protection performance and durability. [0003] For ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00D06N3/06
CPCD06N3/0043D06N3/0097D06N3/06D06N2209/105D06N2211/263D06N2211/28
Inventor 李彬黄江玲付丹熊芬胡玉洁谢德钰
Owner DONGFENG MOTOR CORP HUBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap