Waterproof, breathable and bacteriostatic compound non-woven fabric and preparation method and application thereof

A waterproof, breathable, non-woven technology, applied in textiles and papermaking, non-woven fabrics, rayon manufacturing, etc. Effect

Inactive Publication Date: 2021-03-02
广州扬新科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to overcome the defects and deficiencies of the existing disposable sanitary products such as poor waterproof and breathable properties and unsatisfactory antibacterial properties, and provide a waterproof and breathable composite non-woven fabric and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof, breathable and bacteriostatic compound non-woven fabric and preparation method and application thereof
  • Waterproof, breathable and bacteriostatic compound non-woven fabric and preparation method and application thereof
  • Waterproof, breathable and bacteriostatic compound non-woven fabric and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A preparation method of a waterproof and breathable composite non-woven fabric. First, polyacrylonitrile, polyvinylidene fluoride, fillers, and water-soluble porogen are mixed and melted, and then sprayed out through a spinneret, air-drawn, formed into a web, and hot-pressed. Bonding, water immersion to remove the porogen, namely the composite non-woven fabric; wherein, the filler is prepared by the following method:

[0043] (1) earlier take zinc acetate, sodium tripolyphosphate, sodium hydroxide and porous tourmaline as raw material to make zinc oxide-tourmaline complex through solid phase reaction;

[0044] (2) Carry out epoxy modification to zinc oxide-tourmaline complex body then, then react with amino-terminated fluoropolymer, obtain modified complex body;

[0045] (3) Finally, immerse the modified complex in 1-allyl-3-methylimidazolium tetrafluoroborate for surface modification to obtain the filler.

[0046] The mass ratio of polyacrylonitrile, polyvinylidene fl...

Embodiment 2

[0063] A preparation method of a waterproof and breathable composite non-woven fabric. First, polyacrylonitrile, polyvinylidene fluoride, fillers, and water-soluble porogen are mixed and melted, and then sprayed out through a spinneret, air-drawn, formed into a web, and hot-pressed. Bonding, water immersion to remove the porogen, namely the composite non-woven fabric; wherein, the filler is prepared by the following method:

[0064] (1) earlier take zinc acetate, sodium tripolyphosphate, sodium hydroxide and porous tourmaline as raw material to make zinc oxide-tourmaline complex through solid phase reaction;

[0065] (2) Carry out epoxy modification to zinc oxide-tourmaline complex body then, then react with amino-terminated fluoropolymer, obtain modified complex body;

[0066] (3) Finally, immerse the modified complex in 1-allyl-3-methylimidazolium tetrafluoroborate for surface modification to obtain the filler.

[0067] The mass ratio of polyacrylonitrile, polyvinylidene fl...

Embodiment 3

[0084] A preparation method of a waterproof and breathable composite non-woven fabric. First, polyacrylonitrile, polyvinylidene fluoride, fillers, and water-soluble porogen are mixed and melted, and then sprayed out through a spinneret, air-drawn, formed into a web, and hot-pressed. Bonding, water immersion to remove the porogen, namely the composite non-woven fabric; wherein, the filler is prepared by the following method:

[0085] (1) earlier take zinc acetate, sodium tripolyphosphate, sodium hydroxide and porous tourmaline as raw material to make zinc oxide-tourmaline complex through solid phase reaction;

[0086] (2) Carry out epoxy modification to zinc oxide-tourmaline complex body then, then react with amino-terminated fluoropolymer, obtain modified complex body;

[0087] (3) Finally, immerse the modified complex in 1-allyl-3-methylimidazolium tetrafluoroborate for surface modification to obtain the filler.

[0088] The mass ratio of polyacrylonitrile, polyvinylidene fl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of non-woven fabric products and in particular relates to a waterproof, breathable and bacteriostatic compound non-woven fabric and a preparation method and application thereof. The preparation method comprises the following steps of mixing and fusing polyacrylonitrile, polyvinylidene fluoride, stuffing and a water soluble pore-foaming agent; and then carrying out spraying by a spinneret plate, air flow drafting, net forming, hot-pressing bonding and water leaching to remove the pore-foaming agent to obtain the waterproof, breathable and bacteriostatic compound non-woven fabric, wherein the stuffing is prepared from raw materials: a zinc oxide- tourmaline compound, an amine-terminated fluorine-containing polymer and 1-allyl-1-3-methylimidazole tetrafluoroborate. The non-woven fabric has good waterproof and breathable properties and is excellent in antibacterial property.

Description

technical field [0001] The invention belongs to the technical field of non-woven fabric products. More specifically, it relates to a waterproof, breathable and antibacterial composite nonwoven fabric, its preparation method and application. Background technique [0002] With the improvement of living standards, people's demand for disposable sanitary products such as baby diapers, adult diapers, and women's sanitary napkins is getting higher and higher, and their requirements for comfort and product quality are also getting higher and higher. [0003] Users of these disposable hygiene products include vulnerable groups such as infants, bedridden adults, and menstruating women. If the air permeability of sanitary products is not good, the skin of vulnerable people wrapped in sanitary products or in contact with the sanitary products for a long time will be in a humid environment for a long time, redness and rash may occur in mild cases, and mild or severe skin rashes may occ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/541D04H1/558D04H3/147D01F1/08D01F1/10D01F8/06D01F8/08
CPCD01F1/08D01F1/103D01F8/06D01F8/08D04H1/541D04H1/558D04H3/147D10B2401/021D10B2401/13
Inventor 黎扬程
Owner 广州扬新科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap