Polypropylene composition with low shrinkage at wide application temperature range

A polypropylene composition and the technology of the composition are applied in the field of polypropylene compositions with low shrinkage rate in a wide application temperature range, and can solve the problems of difficulty in reducing shrinkage rate, impact strength and shrinkage rate, etc.

Active Publication Date: 2020-04-17
BOREALIS AG
View PDF21 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this creates a dilemma between impact strength and shrinkage, as it is difficult to reduce shrinkage without sacrificing impact strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composition with low shrinkage at wide application temperature range
  • Polypropylene composition with low shrinkage at wide application temperature range
  • Polypropylene composition with low shrinkage at wide application temperature range

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0320] The invention will now be described in more detail by the examples provided below.

[0321] example

[0322] 1. Definition / measurement method

[0323] Unless otherwise defined, the following definitions of terms and measurement methods apply to the above general description of the invention as well as to the following examples.

[0324] Melting temperature T m , crystallization temperature T c It is measured on 5 to 10 mg samples according to ISO 11357-1 using a Mettler TA820 Differential Scanning Calorimeter (DSC). Crystallization and melting curves were obtained during 10°C / min cooling and heating scans between 30°C and 225°C. Melting and crystallization temperatures are endothermic and exothermic peaks.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present application relates to a polypropylene composition having a melt flow rate MFR.2 (230 DEG C) measured according to ISO 1133 in the range of 5 to 50 g / 10min, to a composition comprising thepolypropylene composition and one or more additive(s) in an amount of up to 4 wt.-%, based on the total weight of the composition, to a process for the preparation of the polypropylene composition and an article comprising the polypropylene composition as well as the use of the polypropylene composition for decreasing the brittle-to-ductile transition temperature.

Description

technical field [0001] The present application relates to a polypropylene composition having a melt flow rate MFR measured according to ISO 1133 in the range of 5 to 50 g / 10min 2 (230°C), relating to a composition comprising a polypropylene composition and one or more additives in an amount of up to 4% by weight based on the total weight of the composition, relating to a method for preparing a polypropylene composition A method and an article comprising the polypropylene composition and the use of the polypropylene composition for lowering the brittle-ductile transition temperature. Background technique [0002] Polypropylenes are used in a variety of applications such as the preferred material in automotive applications as they can be tailored to the specific application required. In automotive applications it is particularly desirable to provide low shrinkage during processing combined with a wide application temperature range. Conventional heterophasic polypropylene pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F210/16C08L23/16
CPCC08F210/16C08L2205/025C08L2207/02C08L23/12C08F210/06C08F2500/12C08F2500/17C08L23/16C08F4/65927C08F2/001C08F210/02C08L2201/00C08F2500/37C08L2314/06C08F2500/33C08F2500/34
Inventor 马库斯·加莱特纳克劳斯·贝恩赖特纳王静波
Owner BOREALIS AG
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com