Thermal sensitive imaging composition for direct platemaking by positive thermal sensitive computer

An imaging composition and heat-sensitive technology, applied in photothermographic systems, replication/marking methods, printing, etc., can solve problems such as film strength decline, application impact, and acceleration

Inactive Publication Date: 2004-04-21
TAIXING CITY ORIENT IND
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, unfortunately, 3M’s invention has two serious problems: ① The product is a liquid with extremely low viscosity, and the strength of the film layer in the photosensitive composition of the PS plate decreases, which seriously affects the printing resistance
In addition, its ability to resist ink solvents is also very poor; ②This compound is stored at room temperature, especially when it encounte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal sensitive imaging composition for direct platemaking by positive thermal sensitive computer
  • Thermal sensitive imaging composition for direct platemaking by positive thermal sensitive computer
  • Thermal sensitive imaging composition for direct platemaking by positive thermal sensitive computer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] For the preparation methods of the above compounds, please refer to the Chinese patent application 01123686.8 submitted by the applicant of the present application on September 5, 2001, and the contents related to the compounds and their preparation in this application are hereby incorporated by reference.

[0040] The compound of general formula I or II is used in the thermal imaging formulation of the thermal CTP plate material of the present invention as a dissolution-inhibiting compound, and generally has a dissolution-inhibiting property, and some have shown very good solubility-inhibiting property, The ratio of film-forming resin / solution-inhibiting-solution-promoting compound can be as high as 8:1, and the developing performance and other imaging properties are good. The changes before and after imaging are shown in the following formula:

[0041]

[0042]

[0043]

[0044] Repellant Solvent Solubilizer

[0045] Insoluble in dilute lye Easily so...

Embodiment 1

[0114] Thermal imaging composition formula: 1.55g BTB-24 phenolic resin (produced by Beijing Normal University Chemical Experimental Factory, the same below), 0.25g solution-inhibiting and promoting-solubility compound P4, 0.1g acid-producing compound triazine B (Beijing Normal University Chemical Experiment Factory production, the same below), o.1g infrared absorbing dye (830nm maximum absorption) HD-4 (product of Nippon Pigment Co., Ltd., the same below), 1ml 10% alkaline brilliant blue ethanol solution (product of Tianjin Dyestuff Factory, the same below ), 10ml methyl ethyl ketone. After the above formula is dissolved, filter it and apply it on the aluminum plate base for positive PS plate, the coating amount is 70g·m -2 (solid amount), and dried at 90° C. for 3 minutes.

[0115] Infrared laser scanning imaging: Scan the above-mentioned dried plate on a self-made infrared laser scanning device, the laser output power to the plate is 20mW, the spot diameter is 50 microns, ...

Embodiment 2

[0118] Thermal imaging composition formula: 1.55g BTB-21 phenolic resin, 0.25g solubility-inhibiting and solubility-promoting compound P4, 0.1g acid-generating compound triazine B, 0.1g infrared absorbing dye (maximum absorption at 830nm) HD-4, 1ml 10% Basic brilliant blue ethanol solution, 10ml methyl ethyl ketone. After the above formula is dissolved, filter it and apply it on the aluminum plate base for positive PS plate, the coating amount is 70g·m -2 (solid amount), and dried at 90° C. for 3 minutes.

[0119] Infrared laser scanning imaging: Scan the above-mentioned dried plate on the thermal CTP experimental plate-making prototype of Peking University Huatong Company, the laser output power to the plate is 40mW, the spot diameter is 30 microns, and the scanning speed is 10cm s -1 .

[0120] Developing: Kodak thermal CTP plate developer with a dilution ratio of 1:5, develop at 25°C for 35 seconds, and obtain a clear positive image.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The thermosensitive imaging material can be prepared by using 2,2-diphenyl-2-phenolic group acetate derivant as midbody of soluble promotion-resistance compound to carry on addition reaction with olefine ether compound of vinyl diethyl ether and dihydropyran to obtain active ester ether compound or lactone compound containing active ether being used as soluble promotion-resistance compound having ability of high soluble resistance before acidolysis and high soluble promotion ability after acidolysis; and mixing this soluble promotino-resistance compound with linear phenol resin having acidolysis soluble promotion performance, infrared obsorption dye and thermolysis type of acid producing source in proper ratio.

Description

technical field [0001] The technical field of the present invention is thermal computer-to-plate (Computer to plate, hereinafter referred to as "CTP") plate heat-sensitive formulation in the new technology field of photothermal function for information recording materials, that is, thermal imaging for positive thermal CTP plates combination. Specifically, the present invention relates to a novel thermosensitive imaging composition for positive thermosensitive CTP plates, which comprises a film-forming resin, a solution-inhibiting and solubility-promoting component, an infrared absorbing dye and a photothermal acid-generating source compound. The solution of the composition is coated on the aluminum plate base for lithographic printing, and after the film is dried, it is scanned by an infrared laser, and the acid generated by the photothermal acid-generating source compound is used to make the highly acidolytic active dissolution-promoting component Decomposition, from highly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B41M5/00G03C1/498
Inventor 邹应全余尚先施致雄
Owner TAIXING CITY ORIENT IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka