Quaternized cellulose ethers for personal care products

A personal care and cellulose ether technology, which can be used in skin care preparations, hair care, cosmetic preparations, etc., and can solve the problems of reduced foaming, poor viscosity maintenance, and poor thickening efficiency.

Active Publication Date: 2009-09-30
UNION CARBIDE CORP
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Known polymeric thickeners often exhibit poor thickening efficiency or poor surfactant compatibility, while associative thickeners, while not having the...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quaternized cellulose ethers for personal care products
  • Quaternized cellulose ethers for personal care products
  • Quaternized cellulose ethers for personal care products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The quaternized cellulose ethers of the present invention are obtained in combination with the various components listed in Table 1 below:

[0033] Table 1

[0034]

batch 1

batch 2 batch 3

(Compared)

batch 4 batch 5

(Compared)

batch 6

batch 7 HEC1 60 -- -- -- -- -- -- HEC2 -- 80 40 -- 300 40 * 80 HEC3 -- -- -- 60 -- -- -- acetone 360 480 240 -- -- -- 460 6% isopropyl alcohol (IPA) in water -- -- -- -- 1805 -- -- 0% IPA in water -- -- -- -- -- 241 -- 2% IPA in water -- -- -- 360 -- -- -- 25% by weight sodium hydroxide (NaOH)

(calculated as dry weight) aqueous solution

4.9

9.25

5.2

2.85

27

2.45

7.2 QUAB 342 28 60 35 10 150 10 40 QUAB 151 3.0 15 0 12 0 5 4

[0035] * Use batch 5 compound instead of HEC

[0036] The above abbreviations are de...

Embodiment 2

[0044] Following essentially the protocol of Example 1, the batches listed in Table 1 were prepared and characterized. The results are listed in Table 2:

[0045] Table 2

[0046]

[0047]Compounds of batches 1-7 may be represented by formula (II) above, wherein n is about 500-2000, x is selected such that the hydroxyethyl substitution M.S. is about 2.0 to 2.4, and y and z are selected such that the batch Subcompounds have the nitrogen percentages and levels of hydrophobic substitution (HS) listed in Table 2. Nitrogen content, %N: average weight percentage of nitrogen per anhydroglucose repeat unit determined by titration with an automated Buchi Kjeldahl distillation unit using an automated Buchi Kjeldahl distillation unit. The average number of moles of hydrophobic substituents per mole of anhydroglucose units is expressed as hydrophobic substitution (HS). Using nuclear magnetic resonance ( 1 H-NMR, 400 MHz, using sodium trimethylsilyl propionate as a standard a...

Embodiment 3

[0049] The personal care composition of the present invention comprises the quaternized cellulose ether from Example 1 with the components listed in Table 3:

[0050] table 3

[0051] Batch A Batch B Batch D Ammonium Laureth Sulfate (ALS) (28% actives) 20.9％ 20.9％ 20.9％ Sodium Laureth Sulfate, 2 Moles Ethylene Oxygen

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Brookfield viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The present invention describes quaternized cellulose ethers suitable for personal care products.

Description

technical field [0001] The present invention relates to quaternized cellulose ethers suitable for rheological modification of personal care products. Background technique [0002] Typically, rheology modifiers are used to adjust the rheological properties of the composition (including viscosity, flow rate, stability of viscosity over time or with increasing temperature, and the ability of the composition to suspend particles). For personal care products, the rheology of the formulation can have a significant impact on the consumer's perception of the product. Known polymeric thickeners often exhibit poor thickening efficiency or poor surfactant compatibility, while associative thickeners, while not having these disadvantages, show spreading Undesirable properties such as reduced spreadability, poor viscosity maintenance at high temperatures and reduced lather / foam. [0003] Accordingly, there is a continuing need for new rheology modifiers that are effective in thickening ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/73A61K8/23A61K8/60
CPCA61K8/604A61Q19/00A61K8/731A61K2800/5426A61K8/442A61K8/463A61Q5/10A61P9/10A61K8/23A61K8/60A61K8/73A61Q19/10
Inventor 张晓东爱德华·F·黛安托尼奥拉塞尔·L·克里格温·K·李塔蒂亚娜·V·德罗维特斯卡亚
Owner UNION CARBIDE CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka