Latex-type waterborne pigment oil ink for inkjet printing of non-absorbed substrate as well as preparation method and applications thereof

A technology of non-absorbent substrates and water-based pigments, applied in inks, applications, printing devices, etc., can solve problems such as difficulties, poor scratch resistance, and poor light fastness, and achieve high precision and good printing fluency , Excellent anti-smudge effect

Active Publication Date: 2010-12-01
上海英威喷墨科技有限公司 +1
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For dye-based water-based inks, because the dye molecules will quickly decompose and volatilize under the irradiation of ultraviolet light, their light fastness is poor and not suitable for outdoor use; for pigment-based water-based inks, due to the pigment and non-absorbing base There is no chemical bond or strong intermolecular force between the materials, the ink cannot adhere well to the surface of the non-absorbent substrate, and the scratch resistance is poor, so pigment-based water-based ink is used on the surface of the non-absorbent substrate to obtain High-resolution, outdoor-durable images present some difficulties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Latex-type waterborne pigment oil ink for inkjet printing of non-absorbed substrate as well as preparation method and applications thereof
  • Latex-type waterborne pigment oil ink for inkjet printing of non-absorbed substrate as well as preparation method and applications thereof
  • Latex-type waterborne pigment oil ink for inkjet printing of non-absorbed substrate as well as preparation method and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Preparation of emulsion-type water-based pigment red ink

[0038] The formula of table 1 emulsion type water-based pigment red ink

[0039]

[0040] Note: Cab-O-Jet pigment is a kind of self-dispersing pigment, purchased from American Cabot Company.

[0041] According to the formula of the red ink in Table 1, surfactant, water-soluble co-solvent and deionized water are mixed at normal temperature, stir 50min under 800rad / min rotating speed with agitator, obtain mixed solution; Continue to stir and add to mixed solution Slowly add the polymer emulsion AC-570JW, and stir for 30 minutes; finally, slowly add the pigment dispersion while stirring, and continue stirring for 60 minutes. After the various components are fully mixed to form a uniform dispersion system, filter with a 0.2-2 μm microporous membrane to obtain the emulsion-type water-based pigment red ink for inkjet printing.

[0042] The physical properties of this ink at 20°C are as follows: surface tension 28...

Embodiment 2

[0044] Preparation of emulsion-type water-based pigment yellow ink

[0045] The formula of table 2 emulsion type water-based pigment yellow ink

[0046]

[0047]

[0048] Note: Diamond pigment is a self-dispersing pigment purchased from Diamond Dispersions.

[0049] According to the formula of yellow ink in Table 2, surfactant, water-soluble co-solvent and deionized water are mixed at normal temperature, stir 60min under 800rad / min rotating speed with agitator, obtain mixed solution; Continue to stir and add to mixed solution Slowly add the polymer emulsion AS-26080VP, and stir for 20 minutes; finally, slowly add the pigment dispersion while stirring, and continue stirring for 70 minutes, after the various components are fully mixed to form a uniform dispersion system; filter with a 0.2-2 μm microporous membrane , to obtain the emulsion type water-based pigment yellow ink for inkjet printing.

[0050] The physical properties of this ink at 20°C are as follows: surface ...

Embodiment 3

[0052] Preparation of emulsion-type water-based pigment blue ink

[0053] Formulation of table 3 emulsion type water-based pigment blue ink

[0054]

[0055] Note: Diamond pigment is a self-dispersing pigment purchased from Diamond Dispersions.

[0056] According to the formula of blue ink in table 3, surfactant, water-soluble co-solvent and deionized water are mixed at normal temperature, stir 55min under 700rad / min rotating speed with agitator, obtain mixed solution; Continue to stir and add to mixed solution Slowly add polymer emulsion WA-2016 into the medium, stir for 50 minutes, and finally add the pigment dispersion slowly while stirring; continue stirring for 90 minutes, after the various components are fully mixed to form a uniform dispersion system; After filtration, the emulsion-type water-based pigment blue ink for inkjet printing is obtained.

[0057] The physical properties of this ink at 20°C are as follows: surface tension 27.9mN / m (measured by BZY-2 automa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
surface tensionaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to latex-type waterborne pigment oil ink for the inkjet printing of a non-absorbed substrate, which is prepared from the following components in percentage by weight: 1-15 percent of pigment dispersant, 0.01-2.0 percent of surface active agent, 10-40 percent of water-soluble co-solvent, 0.1-30 percent of water-based polymer emulsion and the balance of deionized water. The preparation method comprises the following steps of: stirring and mixing the surface active agent, the water-soluble co-solvent and the deionized water under a normal temperature; then, slowly adding the waterborne polymer emulsion, continuously stirring; and finally, adding the pigment dispersant, fully mixing the contents to form an even dispersing system and filtering the even dispersing system to obtain latex-type waterborne pigment oil ink. The latex-type waterborne pigment oil ink for the inkjet printing has wide range of suitable substrates, is environment-friendly in the oil ink preparation process and the printing process and has good printing smoothness and high accuracy; and printed images on the non-absorbed substrate have excellent resistance to rubbing, scraping, sunshine and water and are suitable for outdoor use.

Description

technical field [0001] The invention belongs to the field of pigment ink for inkjet printing and its preparation and application, in particular to an emulsion-type water-based pigment ink for inkjet printing of non-absorbing substrates and its preparation and application. Background technique [0002] Inkjet printing inks for large inkjet printers can generally be divided into three categories according to their main components: water-based inks, solvent-based inks and UV-curable inks. Currently widely used solvent-based inks generally have disadvantages such as strong odor, high content of volatile organic compounds, and being unfriendly to the environment. Although the weak solvent ink is a relatively environmentally friendly solvent ink, compared with the general solvent ink, many environmental problems are reduced, but not completely resolved. UV-curable inks solve the problems of VOC and ink drying speed, but at the same time, there are disadvantages such as high energ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10B41M1/26C09D11/30
Inventor 李文彬王夏琴李冬梅
Owner 上海英威喷墨科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap