EPT rubber waterproofing paint and process for preparing the same

A technology of EPDM rubber and waterproof coating, applied in recycled rubber coatings, antifouling/underwater coatings, coatings, etc., can solve problems such as performance inferior to EPDM rubber coils, and achieve excellent anti-aging , low cost, convenient for large-scale industrial production

Inactive Publication Date: 2008-01-30
北京立高科技股份有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of EPDM rubber as the main waterproof component, which can be naturally cured, has high elasticity, high bonding performance, can be constructed on a vertical surface, and has excellent anti-ultraviolet performance. The waterproof coating with comprehensive performance solves the defect that the performance of the existing polymer waterproof coating is inferior to that of the EPDM coil, and the problems existing in the construction of the EPDM coil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment 1 selects each raw material by following raw material and parts by weight proportioning:

[0038] EPDM rubber 5 parts

[0039] Chlorinated polyethylene 10 parts

[0040] 20 parts recycled tire rubber

[0041] 2 parts coumarone resin

[0042] 5 parts naphthenic oil

[0043] Soft carbon black 5 parts

[0044] Zinc oxide 0.5 parts

[0045] Stearic acid 0.1 parts

[0046] Sulfur 0.4 parts

[0047] Accelerator M 0.1 parts

[0048] Accelerator DM 0.1 parts

[0049] Accelerator CZ 0.15 parts

[0050] Accelerator TT 0.15 parts

[0051] Anti-aging agent RD 0.5 parts

[0052] Antiaging agent 4010 0.5 parts

[0053] Environmentally friendly solvent oil-D40 17 parts

[0054]The preparation process steps are as follows:

[0055] After masticating EPDM rubber, chlorinated polyethylene, and recycled rubber, add carbon black, zinc oxide, stearic acid, naphthenic oil, accelerator, sulfur, coumarone resin, and anti-aging agent for mixing. After kneading, the mix...

Embodiment 2

[0057] Embodiment 2 selects each raw material by following raw material and parts by weight proportioning:

[0058] EPDM rubber 7 parts

[0059] Chlorinated polyethylene 15 parts

[0060] 25 parts recycled butyl rubber

[0061] 3 parts coumarone resin

[0062] 10 parts naphthenic oil

[0063] Hard carbon black 8 parts

[0064] Zinc oxide 0.7 parts

[0065] 0.3 parts of stearic acid

[0066] Sulfur 0.6 parts

[0067] Accelerator M 0.3 parts

[0068] Accelerator DM 0.15 parts

[0069] Accelerator CZ 0.25 parts

[0070] Accelerator TT 0.2 parts

[0071] Anti-aging agent RD 1.5 parts

[0072] Antiaging agent 4010 1.5 parts

[0073] 21 copies of 380# environmentally friendly solvent oil produced in Guangdong

[0074] The preparation process steps are as follows:

[0075] After masticating EPDM rubber, chlorinated polyethylene, and recycled rubber, add carbon black, zinc oxide, stearic acid, naphthenic oil, accelerator, sulfur, coumarone resin, and anti-aging agent for...

Embodiment 3

[0076] Embodiment 3 selects each raw material by following raw material and parts by weight proportioning:

[0077] EPDM rubber 5 parts

[0078] Chlorinated polyethylene 15 parts

[0079] 20 parts recycled nitrile rubber

[0080] 3 parts coumarone resin

[0081] 10 parts naphthenic oil

[0082] Soft carbon black 5 parts

[0083] Zinc oxide 0.5 parts

[0084] 0.3 parts of stearic acid

[0085] Sulfur 0.6 parts

[0086] Accelerator M 0.5 parts

[0087] Anti-aging agent RD 2 parts

[0088] 20 parts of 26# paint environmental protection solvent oil

[0089] The preparation process steps are as follows:

[0090] After mixing EPDM rubber, chlorinated polyethylene, and recycled rubber, add carbon black, zinc oxide, stearic acid, naphthenic oil, accelerator, sulfur, coumarone resin, and anti-aging agent for mixing After kneading, the mixture is molded and cut into pieces, then added with 26# paint environmental protection solvent oil and stirred at high speed, and mixed eve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to an epdm rubber waterproof coating and a preparation method thereof. The total weight portions of dry raw material component of the waterproof coating are: epdm rubber 5-7, chlorinated polyethylene 10-15, reclaimed rubber 20-25, coumarone resin 2-3, naphthenic oil 5-10, carbon black 5-8, zinc oxide 0.5-0.7, stearic acid 0.1-0.3, sulfur 0.4-0.6, accelerator 0.5-0.9 and antioxidant 1-3. The waterproof coating adopts epdm rubber, reclaimed rubber and chlorinated polyethylene as film forming main bodies and also various modified promoter and fillings, which results in that the waterproof coating not only has excellent waterproof, ageing and cold resistance, but also has the advantages of convenient construction and low cost, and the components and construction thereof meet the requirements of national environmental standards. The invention has simple preparation process steps, is convenient to be widely industrially produced, and the store property and life service of the waterproof coating obtained is greatly prolonged. The waterproof coating can be widely applied to the waterproof construction in building, engineering, vertical plane and various waterproof datum planes.

Description

technical field [0001] The invention belongs to the technical field of waterproof paint and its preparation process, and in particular relates to an EPDM waterproof paint capable of forming an organic rubber elastic film and its preparation process. Background technique [0002] Waterproof membranes and waterproof coatings are commonly used waterproof construction materials for buildings. Because waterproof membranes are mechanized in factories, market conditions and factors affecting product quality can be reasonably controlled. In addition, their thickness is uniform, and they have now become waterproof materials. The mainstream product in China, the EPDM waterproof membrane is made of EPDM mixed with an appropriate amount of butyl rubber, vulcanizing agent, etc., and is made by banburying, filtering, pulling, and extruding. Polymer waterproof membrane. Because of its good aging resistance, long service life, good elasticity, excellent tensile properties, good high and lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D117/00C09D5/16C09D123/16C09D123/28
Inventor 王峰华
Owner 北京立高科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap