Wide-temperature low-distortion mangan zinc ferrite and preparation method thereof
A manganese-zinc ferrite, low-distortion technology, applied in the direction of magnetism of inorganic materials, can solve the problems of poor harmonic distortion performance, difficult to meet the technical requirements of passive magnetic devices, etc. The effect of small and uniform particle size and relative loss factor satisfaction
Active Publication Date: 2010-06-09
TDG HLDG CO LTD
View PDF0 Cites 23 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the harmonic distortion performance of high-permeability ferrite materials developed in China is very poor, and there is no research on this performance at all, so it is difficult to meet the technical requirements of passive magnetic devices for the development of broadband network access technology
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
Embodiment 2~6
Embodiment 7~8
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
dielectric loss factor | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a wide-temperature low-distortion mangan zinc ferrite applicable to a broadband network transformer and a preparation method thereof. The mangan zinc ferrite mainly comprises the following components: 52.0 to 53.0 mol percent of iron oxide computed by Fe2O3, 21.0 to 23.0 mol percent of zinc oxide computed by ZnO, and the balance of trimanganese tetroxide, and also comprises the following auxiliary components in percentage by weight (wt %) computed by respective standard substance CaCO3, SiO2, V2O5 and Co2O3: 0.03 to 0.04 of CaCO3, 0.005 to 0.01 of SiO2, 0.01 to 0.03 of V2O5 and 0.03 to 0.1 of Co2O3. The mangan zinc ferrite is prepared by an oxide method and sintered under the condition of bell-type furnace densification. A product has higher initial magnetic permeability mu i, low relative loss factor tan delta / mu i, and wide-temperature low-magnetic hysteresis coefficient eta B (-40 to 85 DEG C), is capable of reducing waveform distortion, reducing transmission errors and prolonging transmission distance in the process of transmitting signals, and meets the requirement of the application in outdoor severe environment.
Description
technical field The invention belongs to the technical field of manganese-zinc high magnetic permeability soft magnetic ferrite, in particular to a manganese-zinc ferrite for broadband network transformers with low temperature sintering, high initial magnetic permeability, wide temperature and low hysteresis coefficient (-40°C to 85°C) Ferrite and its preparation method. Background technique In recent years, with the rapid development of the Internet and the accelerated process of global economic informatization, new broadband network construction booms have been set off all over the world. Due to the improvement of modulation and demodulation technology and the progress of fast digital signal processing chip production technology, new access methods combining fast digital signal processing technology and advanced modulation and demodulation technology have emerged, such as asymmetric digital subscriber loop line (ADSL, Asymmetrical Digital Subscriber Loop) technology, high...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/36C04B35/622C04B35/64
Inventor 金辉邵峰戴勇飞
Owner TDG HLDG CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com