Aluminum alloy chromate-free passivation agent containing fluorescent agent as well as preparation method and use method of aluminum alloy chromate-free passivation agent

A chromium-free passivation and aluminum alloy technology, applied in the coating process of metal materials, etc., can solve problems such as failure to meet customer requirements, difficulty in online identification, and damage to aluminum products, and meet the requirements of production equipment and production technology. Simple, adhesion-enhancing effect

Pending Publication Date: 2022-07-22
安徽光铧帝业化学有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Colorless conversion coatings are not easy to identify online during on-site application, and it is difficult to judge whether the upper film of the chromium-free conversion coating is complete or not, and whether there are defective areas on the upper film by visual observation. Even if there are some identification methods, it is a very localized judgment. And it will also cause damage to aluminum products (such as high-temperature calcination after cutting and sampling or dripping of acid arsine (Ⅲ) color developer)
Although the yellow conversion film is easy to identify online, for some scenes involving painting, especially for aluminum products using transparent lacquer, transparent powder or light-colored paint, it may cause color difference in appearance, thus failing to meet customer requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy chromate-free passivation agent containing fluorescent agent as well as preparation method and use method of aluminum alloy chromate-free passivation agent
  • Aluminum alloy chromate-free passivation agent containing fluorescent agent as well as preparation method and use method of aluminum alloy chromate-free passivation agent
  • Aluminum alloy chromate-free passivation agent containing fluorescent agent as well as preparation method and use method of aluminum alloy chromate-free passivation agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An aluminum alloy chromium-free passivation agent containing a fluorescent agent contains the following components:

[0031] paint remover ingredients weight percentage Deionized water 74% Hydrofluoric acid 5% Basic zirconium carbonate 2% Optical Brightener BBU 5% water-based acrylic resin 10% Sodium Gluconate 3% Triethanolamine 1%

[0032] The preparation method of above-mentioned embodiment 1 chromium-free passivation agent comprises the steps:

[0033] First dissolve hydrofluoric acid in deionized water to form an acid base solution, then add basic zirconium carbonate, optical brightener BBU, water-based acrylic resin, sodium gluconate and triethanolamine in sequence, and stir to completely dissolve all components to obtain the Described chromium-free passivation agent.

[0034] The using method of above-mentioned embodiment 1 chromium-free passivation agent, may further comprise the steps:

[0035] (1) Afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminum alloy chromate-free passivation agent containing a fluorescent agent as well as a preparation method and a use method of the aluminum alloy chromate-free passivation agent, and belongs to the field of metal surface treatment. The invention discloses an aluminum alloy chromium-free passivation agent containing a fluorescent agent. The aluminum alloy chromium-free passivation agent comprises the following components in percentage by weight: 30%-90% of deionized water, 1%-10% of inorganic acid, 1%-10% of a film-forming main agent, 1%-10% of the fluorescent agent, 1%-10% of an accelerant, 1%-10% of a complexing agent and 1%-10% of a corrosion inhibitor.

Description

technical field [0001] The invention relates to the field of metal surface treatment, in particular to an aluminum alloy chromium-free passivation agent containing a fluorescent agent and a preparation method and use method thereof. Background technique [0002] As one of the light metal materials, aluminum alloy is widely used in aerospace, transportation, construction, metal packaging and 3C electronics due to its low density, high strength, good corrosion resistance, mechanical properties and processing properties. Wide range of applications. Passivation treatment is an effective chemical treatment method to improve the anti-corrosion performance of aluminum alloys. It can form a dense protective layer of conversion coating on the surface of aluminum materials, greatly delaying the electrochemical corrosion rate of aluminum alloys, and at the same time, it can also be used for aluminum alloys. Provides excellent adhesion with subsequent coatings. The traditional aluminu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/34C23C22/56C23C22/40C23C22/44C23C22/46
CPCC23C22/34C23C22/56C23C22/40C23C22/44C23C22/46C23C2222/20
Inventor 苏云鹤于赫男胡发青杨雨霖
Owner 安徽光铧帝业化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products