Car brake pad mixed with aloe fiber powder and preparation method thereof

An aloe vera fiber and brake pad technology, applied in chemical instruments and methods, friction linings, mechanical equipment, etc., can solve problems such as the strength and stability of brake pads that cannot be effectively solved and affect the uniformity of mixing, and achieve stable, Improve overall performance, improve performance

Active Publication Date: 2016-12-07
言璟检测科技(江苏)有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] For example, the publication number is CN 103423345 A, which discloses a kind of automobile brake pad mixed with bamboo fiber. Natural bamboo fiber is added to the brake pad formula, and bamboo fiber is used as a renewable resource, which can be degraded naturally, and the decomposition product is non-toxic and harmless. Excellent friction performance and other characteristics, effectively reduce the noise and vibration of the brake pads during the braking process, and are environmentally friendly, but the fibers generate static electricity and agglomerates during high-speed stirring, which affects the uniformity of mixing and the strength and stability of the brake pads, etc. problem, still cannot be effectively resolved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Car brake pad mixed with aloe fiber powder and preparation method thereof
  • Car brake pad mixed with aloe fiber powder and preparation method thereof
  • Car brake pad mixed with aloe fiber powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Embodiment 1: at first select the raw material of following each component by weight:

[0057]

[0058] Put each raw material into a high-speed mixer with a stirring speed of 650r / min until the raw materials are evenly stirred; using the hot pressing process, pour the mixed raw materials into a mold, and press and solidify them on a hot press machine. The pressure setting is 30MPa, the hot-pressing temperature is 150°C, and the hot-pressing time is 10min; the hot-pressed brake pads are sent to the holding furnace for heat treatment, the furnace temperature is kept at 100°C, and the holding time is 6h to obtain the aloe fiber powder mixed with Car brake pads.

Embodiment 2

[0059] Embodiment 2: at first select the raw material of following each component by weight part:

[0060]

[0061] Put each raw material into a high-speed mixer with a stirring speed of 700r / min until the raw materials are evenly stirred; using the hot pressing method, pour the mixed raw materials into a mold, and heat and solidify them on a hot press machine. The pressure setting is 50MPa, the hot-pressing temperature is 170°C, and the hot-pressing time is 15min; the hot-pressed brake pad is sent to a holding furnace for heat treatment, and the furnace temperature is maintained at 200°C, and the holding time is 10h to obtain the aloe fiber powder mixed with Car brake pads.

Embodiment 3

[0062] Embodiment 3: first select the raw material of following each component by weight part:

[0063]

[0064]

[0065] Put each raw material into a high-speed mixer with a stirring speed of 680r / min until the raw materials are evenly stirred; using the hot pressing process, pour the mixed raw materials into a mold, and heat and solidify them on the hot press. The pressure setting is 40MPa, the hot-pressing temperature is 160°C, and the hot-pressing time is 12min; the hot-pressed brake pads are sent to a holding furnace for heat treatment, the furnace temperature is kept at 150°C, and the holding time is 8h to obtain the aloe fiber powder mixed with Car brake pads.

[0066] Table 1 shows the friction and wear performance comparison results between the car brake pad mixed with aloe fiber powder of the present invention and the existing brake pad.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a car brake pad doped with aloe fiber powder. The car brake pad comprises, by weight, 10 parts to 30 parts of dewaxing aloe fiber powder, 6 parts to 12 parts of cashew nut shell oil modified phenolic resin, 6 parts to 12 parts of butadiene-acrylonitrile rubber powder, 13 parts to 25 parts of conditioning agents and 30 parts to 60 parts of filling agents. According to the invention, the aloe fiber powder is used as a reinforcing material and can be well bonded with phenolic resin and padding; aloe fibers can be directly carbonized at the temperature of about 300 DEG C, and an internal structure of friction materials cannot be damaged, so that friction performance is kept stable, and the performance of braking can be greatly improved. When friction heating reaches a certain degree, substances formed by decomposing friction material surfaces can form a layer of even and tough carbonized membrane which is not prone to falling off, so that relative stability of friction coefficients can be ensured to the greatest extent, and meanwhile, heat fading temperature of the materials can be improved to a certain degree.

Description

technical field [0001] The invention relates to the technical field of a friction material for car braking, in particular to a car brake pad mixed with aloe fiber powder and a preparation method thereof. Background technique [0002] Friction material is a kind of material that realizes the transmission, braking, speed control and steering of mechanical equipment by using the friction force generated between it and its counterpart. It is widely used in braking and transmission devices of various vehicles and mechanical equipment Among them, it is one of the most important functional materials of various power machinery, and its performance is directly related to the reliability of the machine and the safety of people's lives. Automobile friction material is the main application field of friction material, which mainly includes two categories: clutch face and brake pad. The automobile industry is the main pillar industry in my country and the world, and with the development ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): F16D69/00C09K3/14
Inventor 王占红周青青侯贵华何文平王雨新
Owner 言璟检测科技(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap