A kind of preparation method of golden film

A thin film and golden technology, which is applied in the field of preparation of golden thin films, can solve the problems of difficult to achieve ideal golden appearance, low surface gloss, reddish color, etc., and achieve the effect of pure color, high gloss and good antibacterial effect

Active Publication Date: 2022-02-18
JOMOO KITCHEN & BATHROOM
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing aluminum alloy products using the two-acid process are oxidized into a gold film, the surface gloss of the product is low (the surface gloss of the golden yellow sample is less than 150), and the color is reddish, it is difficult to achieve the ideal golden appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of golden film
  • A kind of preparation method of golden film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation method step of the golden thin film of embodiment 1 is:

[0026] 1. Speed ​​gradient mechanical polishing

[0027] ① Perform low-speed mechanical polishing on the surface of the aluminum alloy blank workpiece, the speed is 1000r / min, and the time is 5min;

[0028] ②Then perform medium-speed mechanical polishing on the workpiece after low-speed polishing, the speed is 2000r / min, and the time is 10min;

[0029] ③Finally, perform high-speed mechanical polishing on the workpiece after medium-speed polishing, with a rotation speed of 3000r / min and a time of 15 minutes;

[0030] Through the setting of gradient mechanical polishing, as the rotation speed and polishing time increase, the oxide film naturally formed on the surface of the aluminum alloy substrate will be gradually peeled off, and the roughness of the substrate surface will become smaller and smaller, which can effectively improve the surface gloss of the film .

[0031] 2. Degreasing treatment ...

Embodiment 2

[0052] The preparation method of the golden thin film of Example 2 is basically the same as that of Example 1, the difference is that in the gold dyeing process, the dyeing time is changed, and the dyeing time is 15 minutes.

Embodiment 3

[0054] The preparation method of the golden thin film of Example 3 is basically the same as that of Example 1, the difference is that in the gold dyeing process, the dyeing time is changed, and the dyeing time is 20 minutes.

[0055] The obtained golden thin film is evenly formed, and the copper particles are dispersed and distributed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a golden thin film. The aluminum alloy workpiece is sequentially subjected to mechanical polishing, chemical polishing, anodic oxidation treatment, alternating current electrolytic dyeing treatment and hole sealing treatment, wherein the alternating current electrolytic dyeing treatment is multiple times of rising voltage gradient. Dyeing treatment, the dye solution contains Alizarin Yellow R 0.3-0.8g / L, Alizarin Red S 0.5-1.2g / L, potassium permanganate 4-7g / L, sulfuric acid 20-25g / L and copper chloride 3- 5g / L. The present invention adopts the multiple dyeing process of voltage gradient rise and the dye solution containing copper ions to adjust the color of the dyed layer to obtain a golden oxide film with pure color, uniform color and high gloss, and has better antibacterial effect, comprehensive Good performance.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment, in particular to a method for preparing a golden thin film. Background technique [0002] Aluminum alloy substrates have the characteristics of low cost, light weight, and easy processing, and are widely used in kitchen, bathroom, home, construction and other industries, such as aluminum alloy frames for shower rooms, aluminum alloy door handles, and aluminum alloy pendants. Aluminum alloy oxidation technology has been reported in related patents. For example, in patent CN 104152969 B, aluminum alloy parts with porous oxide film are obtained by direct current electrolysis in sulfuric acid medium after degreasing and oxidation film removal; (AgNO 3 、CuSO 4 etc.), and finally the hot water is sealed to obtain a golden yellow aluminum alloy antibacterial material. [0003] Most of the existing aluminum alloy products using the two-acid process are oxidized into a gold film, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D11/22C25D11/16C25D11/08
CPCC25D11/22C25D11/16C25D11/08
Inventor 林孝发林孝山刘小龙王汉春李日红
Owner JOMOO KITCHEN & BATHROOM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com