Method for quickly predicting dry density, moisture content and water absorption of air-entrained concrete

A technology of air-entrained concrete and water absorption, which is applied in the field of building materials, can solve the problems of high heating temperature, dry density, inaccurate moisture content and water absorption, long processing time, etc., and achieve the effect of simple testing process

Active Publication Date: 2021-04-27
HOHAI UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this test method requires multiple heating treatments, each treatment takes a long time, and the heating temperature is high, which will cause irreversible damage to the internal structure of the air-entrained concrete, so the measured dry density, moisture content and Water absorption is also not accurate
In addition, the structure of the test piece is damaged during the test, and the test piece cannot be used in actual engineering after the test, resulting in waste of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for quickly predicting dry density, moisture content and water absorption of air-entrained concrete
  • Method for quickly predicting dry density, moisture content and water absorption of air-entrained concrete
  • Method for quickly predicting dry density, moisture content and water absorption of air-entrained concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A certain batch of air-entrained concrete is measured according to the method for rapidly predicting the dry density of the air-entrained concrete, the moisture content and the water absorption rate after leaving the kettle provided by the present invention.

[0035] The measurement results are as follows:

[0036] The calculation results when a=1.8 are shown in the table below:

[0037]

[0038] The calculation results when a=2.0 are shown in the table below:

[0039]

[0040] The calculation results when a=2.2 are shown in the table below:

[0041]

[0042] Based on the above data, the dry density of the air-entrained concrete, the water content and water absorption after leaving the kettle are shown in the following table:

[0043]

[0044] According to GB / T11969-2008 "Autoclaved Air-entrained Concrete Performance Test Method", the dry density, water content and water absorption of the air-entrained concrete specimens were measured.

[0045] The measur...

Embodiment 2

[0051] Another batch of air-entrained concrete was measured according to the method for quickly predicting the dry density of air-entrained concrete, water content and water absorption rate after exiting the kettle, and the measurement results are as follows:

[0052] The calculation results when a=1.8 are shown in the table below:

[0053]

[0054] The calculation results when a=2.0 are shown in the table below:

[0055]

[0056] The calculation results when a=2.2 are shown in the table below:

[0057]

[0058] Based on the above data, the dry density of the air-entrained concrete, the water content and water absorption after leaving the kettle are shown in the following table:

[0059]

[0060] According to GB / T11969-2008 "Autoclaved Air-entrained Concrete Performance Test Method", the dry density, water content and water absorption of the air-entrained concrete specimens were measured. The measurement results are shown in the table below:

[0061]

[0062] F...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for rapidly predicting the dry density, water content and water absorption rate of aerated concrete, belonging to the field of new building materials. This method realizes the rapid prediction of the dry density of the aerated concrete, the water content and water absorption rate of the aerated concrete by measuring the volume and mass of the aerated concrete test block just out of the kettle and the mass of the test block when it reaches saturated water absorption, and solves the problem of The problem of long time-consuming and complicated process of standard test method provides a new method for product quality management and construction quality control.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a method for quickly predicting the dry density, water content and water absorption rate of aerated concrete. Background technique [0002] Dry density, moisture content and water absorption are important technical indicators of aerated concrete, which directly affect the strength, impermeability, carbonation resistance, shrinkage and deformation of aerated concrete. [0003] At present, the dry density, moisture content and water absorption of air-entrained concrete are mainly tested according to the methods given in GB / T11969-2008 "Methods for Performance Test of Autoclaved Air-entrained Concrete". Specifically, put the test piece in an electric blast drying oven, keep it warm at (60±5)°C for 24h, then keep it at (80±5)°C for 24h, and then bake it at (105±5)°C until constant mass . After the test piece is cooled to room temperature, put it into a consta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N5/02G01N9/36G01N9/02
CPCG01N5/025G01N9/02G01N9/36G01N2009/024
Inventor 蒋亚清潘亭宏孟凡旭王玉黄鹤
Owner HOHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com