Preparation method of fragrant color paste blasting bead capable of forming film after drying
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A color paste and blasting bead technology, applied in coatings, art coatings, alginic acid coatings, etc., can solve problems such as poor aesthetics and poor color paste interest, achieve convenient fragrance preservation, satisfy interest and entertainment, guarantee aesthetic effect
Inactive Publication Date: 2021-10-22
劳坤仪
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] Aiming at the deficiencies of the prior art, the present invention provides a method for preparing scented color pastes that can form a film after drying, which solves the problems that the existing color pastes are less interesting in use and less aesthetically pleasing after painting
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] The embodiment of the present invention provides a method for preparing scented color paste beads that can form a film after drying, including an internal phase slurry and an external phase slurry. The raw materials of the internal phase slurry include: 5.0% thickener, 5.0% calcium salt %, acrylate polymer 5.0%, humectant 5.0%, preservative 2.0%, acid-base regulator 5.0%, color paste 10%, essence 8.0%, pearlescent powder 10.0%, purified water 45.0%;
[0031] The raw materials of the external phase slurry include: 90.0% of pure water, 5.0% of sodium alginate, 2.0% of carrageenan, 2.0% of chitosan and 1.0% of preservative.
[0032] The preparation method of described internal phase slurry, comprises the following steps:
[0033] S1. Heating and stirring
[0034] Put 3 / 4 of the pure water into the mixing tank, heat the pure water to 65°C, and stir the mixing tank at a speed of 100r / min, and evenly add the thickener xanthan into the mixing tank while stirring Glue, so tha...
Embodiment 2
[0049] The embodiment of the present invention provides a method for preparing scented color paste beads that can form a film after drying, including an internal phase slurry and an external phase slurry. The raw materials of the internal phase slurry include: thickener 8.0%, calcium salt 8.0% %, 8.0% acrylate polymer, 8.0% humectant, 4.0% preservative, 8.0% acid-base regulator, 20% color paste, 10.0% essence, 15.0% pearlescent powder, 95.0% purified water;
[0050] The raw materials of the external phase slurry include: 99.0% of pure water, 10.0% of sodium alginate, 3.0% of carrageenan, 3.0% of chitosan and 3.0% of preservative.
[0051] The preparation method of described internal phase slurry, comprises the following steps:
[0052] S1. Heating and stirring
[0053] Put 3 / 4 of the pure water into the mixing tank, heat the pure water to 60°C, and stir the mixing tank at a speed of 50r / min. While stirring, add the thickener xanthogen evenly into the mixing tank Glue, so tha...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides a preparation method of a fragrant color paste blasting bead capable of forming a film after drying, and relates to the technical field of blasting bead production. According to the color paste blasting bead preparation method, the blasting bead comprises inner phase slurry and outer phase slurry, the inner phase slurry comprise the following raw materials: a thickening agent, calcium salt, an acrylate polymer, a humectant, a preservative, an acid-base regulator, color paste, essence, pearlescent shimmering powder and purified water, and the outer phase slurry comprise the following raw materials: purified water, sodium alginate, carrageenan, chitosan and a preservative. By means of the essence, the color paste, the acrylate polymer and the pearlescent shimmering powder, fragrance is conveniently kept, the entertainment interestingness is increased, an internal phase material body can be used for painting through a writing brush after paste explosion, a color film can be formed after drying, the attractiveness after painting is guaranteed, the forms of color paste products can be enriched, the interestingness and entertainment of consumers are met, meanwhile, the storage form of the water-based color paste can be improved, and the blasting beadis worthy of vigorous popularization.
Description
technical field [0001] The invention relates to the technical field of popping beads production, in particular to a method for preparing popping beads with fragrance and color paste capable of forming a film after drying. Background technique [0002] Explosive beads are also called fragrant pills, brittle capsules, and beads. Explosive beads are large and small, with a diameter of more than 2.6mm. They are crushable beads. When crushed, they have the feeling of bursting. Wrapped in a film, when painting is required, the outer film is squeezed to allow the wrapped color paste to break out of the film to meet the needs of painting and coloring. [0003] At present, the existing color pastes for painting are less fun to use, and the color paste cannot form a color film after drying, resulting in poor aesthetics after painting, and the stability and moisturizing performance of the color paste products during transportation are poor . Contents of the invention [0004] (1) S...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.