Fabric containing nano titanium dioxide mixture with light self cleaning function and its preparing method

A technology of nano-titanium dioxide and mixtures, which can be used in textiles, papermaking, fiber treatment, etc., and can solve problems that have not been adopted

Inactive Publication Date: 2005-05-18
CHENGDU TEXTILE COLLEGE
View PDF0 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, Japan has used photocatalyst TiO 2 With its high-efficiency catalytic and decomposition functions, various photocatalyst TiO2 for air purification have been developed successively. 2 Appliances, such as; sanitary ware, disinfection lamps, exterior wall paint, etc., but so far no use of supercritical CO 2 Fluid technology, using fiber as a carrier to make functional textiles for air purification and harmful gas decomposition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fabric containing nano titanium dioxide mixture with light self cleaning function and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0070] 1), weigh the nano-titanium dioxide-containing mixture with light self-cleaning function according to the following ratio:

[0071] TiO 2 0.1 kg (including anatase TIO 2 with rutile TIO 2 Mixed according to the ratio of 9.5:0.5), 0.1 kg of sodium lauryl sulfate, 0.05 kg of sodium sulfosuccinate 2-ethyl, 0.2 kg of perfluorinated polyether carboxylate amine, di-dodecyl di 0.5 kg of methyl amine bromide, 0.1 kg of octadecyl trihalosilane, 5.0 kg of glycerin, C 6 h 2 (CF 3 ) 4 Cu 0.0005 kg, the balance is water, the total amount is 100 kg.

[0072] 2), prepare the mixture containing nano-titanium dioxide with light self-cleaning function as follows: A, glycerin is dissolved in the total amount 50% water of high-speed stirring (12000rpm), forms emulsion, continues to stir again, drips in the stirring process Add octadecyl trihalosilane, and then add di-dodecyl dimethyl ammonium bromide;

[0073] B. Anatase TIO 2 with rutile TIO 2 Mix with an ultrasonic mixer, and ...

example 2

[0080] 1), weigh the nano-titanium dioxide-containing mixture with light self-cleaning function according to the following ratio:

[0081] TiO 2 2 kg (including anatase TIO 2 with rutile TIO 2 Mixed according to the ratio of 9.5:0.5), 1.0 kg of sodium lauryl sulfate, 0.5 kg of 2-ethyl sodium sulfosuccinate, 1.0 kg of perfluorinated polyether carboxylate amine, di-dodecyl di 1.0 kg of amine bromide, 1.0 kg of octadecyl trihalosilane, 10 kg of glycerin, C 6 h 2 C 10 h 14 o 4 Pd0.001 kg, the balance is water, the total amount is 100 kg.

[0082] 2), the method for preparing mixture and fabric is the same as example 1, and the amount of mixture on fabric is 3% of fabric weight.

example 3

[0084] 1), weigh the nano-titanium dioxide-containing mixture with light self-cleaning function according to the following ratio:

[0085] TiO 2 1 kg (including anatase TIO 2 with rutile TIO 2 Mixed in a ratio of 9.0:1.0), 0.5 kg of sodium lauryl sulfate, 0.1 kg of 2-ethyl sodium sulfosuccinate, 0.6 kg of perfluorinated polyether carboxamide (PFPE), di-dodecyl Alkyl dimethyl amine bromide (DDAB) 0.7 kg, octadecyltrihalosilane 0.6 kg, glycerin 7 kg, C 6 h 2 (CF 3 ) 4 Cu 0.0003 kg, the balance is water, the total amount is 100 kg.

[0086] 2), the method for preparing mixture is the same as example 1;

[0087] 3), prepare the fabric containing the nano-titanium dioxide mixture with light self-cleaning function as follows:

[0088] The fabric soaked and dried in the calcium chloride-phosphate solution that concentration is 2.23-22.3% by weight is put into the sample tube in the supercritical carbon dioxide treater respectively, then the photoautonomous fabric prepared b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a kind of fabric containing nano titania mixture and thus self-cleaning function. The titania mixture inside or between the fiber of the fabric contains TiO2 in 0.1-2 wt%. The nano level TiO2 powder is used as photocatalytic material, prepared into reverse emulsion and fixed onto the surface of fiber material via supercritical CO2 processing mode. The fabric containing nano level TiO2 powder is used in bedding, berth cover, curtain, etc. and under the photocatalysis of ultraviolet light in sunlight or lamp light, TiO2 will produce photocatalysis effect to decompose formaldehyde and other harmful gas, purify inside air and provide comfortable health life environment.

Description

1. Technical field [0001] The invention relates to a fabric with light self-cleaning function and a preparation method thereof, more particularly to a fabric containing nano-titanium dioxide mixture with light self-cleaning function and a preparation method thereof. 2. Background technology [0002] Light on TiO 2 The catalysis to promote the chemical reaction was first discovered by Mr. Fujishima, a professor of engineering at the Graduate School of Engineering, University of Tokyo, and it was called the "Fujishima effect" at that time. It has been more than 30 years since its discovery, and countries all over the world have paid attention to the photocatalyst TiO 2 The applied research is also getting more and more in-depth. [0003] The research results found that the photocatalyst reaction is only a surface reaction, and the substances adsorbed (contacted) on the surface react with free radicals, which are only effective for organisms with very small molecules (bacteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/46
Inventor 郑光洪
Owner CHENGDU TEXTILE COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com