Tungsten-strengthened wear-resistant submerged-arc overlaying welding flux-cored wire
A technology of submerged arc surfacing and flux-cored welding wire, which is applied in welding medium, welding equipment, welding/cutting medium/material, etc., and can solve problems such as inability to meet
Inactive Publication Date: 2010-10-27
HOHAI UNIV CHANGZHOU
View PDF4 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
It can be seen that the existing flux-cored wires used for surfacing and repairing are far from meeting the needs of composite manufacturing and repairing of steel mill rolls, coal grinding rolls of thermal power plants, and engineering excavation machinery.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment approach
[0028] The second specific implementation mode, as attached figure 1 shown.
[0029] A tungsten-enhanced submerged-arc surfacing flux-cored welding wire, comprising an H10 low-carbon steel hollow welding wire and a powder flux core arranged in the hollow welding wire, the proportion of the powder flux core being: the high-carbon ferrochrome 50%, 12% of the tungsten powder, 8% of the ferromanganese deoxidizer, and 30% of the iron powder. The filling rate is 45%. The average hardness of the surfacing layer of flux-cored wire is HRC63.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| hardness | aaaaa | aaaaa |
Login to view more
Abstract
The invention discloses a tungsten-strengthened wear-resistant submerged-arc overlaying welding flux-cored wire which comprises a low-carbon steel cored solder wire and flux-cored powder arranged in the cored solder wire, wherein the flux-cored powder is mainly characterized by comprising the following components in percentage by weight (%): 30-55% of high carbon ferrochrome, 3-15% of tungsten powder, 3-8% of deoxidizer and 25-55% of iron powder. The overlaying welding layer of the invention has the characteristics of uniform hardness distribution, high wear resistance, excellent welding technological properties and the like.
Description
technical field [0001] The invention relates to a tungsten-strengthened wear-resistant submerged arc surfacing flux-cored welding wire, which belongs to the technical field of welding materials. Background technique [0002] Flux-cored welding wire is a flux-cored welding wire made by wrapping alloying elements (powder core) in steel skin and drawing them into different diameters. [0003] After the flux-cored wire is melted by welding, an alloy welding layer with special properties such as wear resistance, corrosion resistance and high temperature resistance is formed. Flux cored wire submerged arc welding plays an important role in repair and composite manufacturing, and is widely used in composite parts of mechanical structural parts such as high wear resistance of mechanical engineering structures. [0004] At present, the wear-resistant flux-cored wires for surfacing repair generally contain alloying elements such as carbon, chromium, silicon, and manganese, and rarely...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/368B23K35/30
Inventor 杨可包晔峰蒋永锋
Owner HOHAI UNIV CHANGZHOU
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap