High-strength castable

A castable, high-strength technology, applied in the field of high-strength castables, can solve the problems of high cost of corundum materials, high raw material costs, increased production costs of production enterprises, etc., and achieve good thermal shock resistance and high softening temperature under load , the effect of reducing consumption

Active Publication Date: 2010-05-26
郑州真金耐火材料有限责任公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In cement kiln kilns, preheaters, grate coolers and other kilns that require high strength and poor service conditions, high-strength corundum castables are often used. Due to the high cost of corundum materials, the cost of raw materials is high, so that Manufacturers increase production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength castable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The high-strength castable according to the present invention is composed of raw materials bauxite, brown corundum, silicon carbide, silicon micropowder, CA-70 cement, alumina powder, sodium tripolyphosphate, and sodium hexametaphosphate according to the following parts by weight Formulated with:

[0016] 2.5 parts of bauxite materials with a particle size of 8-5mm, 2.3 parts of bauxite materials with a particle size of 0.075mm<5mm; 2 parts of brown corundum particles with a particle size of 3-1mm; 0.4 parts of alumina superfine powder with a particle size of 0.025 mm; 0.6 parts of silicon carbide powder with a particle size of ≤0.075 mm; 0.3 parts of silicon powder with a particle size of <0.019 mm; 0.6 parts of CA-70 cement; 0.5 parts of brown corundum powder with a particle size of <0.053 mm; Sodium tripolyphosphate of 0.1% of the total material weight; sodium hexametaphosphate of 0.08% of the total material weight; use a jaw crusher or a cone crusher to crush the ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength castable, which is prepared from the following raw materials in part by weight: 4.8 parts of bauxite aggregate, 2 parts of brown aluminium oxide granules, 0.8 part of bauxite powder, 0.4 part of alumina super-micro powder, 0.6 part of silicon carbide powder, 0.3 part of silicon micro powder, 0.6 part of CA-70 cement, 0.5 part of brown aluminium oxide powder, sodium tripolyphosphate accounting for 0.1 percent of weight of the total material, and sodium hexametaphosphate accounting for 0.08 percent of the weight of the total material. The castable has the advantages of high compression strength, high breaking strength, high load softening temperature, good thermal shock resistant stability, micro-expansion property at high temperature, good abrasion resistance and the like; the cost is reduced by about two fifth compared with that of the conventional high-strength castable; and the castable can be widely applied to kilns of cement kiln eyes, pre-heaters, grate coolers and the like with high strength requirement and severe using conditions, and is an ideal new product for replacing a high-strength corundum castable.

Description

technical field [0001] The invention relates to castables for cement kilns, in particular to a high-strength castable with low cost and long service life. Background technique [0002] In cement kiln kilns, preheaters, grate coolers and other kilns that require high strength and poor service conditions, high-strength corundum castables are often used. Due to the high cost of corundum materials, the cost of raw materials is high, so that Manufacturers increase production costs. Contents of the invention [0003] The object of the present invention is to provide a high-strength castable with low cost and long service life. [0004] To achieve the above object, the present invention can take the following technical solutions: [0005] The high-strength castable according to the present invention is composed of raw materials bauxite, brown corundum, silicon carbide, silicon micropowder, CA-70 cement, alumina powder, sodium tripolyphosphate, and sodium hexametaphosphate accor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 宋金标宋禄峰宋彩红宋马峰樊建令卢中立郭英超付鸿正樊召峰孙艳秋
Owner 郑州真金耐火材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com