Wormwood or mint extract modified polyamide fiber and preparation method thereof

A technology of mint extract and nylon fiber, which is applied in the textile field, can solve the problems of affecting the antibacterial performance of finished fibers, affecting the performance of fiber mechanics, and reducing the antibacterial performance of wormwood or mint fibers, so as to achieve uniform performance and reduce yarn shrinkage , Improve the effect of antibacterial rate

Inactive Publication Date: 2020-06-05
BESTEE MATERIAL (TSINGTAO) CO LTD
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Peppermint contains flavonoids, phenols, alcohols and organic acids. Directly exposing mint to strong acid, strong alkali and high temperature for spinning will easily decompose the active ingredients in it, which greatly affects the antibacterial properties of the finished fiber
[0005] The modification...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wormwood or mint extract modified polyamide fiber and preparation method thereof
  • Wormwood or mint extract modified polyamide fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The modified nylon fiber of the wormwood extract of the present embodiment, first, the wormwood extract is modified, and the modified method includes the following steps:

[0037] (1) Take an appropriate amount of water and heat it to 55°C, add the wormwood extract, the mass ratio of water to wormwood extract is 1:12, stir and dissolve evenly to obtain a mixed solution, the bath ratio is 1:14;

[0038] (2) Add montmorillonite and zeolite powder to the mixed solution, the total mass ratio of wormwood extract to montmorillonite and zeolite powder is 1:6, and the mass ratio of montmorillonite and zeolite powder is 1 : 1, stirring and mixing evenly, the stirring speed is 30r / min, and the stirring time is 100min to obtain the modified nanocomposite material containing the wormwood extract.

[0039] The preparation method of the wormwood extract modified nylon fiber of the present embodiment comprises the steps:

[0040] (a) Preparation of functional masterbatch: sequentiall...

Embodiment 2

[0043] A kind of peppermint extract modified nylon fiber of the present embodiment, at first, carry out modification treatment to peppermint extract, the method for modification comprises the following steps:

[0044] (1) Take an appropriate amount of water and heat it to 60°C, add the peppermint extract, the mass ratio of water to peppermint extract is 1:15, stir and dissolve evenly to obtain a mixed solution, the bath ratio is 1:15;

[0045] (2) Porous nano-TiO 2 Microspheres and zeolite powder are added to the mixed solution, peppermint extract and porous nano TiO 2 The mass ratio of the microspheres was 1:7.5, and the mixture was uniformly stirred, the stirring speed was 45r / min, and the stirring time was 70min to obtain a modified nanocomposite material containing peppermint extract.

[0046] The preparation method of the peppermint extract modified nylon fiber of the present embodiment may further comprise the steps:

[0047](a) Preparation of functional masterbatch: s...

Embodiment 3

[0050] A kind of mugwort extract modified nylon fiber of the present embodiment, first, carry out modification treatment to mugwort extract, the modification method comprises the following steps:

[0051] (1) Take an appropriate amount of water and heat it to 65°C, add the wormwood extract, the mass ratio of water to wormwood extract is 1:18, stir and dissolve evenly to obtain a mixed solution, the bath ratio is 1:18;

[0052] (2) Porous nano-SiO 2 Microspheres are added to the mixed solution, and the wormwood extract and porous nano-SiO 2 The mass ratio of the microspheres was 1:9, and the mixture was uniformly stirred, the stirring speed was 60r / min, and the stirring time was 40min, to obtain a modified nanocomposite material containing wormwood extract.

[0053] The preparation method of the wormwood extract modified nylon fiber of the present embodiment comprises the steps:

[0054] (a) Preparation of functional masterbatch: slice 100kg of nylon 66, 0.3kg of zinc stearat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a wormwood or mint extract modified polyamide fiber and a preparation method thereof. The wormwood or mint extract accounts for 0.1-5mass% of the wormwood or mint extract modified polyamide fiber. According to the preparation method, the wormwood or mint extract and a nano-porous material are mixed and subjected to modification treatment firstly; the nano-porous material has a relatively large specific surface area, and the wormwood or mint extract are packaged in the pore channels of the porous material, so that in the later fiber synthesis, materials in the wormwoodor mint extract can be protected from damage, thereby improving the bacteriostasis rate, the mechanical property and the like; and the wormwood or mint extract is subjected to modified treatment to obtain the modified nano composite material used for preparing the functional master batch, and then spinning is performed, so that uniform mixing is ensured, and the prepared wormwood or mint extract modified polyamide fiber is uniform in performance.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a wormwood or peppermint extract modified nylon fiber and a preparation method thereof. Background technique [0002] The existing conventional viscose fiber is the largest type of regenerated cellulose fiber. The fiber and its follow-up fabric have good moisture absorption and air permeability, and the characteristics of comfortable wearing have always been favored by people. With the development of society, people pay more attention to fabrics. Functional requirements are getting higher and higher. [0003] Wormwood is a perennial herb. The leaves of wormwood are used as medicine. It is warm in nature, bitter in taste, non-toxic, pure in nature, clears the twelve meridians, restores yang, regulates qi and blood, expels dampness and cold, stops bleeding and relieves miscarriage, etc. Efficacy, also commonly used in acupuncture. Wormwood has the specific function o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/90D01F1/10C08J3/22
CPCC08J3/226C08J2377/02C08J2377/06C08J2477/02C08J2477/06D01F1/103D01F6/90
Inventor 黄效华伏广伟姜义军郑天勇穆伟华刘潇甄丽刘彦明
Owner BESTEE MATERIAL (TSINGTAO) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap