Method for producing disposable convenient tableware using puffing corn

A kind of puffed corn, one-time technology, applied in household utensils, table utensils, applications, etc., can solve the problems of no longer changing shape, complex process, low price, etc., solve oxidation and corrosion problems, simple production process, and reduce weight Effect

Inactive Publication Date: 2004-11-10
于成友
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, a large number of convenient tableware made of foamed plastics are still being used in the market. The disposable convenient tableware made of foamed plastics pollutes the environment after use. , however, it has been banned repeatedly due to the low price, and the subsequent substitute products such as paper convenience tableware, straw products, etc. have high prices
The Chinese patent (patent number: ) discloses a method of utilizing cornstarch material to manufacture fully degradable packaging products. Although the method solves the degradation problem of the material, there are still some problems to be solved in production due to the complicated process, such as, After the raw material is expanded, it has good plasticity and toughness at high temperature, and can be processed to change its shape at this time. After cooling, it no longer has plasticity and toughness, and can no longer change its shape. In the above-mentioned patent, it is used after cooling. The method of steam humidification, puffed corn is very easy to absorb water, after absorbing water, it spreads soft, and then pressed into shape. The foamy sponge function of the expanded material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for producing disposable convenience tableware with puffed corn:

[0019] (1) select corn with lower price in the grain as raw material, process it into 3-5mm corn dregs after screening, and the water content is 13%-17%;

[0020] (2) expand the corn dregs with an extruder;

[0021] (3) A cutter and a flattening shaft roller are installed at the outlet of the Penghua machine, and the materials are cut and flattened in a hot state;

[0022] (4) When the temperature of the material is 150-180 ° C, the above-mentioned sheet-shaped puffed material is pressed and formed with a wheel-type convex-concave molding machine, and the thickness is 4-5 mm;

[0023] (5) After the product is pressed and formed, when the temperature drops to 50-60°C, the inner and outer surfaces are sprayed with a waterproof adhesive layer; when the product temperature is 50-60°C, it contains 17%-20% of moisture; it still has a certain degree of toughness;

[0024] (6) Natural cooling, inspect...

Embodiment 2

[0026] A method for producing disposable convenience tableware with puffed corn:

[0027] (1) select corn with lower price in the grain as raw material, process it into 3-5mm corn dregs after screening, and the water content is 13%-17%;

[0028] (2) expand the corn dregs with an extruder;

[0029] (3) A cutter and a flattening shaft roller are installed at the outlet of the Penghua machine, and the materials are cut and flattened in a hot state;

[0030] (4) When the temperature of the material is 150-180 ° C, the above-mentioned sheet-shaped puffed material is pressed and formed with a wheel-type convex-concave molding machine, and the thickness is 4-5 mm;

[0031] While the sheet-shaped puffed material is pressed and formed by a wheel-type convex-concave molding machine, the degradable plastic film is directly pressed on the surface of the inner and outer layers by using the puffed material at a high temperature of 150-180 ° C. Spikes, used to pierce the plastic film, rele...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing disposable convenient dinnerware from swelling maize comprising the steps of, (1) screen selecting and processing into 3-5 mm maize dross, with the water content being 13-17%, (2) swelling with a swelling machine, (3) cutting under thermal state, flattening, (4) performing press compacting to the sheet form swelled articles, till the thickness is 4-5 mm, (5) spraying waterproof adhesive layer or composite plastic film on the inner and outside surfaces, (6) naturally cooling down, inspecting and packaging.

Description

technical field [0001] The invention relates to a method for producing disposable convenient tableware by puffing corn after being processed. Background technique [0002] At present, a large number of convenient tableware made of foamed plastics are still being used in the market. The disposable convenient tableware made of foamed plastics pollutes the environment after use. However, it has been banned repeatedly due to the low price, and the subsequent substitute products such as paper tableware and straw products have high prices. The Chinese patent (patent number: ) discloses a method of utilizing cornstarch material to manufacture fully degradable packaging products. Although the method solves the degradation problem of the material, there are still some problems to be solved in production due to the complicated process, such as, After the raw material is expanded, it has good plasticity and toughness at high temperature, and can be processed to change its shape at thi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A47G19/00
Inventor 于成友
Owner 于成友
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap