Environmental protection highly effective additive for electrolyzing selenium-free manganese metal and preparation method thereof

A technology of metal manganese and additives, applied in the field of metallurgy, can solve the problems of reducing the amount of selenium, achieve the effects of reducing the formation of manganese junctions on the surface, increasing overvoltage, and improving product quality

Inactive Publication Date: 2010-09-29
LUXI XIBANG SCI & TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Domestic scientific and technological workers have done a lot of research work on electrolytic manganese. For example, Yao Yuexiang and others in China proposed the use of auxiliary additives and SeO 2 Mixed use, to achieve the purpose of reducing the amount of selenium; Yang Zaifa will SO 2 and SeO 2 Mixed use, thereby reducing the content of sulfur and selenium in the product, but still not getting rid of SeO 2

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental protection highly effective additive for electrolyzing selenium-free manganese metal and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Environmentally friendly and efficient electrolytic selenium-free metal manganese additives are prepared from water-soluble polyacrylamide, animal glue, polyethylene glycol, boric acid and water. The weight percentage of each raw material is: water-soluble polyacrylamide 8%, Animal glue 11%, polyethylene glycol 20%, boric acid 4%, water 57%.

[0016] The water-soluble polyacrylamide is cationic, with a molecular weight of 8 million to 12 million; for example, the cationic of Guangzhou Huabei Chemical Technology Co., Ltd. is 12 million.

[0017] Described animal glue is bone glue, such as the industrial bone glue produced by Hebei Hengshui Brothers Gelatin Factory.

[0018] The molecular weight of the polyethylene glycol (PEG) is 2000-6000, such as PEG4000 produced by Fushun Jiahua Polyurethane Co., Ltd.

[0019] The preparation method of the above-mentioned environmentally friendly and high-efficiency electrolytic selenium-free metal manganese additives comprises the f...

Embodiment 2

[0027] Environmentally friendly and efficient additives for electrolytic selenium-free metal manganese are prepared from water-soluble polyacrylamide, animal glue, polyethylene glycol, boric acid and water. The weight percentage of each raw material is: water-soluble polyacrylamide 5%, Animal glue 8%, polyethylene glycol 30%, boric acid 5%, water 52%.

[0028] The water-soluble polyacrylamide is cationic, with a molecular weight of 8 million to 12 million; for example: CPF-800 produced by Gongyi Jinyuan Chemical Co., Ltd.

[0029] The animal glue is bone glue, such as the industrial bone glue produced by Dongguan Ande Gelatin Co., Ltd.

[0030] The molecular weight of the polyethylene glycol (PEG) is 2000-6000, such as PEG6000 produced by Fushun Jiahua Polyurethane Co., Ltd.

[0031] The preparation method of the above-mentioned environmentally friendly and high-efficiency electrolytic selenium-free metal manganese additives comprises the following steps:

[0032] 1) Accordi...

Embodiment 3

[0039] Environmentally friendly and efficient additives for electrolytic selenium-free metal manganese are prepared from water-soluble polyacrylamide, animal glue, polyethylene glycol, boric acid and water. The weight percentage of each raw material is: water-soluble polyacrylamide 10%, Animal glue 15%, polyethylene glycol 40%, boric acid 3%, water 32%.

[0040] The water-soluble polyacrylamide is cationic, with a molecular weight of 8 million to 12 million; for example: CPF-1000 or CPF-1200 of Jiangdu Runhua Water Purifier Co., Ltd.

[0041] Described animal glue is gelatin, such as the industrial gelatin produced by Hebei Hengshui Brothers Gelatin Factory.

[0042] The molecular weight of the polyethylene glycol (PEG) is 2000-6000. Such as PEG2000 produced by Fushun Jiahua Polyurethane Co., Ltd.

[0043] The preparation method of the above-mentioned environmentally friendly and high-efficiency electrolytic selenium-free metal manganese additives comprises the following ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the metallurgical field, and in particular relates to an environment-friendly high-efficient electrolytic selenium-free manganese metal additive and a preparation method for the same. The environment-friendly high-efficient electrolytic selenium-free manganese metal additive is characterized in that: the additive is prepared by raw materials of water-soluble polyacrylamides, animal glue, polyethylene glycol, boric acids and water. The content of various raw materials by weight percent is as follows: 5 to 10 percent of polyacrylamides; 8 to 15 percent of animal glue; 30 to 40 percent of polyethylene glycol; 3 to 5 percent of boric acids; and residual water. The sum of the content of various raw materials by weight percent is 100 percent. The additive is nontoxic and non-corrosive; volatilization and so on can not be generated during the electrolysis process; the operation is convenient and safe; and the environmental protection performance is good. Moreover, the additive is used for electrolytic manganese and is characterized by high current efficiency and good product quality of the electrolytic manganese.

Description

technical field [0001] The invention belongs to the field of metallurgy, and in particular relates to an environmentally friendly and efficient additive for electrolytic selenium-free metal manganese and a preparation method thereof, which is used for the electrolytic production of metal manganese in an ammonium sulfate-manganese sulfate solution system. Background technique [0002] In 1923, A.J.Allmand and A.N.Campbell in the United Kingdom electrolyzed metallic manganese with a ceramic diaphragm. However, it was not until the mid-1940s that a suitable additive was found, and electrolytic manganese really entered industrial production. Looking at every progress in the electrolytic manganese industry, it is accompanied by the research and utilization of new additives. It can be said that additives play a pivotal role in the progress of electrolytic manganese technology. During the development of electrolytic manganese additives, SO 2 , sulfur compounds, SeO 2 , selenium-c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25C1/10
Inventor 田熙科杨超田熙学皮振邦田熙文
Owner LUXI XIBANG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com