Steel wire surface treatment process

A surface treatment and wire technology, applied in metal material coating process, hot dip plating process, surface polishing machine tools, etc. Deal with problems such as low efficiency, achieve the effect of thorough cleaning, save labor costs, and avoid manual cleaning

Pending Publication Date: 2021-03-02
德清县豪鹰金属制品有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing steel wire rod surface treatment process has poor effect, and cannot handle the oil stain and rust on the steel wire rod surface well. The surface treatment efficiency of the steel wire rod is low, which greatly affects the later coating or spraying effect, and at the same time makes the quality of the steel wire rod better. less than guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The invention provides a surface treatment process for steel wire, which specifically includes the following steps:

[0029] Step 1. One-time hot water cleaning: Put the steel wire into the container, then add the hot water at 80°C-90°C, add hydrocarbon cleaning agent, soak for 3-5 hours, and put one end of the steel wire through the sleeve after soaking There is a cleaning cloth inside the sleeve, the cleaning cloth wraps the steel wire, the sleeve is installed firmly with a clamp and a positioning device, the steel wire passes through one end of the sleeve, and then fixed on the roller, driven by a motor The roller rotates to clean off the oil stain on the outer surface of the steel wire, and then rinse it again with clean water;

[0030] Step 2, one-time mechanical polishing treatment: the steel wire cleaned in step 1 is processed by polishing method, and one end of the steel wire is passed between the two brush rollers, and the two brush rollers are driven by the mo...

Embodiment 2

[0041] The invention provides a surface treatment process for steel wire, which specifically includes the following steps:

[0042] Step 1. One-time hot water cleaning: Put the steel wire into the container, then add the hot water at 80°C-90°C, add hydrocarbon cleaning agent, soak for 3-5 hours, and put one end of the steel wire through the sleeve after soaking There is a cleaning cloth inside the sleeve, the cleaning cloth wraps the steel wire, the sleeve is installed firmly with a clamp and a positioning device, the steel wire passes through one end of the sleeve, and then fixed on the roller, driven by a motor The roller rotates to clean off the oil stain on the outer surface of the steel wire, and then rinse it again with clean water;

[0043] Step 2, one-time mechanical polishing treatment: the steel wire cleaned in step 1 is processed by polishing method, and one end of the steel wire is passed between the two brush rollers, and the two brush rollers are driven by the mo...

Embodiment 3

[0054] The invention provides a surface treatment process for steel wire, which specifically includes the following steps:

[0055] Step 1. One-time hot water cleaning: Put the steel wire into the container, then add the hot water at 80°C-90°C, add hydrocarbon cleaning agent, soak for 3-5 hours, and put one end of the steel wire through the sleeve after soaking There is a cleaning cloth inside the sleeve, the cleaning cloth wraps the steel wire, the sleeve is installed firmly with a clamp and a positioning device, the steel wire passes through one end of the sleeve, and then fixed on the roller, driven by a motor The roller rotates to clean off the oil stain on the outer surface of the steel wire, and then rinse it again with clean water;

[0056] Step 2, one-time mechanical polishing treatment: the steel wire cleaned in step 1 is processed by polishing method, and one end of the steel wire is passed between the two brush rollers, and the two brush rollers are driven by the mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a steel wire surface treatment process, and particularly relates to the technical field of steel wires. The steel wire surface treatment process comprises the following steps that step 1, primary hot water cleaning is carried out, specifically, a steel wire is put into a container, adding-into hot water of 80 DEG C-90 DEG C is carried out, a hydrocarbon cleaning agent is added, soaking is carried out for 3-5 hours, and one end of the steel wire is enabled to penetrate through a sleeve after soaking; and cleaning cloth is arranged in the sleeve, the steel wire is wrappedby the cleaning cloth, the sleeve is firmly installed through a clamp and a positioning device, the steel wire penetrates through one end of the sleeve and then is fixed to a roller, a motor is usedfor driving the roller to rotate, oil stains on the outer surface of the steel wire are cleaned away, and then clean water is used for flushing again. After the steel wire is subjected to surface treatment, the steel wire is cleaner and brighter, the cleaning effect is thorough, a very good foundation is laid for later plating or spraying, the steel wire surface treatment efficiency is improved, and the quality of the steel wire is guaranteed.

Description

technical field [0001] The invention belongs to the technical field of steel wires, in particular to a surface treatment process for steel wires. Background technique [0002] Steel wire is one of the four types of steel plate, tube, profile and wire. It is a reprocessed product made of hot-rolled wire rod through cold drawing. Wire rod is the smallest cross-sectional size of hot-rolled section steel. In my country, the hot-rolled round steel supplied in coils with a diameter of 5-9 mm and a total of eight specifications is called wire rod. Wire rod is also called wire rod because it is delivered in coils. The concept of wire rod in foreign countries is slightly different from that in my country. There are other shapes besides circular cross-section, and its diameter is inconsistent due to different demand conditions and production technology levels. According to different rolling mills, it can be divided into two types: high-speed wire rod (high wire) and ordinary wire ro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/08C23G1/06C23C2/02C23C2/06C23C2/38B24B1/00B24B29/08B24B27/033B24B9/04B24B47/12B24B41/00
CPCC23G1/08C23G1/068C23G1/065C23G1/066C23C2/02C23C2/06C23C2/38B24B1/00B24B29/08B24B29/005B24B27/033B24B9/04B24B47/12B24B41/005
Inventor 于永忠
Owner 德清县豪鹰金属制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap