Fluxing agent as well as preparation method and application thereof

A technology of flux and thixotropic agent, which is applied in the manufacture of fuses, electrical components, circuits, etc., and can solve the problems of slow melting speed and non-disconnection of eutectic alloy wires

Active Publication Date: 2014-01-01
上海神沃电子有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the organic amine hydrohalide in the above-mentioned flux plays a vital role in the activity of the flux. If it is missing, the fusing speed of the fusible alloy wire will slow down, and even the phenomenon of continuous disconnection after melting may occur.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-7

[0023] The rosin, organic acid and stearic acid amide are weighed according to the ratio in Table 1, after mixing the rosin and stearic acid amide, heat to melt, then add the organic acid, and stir until the organic acid dissolves. The resulting mixture is cooled.

[0024] When the flux also contains a thixotropic agent, after mixing the thixotropic agent with rosin and stearic acid amide, heat to melt, then add an organic acid and stir until the organic acid dissolves. The resulting mixture is cooled.

[0025] The composition of table 1 flux (unit: wt %)

[0026] Example

[0027] Comparative Experiment:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fluxing agent as well as a preparation method and application thereof. The fluxing agent comprises the following components in percentage by weight: 60-80 percent of rosin, 2-20 percent of organic acid and 10-30 percent of octadecanamide. The fluxing agent can be applied to temperature fuse elements to promote the fusing of a fusible ally wire. Compared with the prior art, the fluxing agent does not contain halogen and accords with the development tendency of environment protection. When applied to temperature fuse, the fluxing agent can achieve the effect of using a fluxing agent containing halogen.

Description

technical field [0001] The invention relates to a flux, in particular to a halogen-free flux for a temperature fuse. Background technique [0002] People are paying more and more attention to the safety of electronic and electrical equipment, requiring these equipment to be equipped with over-temperature and over-current protection devices. At present, thermal fuses are commonly used over-temperature protection components. [0003] The main part of the thermal fuse is a fusible alloy wire. When the ambient temperature rises to the melting point of the fusible alloy, the fusible alloy wire melts and disconnects, thereby cutting off the circuit protection device. Therefore, whether the fusible alloy wire can be completely disconnected in time is the key technology of the thermal fuse. In order to improve the fusibility of the fusible alloy wire, it is common practice to wrap flux around the fusible alloy wire. The main component of the flux is rosin, including natural rosin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01H85/06H01H69/02
Inventor 周欣山宋华傅坚李凯
Owner 上海神沃电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products