Low alloy steel flux-cored welding wire for carbon dioxide gas protection welding

A technology of gas shielded welding and low-alloy steel, which is applied in the direction of welding medium, welding equipment, welding equipment, etc., can solve the problems that are not suitable for all-position welding of low-alloy high-strength steel, cannot guarantee low-temperature impact toughness, and achieve good arc stability and welding operation performance, maintaining the arc stability and welding operation performance, and the effect of smoothing the weld seam

Inactive Publication Date: 2009-07-22
WUHAN TEMO WELDING CONSUMABLES CO LTD
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned flux-cored wire is obviously not suitable for all-position welding of low-alloy high-strength steel, and cannot guarantee low-temperature impact toughness below -40°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low alloy steel flux-cored welding wire for carbon dioxide gas protection welding
  • Low alloy steel flux-cored welding wire for carbon dioxide gas protection welding
  • Low alloy steel flux-cored welding wire for carbon dioxide gas protection welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention will be described in further detail below in conjunction with accompanying drawing description and specific embodiment:

[0032] The steel sheath of the flux-cored wire is made of low-carbon steel, and its chemical composition is shown in Table 1.

[0033] Table 1: Chemical Composition % of Flux Cored Wire Steel Sheath

[0034] C

[0035] The sum of the contents of other components S, P, Sn and Bi in the flux core and carbon steel sheath of the present invention should be less than 0.035 in % of the total weight of the welding wire, wherein S is less than 0.015, P is less than 0.020, Sn is less than 0.001, and Bi is less than 0.001.

[0036] The chemical composition and raw material composition of the drug core powder are shown in Table 2.

[0037] Table 2: Composition of drug core powder

[0038] Core composition

[0039] The outer skin (14 mm wide and 0.9 mm thick) made of low carbon steel strip is filled with core powder, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

A low-alloy steel flux-cored welding wire for carbon dioxide gas shielded welding, the composition and content of the flux core in % of the total weight of the welding wire are as follows: TiO2: 3-6, Si: 0.3-0.5, Mn: 1.5-3.2, SiO2: 0.1 -0.8, ZrO2: 0.1-0.5, Fe: 2-7, Al+Mg: 0.5-1.2, Ni: 0.5-5, B: 0.002-0.015, Ti: 0.1-0.3, oxidation of alkali metal K, Na, Li The content of fluoride or fluoride equivalent to K, Na, and Li is 0.1-0.35, the content of fluoride F is 0.05-0.2, the fluoride or oxide of rare earth metal is equivalent to 0.005-0.2 of rare earth metal, and the content of C, Si, and Mn in the welding wire The product of the contents is 0.058-0.11. For high-strength low-alloy steel all-position welding process performance is good, it can maintain good arc stability and welding operation performance under the condition of high current and fast welding, the weld seam is smooth, the connection strength is high and it has a good -40 ℃ low temperature Impact toughness and excellent crack resistance.

Description

Technical field [0001] The invention relates to a welding material for metal welding, in particular to a low-alloy steel flux-cored welding wire for carbon dioxide gas shielded welding. Background technique [0002] Carbon dioxide gas-shielded flux-cored welding is compatible with the advantages of welding rods and gas-shielded solid wire welding, with high production efficiency and good welding process performance. Therefore, this welding method has been widely used in the processing and manufacturing of steel structures such as ships and bridges. Because of this, the functional requirements for flux-cored welding wire are getting higher and higher. It is required that the flux-cored welding wire can not only adapt to faster welding speed, but also have good arc stability and welding operation performance; Chinese patent announcement number: CN 1775452C, date of announcement: May 24, 2006, the name of the invention is "Carbon Steel Flux-Cored Wire for Gas Shielded Welding"...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/368B23K9/16
Inventor 卢济培杜晓琪
Owner WUHAN TEMO WELDING CONSUMABLES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com