Flame-proof smoke-inhibiting wood-plastic composite material

A wood-plastic composite material and smoke suppression technology, which is applied in the field of wood-plastic composite materials, can solve the problems of large addition of flame retardants, low flame retardant performance, cost reduction, etc., and achieves small adverse effects, good processing performance, Easy to install effects

Inactive Publication Date: 2010-08-18
NORTHEAST FORESTRY UNIVERSITY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to solve the shortcomings of existing wood-plastic composite materials such as low flame retardancy, large smoke generation, large addition of flame retardant, increased cost and reduced mechanical properties of the material, and to provide a flame-retardant Smoke-suppressing wood-plastic composite material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0023] Embodiment 1: In this embodiment, 100 to 610 parts of plastic, 20 to 300 parts of wood fiber, 9 to 100 parts of intumescent flame retardant, 4.5 to 80 parts of compatibilizer and 0.75 to 20 parts of The lubricant is formed by melt blending and one-step molding; wherein the plastic is polystyrene and / or polyvinyl chloride added with heat stabilizer, and the weight ratio of polyvinyl chloride to heat stabilizer is 4-20:1; its preparation The method adopts a conventional preparation method, and the steps of the method are as follows: 1. Under the conditions of 105-150° C. and a rotating speed of 600-1000 r / min, stir the wood fiber in a high-speed mixer until the moisture content is 2-5%. . (Remove the components that are not conducive to interfacial bonding in lignocellulosic materials); 2. Add plastics, intumescent flame retardants, compatibilizers, lubricants, and heat stabilizers to the high-mixer in turn for premixing, and then mix them at 80- At 120°C, mix in a high-...

specific Embodiment approach 2

[0026] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the flame-retardant and smoke-suppressing wood-plastic composite material consists of 200-500 parts by weight of polystyrene, 80-200 parts of wood fiber, 20-80 parts Intumescent flame retardant, 10-60 parts of compatibilizer and 5-15 parts of lubricant are formed by melt blending and one-step molding.

specific Embodiment approach 3

[0027] Embodiment 3: The difference between this embodiment and Embodiment 1 is that the flame-retardant and smoke-suppressing wood-plastic composite material consists of 300 parts by weight of polystyrene, 150 parts of wood fiber, and 40 parts of intumescent flame retardant. , 20 parts of compatibilizer and 5 parts of lubricant are formed by melt blending and one-step molding.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
aspect ratioaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to View More

Abstract

A flame retardant smoke resistant wood plastic composite material relates to a wood plastic composite material, which solves the disadvantages of low flame retardant performance, big smoke mass, large addition of flame retardants, increased cost and decreased mechanical property of existing wood plastic composite materials. The product of the invention is mainly formed by polystyrene and / or polyvinyl chloride fortified with heat stabilizers, lignocellulose, intumescent flame retardant, compatibilizer, lubricant. The flame retardant and smoke-resistant performance of the product of the invention is greatly improved. For wood powder / polystyrene composite material, compared with no addition of flame retardant, the average heat release rate is decreased by 48 percent, the quantity of smoke yield is reduced by 30 percent and the CO yield is decreased by 28 percent during combustion. The product of the invention has high oxygen-index, long ignition time and no droplet, which greatly reduces the fire hazard of the material, and the appearance of the material is similar with wood. The product of the invention also has low cost, wide application range and good creep resistance, forming performance and mechanical property.

Description

technical field [0001] The invention relates to a wood-plastic composite material. Background technique [0002] Wood-plastic composites are composite materials made of wood fiber materials and plastics as the main raw materials. As a new type of engineering material, wood-plastic composite material is characterized by its excellent water resistance and corrosion resistance, insect resistance, good dimensional stability, flexible production process, and little damage to equipment. It can also use recycled waste wood and plastics. It is made from raw materials and has attracted much attention due to its advantages of being recyclable. [0003] It is precisely because of the many advantages of wood-plastic composite materials that its market is growing rapidly, especially in construction and automotive applications. On the other hand, the rapidly expanding market has put forward higher performance requirements for the wider application of wood-plastic composite materials. F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L27/06C08K5/57C08L97/02C08K5/09C08K3/32
Inventor 王清文房轶群宋永明张志军隋淑娟
Owner NORTHEAST FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com