Superalloy regulator and preparation method thereof

A high-temperature alloy and regulator technology, used in weapon accessories, offensive equipment, etc., can solve the problems of less than 8,000 rounds of service life and low service life, and achieve the effect of improving mechanical performance, improving service life and improving mechanical performance.

Active Publication Date: 2021-08-13
BEIJING CISRI GAONA TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the regulators of automatic rifles are mostly made of Cr-plated steel, and their service life does not exceed 8,000 rounds, which is relatively low and cannot meet the requirements of personnel in this field for the service life of regulators.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Superalloy regulator and preparation method thereof
  • Superalloy regulator and preparation method thereof
  • Superalloy regulator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-35

[0063] Examples 1-35 respectively provide the preparation methods of superalloy regulators.

[0064] The preparation method of the superalloy regulator specifically comprises the following steps:

[0065] (1) Electrode casting: use vacuum induction melting technology to cast superalloy to form electrodes;

[0066] (2) Preparation of superalloy powder: using an argon atomization process to make the electrode prepared in step (1) into superalloy powder;

[0067] (3) Preparation of feeding material: uniformly mixing the superalloy powder and binder obtained in step (2) to form feeding material;

[0068] (4) Injection molding: the feeding material prepared in step (3) is placed in a powder injection molding machine, and injected into the mold cavity to form an injection blank;

[0069] (5) catalytic degreasing: carry out nitric acid catalytic degreasing to the injection base that step (4) makes, form the degreasing base;

[0070] (6) Sintering: sintering the degreased body prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of automatic rifle regulators, in particular to a superalloy regulator and a preparation method thereof. The preparation method comprises the following steps: casting of an electrode, wherein the casting temperature is 1400-1500 DEG C; preparation of superalloy powder; preparation of a feed: uniformly mixing the superalloy powder and a binder to form the feed; injection molding: injecting the feed into a mold cavity to form an injection blank; catalytic debinding: carrying out nitric acid catalytic debinding on the injection blank to form a debound blank; sintering: sintering the debound blank in a vacuum environment or a protective atmosphere to obtain a sintered blank, wherein the sintering temperature is 1150-1300 DEG C, and the heat preservation time is 3-6 hours; and heat preservation and pressure maintaining: placing the sintered blank in a high-temperature and high-pressure environment, and carrying out heat preservation and pressure maintaining treatment, wherein the treatment time is greater than 3 hours. The invention also provides the regulator prepared by the preparation method. The service life of the regulator prepared by the preparation method is remarkably prolonged.

Description

technical field [0001] The present application relates to the technical field of automatic rifle regulators, and more specifically, it relates to a superalloy regulator and a preparation method thereof. Background technique [0002] Common ways for automatic rifles to be automatic include recoil and gas-guided. Among them, the automatic mode of the gas-guided type is to push the piston by shunting part of the gunpowder gas to realize automaticity. In the gas-guided automatic rifle, the part used to adjust the amount of diverted gas is a regulator, and the regulator is provided with a regulating hole for the passage of gunpowder gas. [0003] During the use of automatic rifles, the adjustment hole on the regulator will not only be washed by high temperature, high pressure and high speed brought by the gunpowder combustion airflow, but also be chemically corroded by various gas components in the gunpowder airflow. The regulator is different from the barrel. The barrel is rep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F5/00B22F9/14B22F3/10B22F3/22F41A35/00
CPCB22F5/00B22F9/14B22F3/225B22F3/1025B22F3/1007F41A35/00
Inventor 张亚玮张世霄毛赞惠李开松胥国华
Owner BEIJING CISRI GAONA TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products