Pre-coating solution for digital jet printing for cotton
A digital inkjet and pre-coating liquid technology, applied in dyeing, textile and papermaking, fiber processing, etc., can solve the problems of easy penetration, poor water fastness, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0009] Precoating liquid formula: (weight ratio)
[0010] Cationic resin (20% solid content): 40 parts
[0011] Silica 20 parts
[0012] Silicone dispersant 0.2 parts
[0013] Polyvinyl alcohol (18% solid content) 30 parts
[0014] 10 parts deionized water
[0015] Add a certain amount of deionized water into the reactor, add an appropriate amount of silicone dispersant, add silica powder while stirring at high speed, filter after stirring for 30 to 60 minutes, and then mix the dispersed silica aqueous solution, water-based cationic resin , polyvinyl alcohol aqueous solution, and deionized water were added to the reactor in turn and stirred fully for 30 minutes. After stirring for 10 minutes, let it stand still for use. After spraying the pre-coating liquid evenly on the surface of the cotton to be ink-jet printed, ink-jet printing was performed, and the printing was completed. Finally, bake at 130°C for 5 minutes to obtain the finished product.
Embodiment 2
[0017] Cationic styrene-acrylic resin (40% solid content) 30 parts
[0018] Light calcium carbonate 15 parts
[0019] Silicone dispersant 0.3 parts
[0020] 10 parts methyl cellulose
[0021] Polyvinyl alcohol aqueous solution (20%) 20 parts
[0022] 25 parts deionized water
[0023] Add a certain amount of deionized water into the reactor, add an appropriate amount of silicone dispersant, add light calcium carbonate powder while stirring at high speed, filter after stirring for 30 to 60 minutes, and then mix the dispersed light calcium carbonate aqueous solution, Cationic styrene-acrylic resin emulsion, methyl cellulose aqueous solution, polyvinyl alcohol aqueous solution, and deionized water were sequentially added to the reactor and stirred for 30 minutes. After stirring for 10 minutes, let it stand for use. Ink-jet printing is carried out after the pre-coating solution, and the finished product is obtained by baking at 120°C for 6 minutes after printing.
Embodiment 3
[0025] Cationic polyurethane resin (40% solid content) 40 parts
[0026] Silicon dioxide 10 parts
[0027] Silicone dispersant 0.2 parts
[0028] Polyvinyl alcohol aqueous solution (20%) 30 parts
[0029] 20 parts deionized water
[0030] Add a certain amount of deionized water into the reactor, add an appropriate amount of silicone dispersant, add silicon dioxide powder while stirring at high speed, filter after stirring for 30-60 minutes, and then mix the dispersed silicon dioxide aqueous solution and cationic polyurethane resin Emulsion, polyvinyl alcohol aqueous solution, and deionized water were added to the reactor in turn and stirred for 30 minutes. After stirring for 10 minutes, let it stand still for use. After spraying the pre-coating liquid evenly on the surface of the cotton to be ink-jet printed, ink-jet printing was carried out. After the end, bake at 100°C for 10 minutes to get the finished product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap