Steel plate for low-carbon high-niobium extra-high strength welding structure and method for manufacturing same
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An ultra-high-strength, welded structure technology, applied in the direction of temperature control, etc., can solve the problems of low steel plate strength level, low production efficiency, low controlled rolling temperature, etc., achieve small rolling load, high production efficiency, and improve rolling start. The effect of temperature
Inactive Publication Date: 2010-01-06
ANGANG STEEL CO LTD +1
View PDF4 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0008] In view of the defects in the above-mentioned prior art, such as low non-recrystallized controlled rolling temperature, large mill load, long waiting time, low production efficiency, poor welding performance, low steel plate strength level, etc., the purpose of the present invention is to overcome the disadvantages of the prior art. Insufficient to provide a yield strength ≥ 960N / mm 2 Grade ultra-high strength welded structural steel and production method thereof
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0028] The present invention will be further described below by way of examples.
[0029] See Table 1 for the chemical composition of the steel grades of the embodiments of the present invention.
[0030] The process parameters of the corresponding steel types in the embodiments of the present invention are shown in Table 2.
[0031] The mechanical properties of the corresponding steel types in the examples of the present invention are shown in Table 3.
[0032] Table 1, the smelting composition (Wt%) of steel grade of the embodiment of the present invention
[0033] Example
C
Si
mn
P
S
Cu
Ni
Cr
Mo
Nb
Ti
V
Bt
als
0#
0.05
0.22
1.65
0.010
0.005
1.25
1.50
0.81
0.3
0.075
0.02
0.07
0.0013
0.03
51#52#53#
0.047
0.25
1.63
0.010
0.010
1.14
1.00
0.52
0.59
...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention provides a steel plate for a low-carbon high-niobium high strength welding structure. The steel plate comprises the following chemical components in percentage by weight: 0.015 to 0.075 percent of C, 0.20 to 0.50 percent of Si, 1.63 to 2.0 percent of Mn, 0.081 to 0.12 percent of Nb, 0.005 to 0.030 percent of Ti, 0.0005 to 0.0030 percent of B, 0.50 to 0.95 percent of Cr, 0.70 to 1.25 percent of Cu, 0.50 to 1.50 percent of Ni, 0.30 to 0.60 percent of Mo, 0.010 to 0.050 percent of Als, and the balance of Fe and inevitable impurities. The method for manufacturing the steel plate comprises the steps of molten iron pretreatment, rotary furnace smelting, refining, continuous casting and rolling, wherein the rolling process adopts the HTP plus RPC process, the heating temperature before rolling is between 1,140 and 1,220 DEG C, and two-stage controlled rolling is adopted. The steel plate is low in carbon content and high in Nb content, so that the initial rolling temperature of the non-recrystallization controlled rolling is increased, the temperature holding time is short, and the manufacturing efficiency is high; because the carbon content and the carbon equivalent are low, the welding performance is good; and with the HTP plus RPC plus annealing process, the steel plate for the welding structure with good toughness and plasticity and the yield strength more than or equal to 960N / mm<2> can be manufactured.
Description
technical field [0001] The invention belongs to the technical field of metal materials, and in particular relates to a low-alloy high-performance steel plate and a manufacturing method thereof. Background technique [0002] At present, the development trend in fields such as construction machinery, heavy-duty trucks, cement pump trucks, semi-trailers, containers, and pressure pipes of hydropower stations is to use more and more high-strength and ultra-high-strength welded structural steels. Carrying capacity, saving energy. At the same time, ultra-high-strength steel plates are required to have the characteristics of low cost, good welding performance, and high low-temperature impact toughness. [0003] Internationally, a number of patents have been formed on the manufacturing method of ultra-high-strength steel plates with a yield strength of about 960MPa, such as: [0004] The publication number CN1148416A that Nippon Steel Co., Ltd. applied for in China is named "high-s...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.