Zirconium corundum refractory ball

A zirconium corundum, refractory ball technology, applied in the field of metallurgy, can solve the problems of furnace shutdown, ball replacement, prone to pulverization, broken balls, bonding, poor thermal shock stability, etc.

Inactive Publication Date: 2007-01-24
郑州豫兴氮氧结合耐火材料有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In use, the balls are naturally piled up to form a curved airflow channel to achieve heat exchange. However, due to the high porosity, low bulk density, low strength, and poor thermal shock stability of this refractory ball, it is easy to appear in use. Problems such as pulverization, broken balls, and bonding reduce the air flow channel and lower the air supply temperature, which eventually lead to frequent shutdowns, ball replacements, and overhauls; due to its small heat storage, it can only be used at 450m 3 Use on hot blast stove above blast furnace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zirconium corundum refractory ball

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0005] The specific implementation of the present invention will be described in detail below in conjunction with specific conditions and process flow diagrams. Given by the technical scheme and process flow chart, the refractory ball of the present invention is calculated by weight percentage: corundum 75-80%, α-Al 2 o 3 5-10%, zircon concentrate 8-15%, clay powder (bonding agent) 5-8%, and the above-mentioned corundum, α-Al 2 o 3 It is made with 3-5% lignin solution based on the total weight of zircon concentrate and clay powder, wherein the corundum and lignin solution are first wet-milled and stirred, and then zircon concentrate and α-Al are added 2 o 3 , after stirring, add clay powder and grind evenly (the above is generally called mixed rolling), after being pressed into a spherical shape by a molding machine, it is dried in a drying furnace (residual water content 2 o 3 80-85% and ZrO 2 5-10%, refractoriness greater than 1790°C, load softening start temperature ab...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

A refractory zirconium corundum sphere for the air heater of blast furnace is proportionally prepared from conundum, alpha-Al2O3, zircon concentrate, clay powder and lignin solution through mixing, grinding, baking and sintering.

Description

1. Technical field [0001] The invention relates to metallurgical technology, in particular to a zirconium corundum refractory ball used in a hot blast furnace of a metallurgical blast furnace. 2. Technical background [0002] Generally, the refractory balls used in the hot blast stove of the metallurgical blast furnace are mainly used for heat exchange and provide high blast temperature for the blast furnace. In use, the balls are naturally piled up to form a curved airflow channel to achieve heat exchange. However, due to the high porosity, low bulk density, low strength, and poor thermal shock stability of this refractory ball, it is easy to appear in use. Problems such as pulverization, broken balls, and bonding reduce the air flow channel and lower the air supply temperature, which eventually lead to frequent shutdowns, ball replacements, and overhauls; due to its small heat storage, it can only be used at 450m 3 It is used on the hot blast stove above the blast furnace...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/106C04B35/66
Inventor 刘世聚周福辰魏富军黄丙乾张德松范建超
Owner 郑州豫兴氮氧结合耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com