Super wear-resistant ceramic-steel composite lining plate for mixer and preparation method thereof

A composite liner and super wear-resistant technology, which is applied in the field of wear-resistant parts, can solve the problems of limited application of ceramic materials, difficulty in processing, and easy cracking, etc., and achieve the goal of improving equipment use efficiency, prolonging service life, and low price Effect

Inactive Publication Date: 2010-09-01
洛阳万晟耐磨科技有限公司
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ceramic materials are relatively brittle, cannot withstand large impacts, and are difficult to process, and their products are prone to fragmentation during installation and fixing, which limits the application of ceramic materials in these fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super wear-resistant ceramic-steel composite lining plate for mixer and preparation method thereof
  • Super wear-resistant ceramic-steel composite lining plate for mixer and preparation method thereof
  • Super wear-resistant ceramic-steel composite lining plate for mixer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] a. Overall design: According to the requirements of use, the geometric shape of the lining plate is designed to be arc-shaped and the size is 800×1000×45mm, and the molding mold is designed and manufactured; the thickness of the ceramic material layer is set to 40mm, and the thickness of the metal substrate is 5mm. And there are 9 installation parts with a thickness of 10mm; the diameter of the anchor nail is 5mm, the height is 30mm, about every 10cm 2 Set one; the width of the rib is 8mm, the height is 15mm, and one is set at about 15cm in the length and width directions.

[0031] Brown corundum (Al 2 o 3 ) segment sand raw material, the segment sand with a particle size of 15-20mm is the main aggregate, accounting for 45% by weight of the total amount, and the segment sand with a particle size of 6-8mm, 2-3mm, 1-2mm and 0-0.5mm The segment sand is auxiliary aggregate, and the weight percentages of the total amount are 20%, 15%, 10% and 5% respectively. The particle...

Embodiment 2

[0037] a. Overall design: According to the requirements of use, the geometric shape of the liner is designed as a fan-shaped flat plate, and its outline size is 600×800×35mm, and the molding mold is designed and manufactured; the thickness of the ceramic material layer is set to 29mm, and the thickness of the metal substrate 6mm, and there are 6 installation parts with a thickness of 6mm; the diameter of the anchor nail is 4mm, the height is 25mm, about every 20cm 2 Set one; the width of the rib is 8mm, the height is 15mm, and one is set at about 15cm in the length and width directions.

[0038] The ceramic material is made of silicon carbide section sand, with 8-10mm section sand as the main aggregate, accounting for 40% of the total weight, and three grades of 3-5mm, 1-2mm and 0-0.5mm section sand As the auxiliary aggregate, the percentage by weight of the total amount is 25%, 18 and 12% respectively; the particle size of the selected ceramic powder is 200 mesh, and the perc...

Embodiment 3

[0044] a. Overall design: According to the requirements of use, the geometric shape of the whole liner is flat and the size is 1000×1200×35mm. Due to the large area, the overall strength of the composite product is low, and it is not convenient for the composite process; therefore , using the splicing and combination design method, the whole liner is designed into four small pieces, a 5mm gap is reserved for the splicing position, and the geometric shape and size of each small liner are determined to be 500×600mm. The original whole liner has 9 There are 1 mounting bolt hole and 1 complete mounting bolt hole and 3 circular arc mounting bolt holes on each small liner after division, such as image 3 As shown; and design and make the forming mold accordingly; the thickness of the ceramic material layer is set to 31mm, the thickness of the metal substrate is 4mm; the diameter of the anchor nail is 3mm, the height is 13mm, about every 8cm 2 Set one; the reinforcing rib adopts a ro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a super wear-resistant ceramic-steel composite lining plate for a mixer and a preparation method thereof. The composite lining plate comprises a metal base plate and a ceramic material layer, wherein a mixture of a ceramic material and an adhesive is pressed on a combining surface of the metal base plate by a pressing force, which is coated with the adhesive so that the ceramic material and the steel are compounded; the metal base plate is provided with a mounting bolt hole; and metal anchoring nails and reinforced ribs are distributed on the combining surface. The preparation method comprises four processes, namely a metal base plate manufacturing process, a ceramic material preparing process, a compounding process, a curing process and the like. The super wear-resistant ceramic-steel composite lining plate has rich raw material resources, simple process, low price and higher cost performance. After the super wear-resistant ceramic-steel composite lining plate is comprehensively constructed, the service life of the lining plate is prolonged by 10 to 15 times; the capital consumption is reduced by 50 percent; the maintenance and replacement time is shortened by over 90 percent; the utilization rate of equipment is improved by about 10 percent; labor intensity and production cost are reduced; human resources and materials are saved; and further potential economic benefit is brought to the society.

Description

technical field [0001] The invention is applicable to the field of wear-resistant parts of mechanical devices such as mixing and stirring, and mainly relates to a super wear-resistant ceramic-steel composite liner for a mixer and a preparation method thereof, and is especially suitable for metallurgy, glass manufacturing, refractory materials, thermoelectric , Mineral dressing, ceramics, chemical industry and other industries. Background technique [0002] At present, it is used as anti-wear parts such as lining boards on mixers and mixers in metallurgy, refractory materials, glass manufacturing, thermal power plants, mineral processing, ceramics, chemical industry and other industries. About 30,000 tons of high-quality wear-resistant steel are consumed every year, and the capital consumption is about 600 million yuan, which consumes a large amount of resources and funds, and also consumes a large amount of strategic materials such as precious metals, which does not conform ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01F15/00B32B15/04B32B18/00B32B7/04
Inventor 杨国兴
Owner 洛阳万晟耐磨科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap