RF plasma transparent conductive film

A transparent conductive film, radio frequency plasma technology, applied in the direction of the conductive layer on the insulating carrier, can solve the problems of scattering, affecting the visual effect and light transmittance of the product, and increasing the manufacturing cost, so as to reduce the surface roughness and improve the chemical quality. Composition and wettability, effect of reducing sheet resistance

Inactive Publication Date: 2011-05-25
SUZHOU HESHENG NEW MATERIALS
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Transparent conductive film is an important material for preparing solar cells, liquid crystal displays and other devices. Transparent conductive film is formed by covering a transparent conductive layer on a transparent substrate. In order to improve the interface adhesion between the substrate and the conductive layer, it is often necessary to A layer of hardened coating is added between the substrate and the transparent conductive layer. The hardened coating needs to be cured under high temperature conditions. However, during the high temperature treatment process, the uneven distribution of molecular structure on the surface of the substrate will cause scattering phenomena, forming " "Rainbow pattern" affects the visual effect and light transmittance of the product. In addition, the various materials and solvents used in the hardened coating also increase the manufacturing cost of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • RF plasma transparent conductive film
  • RF plasma transparent conductive film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Such as figure 1 As shown, the transparent conductive film of radio frequency plasma, the substrate is PET film 1, the front of PET film 1 is coated with hard coating 2, and the surface of hard coating 2 is covered with PE protective film 5; The back of PET film 1 is treated with radio frequency plasma An RF plasma treatment layer 3 is formed, a transparent conductive layer 4 is sputtered on the RF plasma treatment layer 3 , and a PE protective film 6 is covered on the transparent conductive layer 4 .

[0014] The light transmittance of the PET film 1 is above 90%, the dielectric strength is 16.9KV / mm, can block ultraviolet rays, and has low gas and water vapor permeability. The front of the PET film is coated with a hardened coating, and the surface of the hardened coating is covered with a PE protective film; the surface hardness of the hardened coating 2 after hardening reaches more than 3H / 750g, and the light transmittance is > 90%. The hardening process of the hard...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a radio frequency (RF) plasma transparent conductive film. A base material is a polyethylene terephthalate (PET) film, the front face of the PET film is coated with a hardened coating, and the surface of the hardened coating is coated with a polyethylene (PE) protective film; and an RF plasma treatment layer is formed on the back face of the PET film, and a transparent conductive layer is sputtered on the RF plasma treatment layer and is coated with the PE protective film. In the transparent conductive film, one hardened coating is saved, and the RF plasma treatment layer is added, so that a reliable adhesion effect still exists between the transparent conductive layer and the PET film, the resistance value of the transparent conductive film still can keep high properties of uniformity and stability even if the transparent conductive film is subjected to high-temperature tempering, and the transparent conductive film can be widely applied to the aspects of touch panels, electronic games, child teaching machines, intelligent mobile phones, tablet personal computers (PCs) and the like.

Description

technical field [0001] The invention relates to a conductive composite material, in particular to a transparent conductive film prepared by radio frequency plasma technology. Background technique [0002] Transparent conductive film is an important material for preparing solar cells, liquid crystal displays and other devices. Transparent conductive film is formed by covering a transparent conductive layer on a transparent substrate. In order to improve the interface adhesion between the substrate and the conductive layer, it is often necessary to A layer of hardened coating is added between the substrate and the transparent conductive layer. The hardened coating needs to be cured under high temperature conditions. However, during the high temperature treatment process, the uneven distribution of molecular structure on the surface of the substrate will cause scattering phenomena, forming " "Rainbow pattern" further affects the visual effect and light transmittance of the prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01B5/14
Inventor 汪倩文武俊
Owner SUZHOU HESHENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products