Vinyl chloride polymer and method for preparing same

A vinyl chloride polymer and vinyl chloride polymerization technology, applied in the field of vinyl chloride polymer and its preparation, can solve the problems of low polymerization productivity, fish eyes and deterioration of initial coloring performance, and achieve low melt viscosity, fish eyes quality and The effect of improving the quality of initial coloring performance and shortening the polymerization reaction time

Active Publication Date: 2020-09-04
LG CHEM LTD
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] An aspect of the present invention provides a method for producing a vinyl chloride polymer, which has excellent processability while solving the problems of low polymerization productivity and fish problems due to undissolved particles of reactants when producing vinyl chloride polymers. Problems with degradation of eye and initial coloring performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vinyl chloride polymer and method for preparing same
  • Vinyl chloride polymer and method for preparing same
  • Vinyl chloride polymer and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0060] A method of preparing a vinyl chloride polymer according to an embodiment of the present invention may include stirring the above-prepared reaction mixture, and suspension polymerization may be performed by stirring.

[0061] In addition, if necessary, the method for preparing vinyl chloride polymer according to one embodiment of the present invention may also include sodium bicarbonate (NaHCO 3 ), sodium borate (Na 2 B 4 o 7 ), disodium hydrogen phosphate (Na 2 HPO 4 ), sodium carbonate (Na 2 CO 3 ), Potassium dihydrogen phosphate (KH 2 PO 4 ), ammonium hydroxide (NH 4 OH), potassium tartrate (KHC 4 h 4 o 6 ), potassium hydrogen phthalate (KHC 8 h 4 o 4 ) and calcium hydroxide (Ca(OH) 2 ) in any one or a mixture of two or more as a hydrogen ion concentration control agent.

[0062] In addition, the method for preparing a vinyl chloride polymer according to one embodiment of the present invention may further include diallyl maleate (DAM), diallyl phthala...

Embodiment 1

[0082] The internal volume is 0.2m 3 90kg of deionized water, 45g of hydroxy-dimethylbutyl peroxide, 60g of hydration degree of 80% and a viscosity of 30cps in a 4% aqueous solution at room temperature were introduced into the reactor (pre-polymerization reactor) Polyvinyl alcohol, 40 g of polyvinyl alcohol with a hydration degree of 40% and a viscosity of 20 cps in a 4% aqueous solution at room temperature. After the vacuum was applied, 75 kg of vinyl chloride monomer was introduced into the reactor, and the polymerization temperature was raised to 62° C. to perform a polymerization reaction. Afterwards, when the polymerization conversion rate reaches 13% (13±2%), all the prepared vinyl chloride polymerization seeds and unreacted monomers are transferred to the main polymerization reactor. At this time, the polymerization conversion was measured by gas chromatography using a butane tracer. Under predetermined polymerization conditions, whenever each polymerization condition...

Embodiment 2

[0086] In addition to raising the polymerization temperature of the pre-polymerization reactor to 67°C for polymerization, and controlling the polymerization temperature of the main polymerization reactor to 56°C for polymerization, then when the pressure of the polymerization reactor reaches 6.3kgf / cm 2 (when the polymerization conversion rate was 84% ​​(84±2%)), except that the polymerization reaction was terminated, a vinyl chloride polymer was obtained in the same manner as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a vinyl chloride polymer and a method for preparing same and, more specifically, to a vinyl chloride polymer of which the polydispersity index is 2.0 to 2.3 and the porosity is 60% or higher, and a method for preparing the vinyl chloride polymer. More particularly, in the method for preparing the vinyl chloride polymer, a vinyl chloride polymerization seed having aconversion rate of 5 to 20% is first prepared by means of prepolymerization, and then a vinyl chloride monomer is input to the vinyl chloride polymerization seed and a vinyl chloride polymer is polymerized (main polymerization), wherein the temperature differential between the prepolymerization and the main polymerization is adjusted to 5 to 15 DEG C. The preparation method has the advantage of increasing polymerization productivity. The vinyl chloride polymer polymerized by means of the preparation method shows said physical properties and thus has the advantages of enhancing the fish eye quality and initial coloration as well as enabling excellent processability.

Description

technical field [0001] Cross References to Related Applications [0002] This application claims Korean Patent Application No.10-2018-0049563 filed with the Korean Intellectual Property Office on April 30, 2018 and Korean Patent Application No.10-2019 filed with the Korean Intellectual Property Office on April 25, 2019 -0048264, the disclosures of both patent applications are hereby incorporated by reference in their entirety. technical field [0003] The present invention relates to a vinyl chloride polymer having excellent processability and improved fisheye and initial coloring properties, and a method for producing a vinyl chloride polymer having improved polymerization productivity. Background technique [0004] Vinyl chloride polymers are inexpensive while having an excellent mass balance, and therefore are used in a wide range of fields such as hard materials and soft materials. Specifically, in the rigid field, vinyl chloride polymers are used for pipes, films...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F14/06C08F114/06C08F2/18
CPCC08F14/06C08F114/06C08F2/001C08F2/18C08L27/06C08F2500/03C08F2500/24
Inventor 安晟镕金健地李世雄朱镇爀河玄圭
Owner LG CHEM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap