Methyl tri(2-chloroethoxy) silane compound and preparation method thereof

A silane compound and chloroethoxy technology, applied in the field of methyltrisilane compound and its preparation, can solve the problems of high price of silicon-based flame retardant plasticizer, limited development and application, etc., and achieve easy large-scale production and low cost , good flame retardant effect

Active Publication Date: 2011-09-07
河南森远科技有限公司
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, phosphorus-based flame-retardant plasticizers have been used, and the development and application of silicon-based flame-retardant plasticizers has been limited due to their high price.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Methyl tri(2-chloroethoxy) silane compound and preparation method thereof
  • Methyl tri(2-chloroethoxy) silane compound and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1 In a 200ml four-necked flask equipped with a stirrer, a thermometer, a dropping funnel, a reflux condenser and a hydrogen chloride absorption device on the mouth of the condenser, add 0.2mol (29.9g) methyltrichlorosilane, Then add 0.6mol (48.3g) of chloroethanol dropwise under the condition of cooling in a water bath, and control the temperature at a rate of addition not to exceed 35°C. After the drop is completed, the temperature is raised to 100°C and the reaction is refluxed for 8 hours. After the melamine is stirred evenly, a small amount of low boiling point matter is removed by distillation under reduced pressure, cooled and filtered to obtain a colorless liquid methyl tris(2-chloroethoxy)silane, and the product yield is 91%. Its decomposition temperature is 235±5°C, and its flash point (open cup) is 195±5°C. Density is 1.333 (20°C), refractive index n D 25 = 1.4558.

Embodiment 2

[0018] Example 2 In a 200ml four-necked flask equipped with a stirrer, a thermometer, a dropping funnel, a reflux condenser and a hydrogen chloride absorption device at the mouth of the condenser, add 0.2mol (29.9g) methyltrichlorosilane, Then add 0.66mol (53.1g) of chloroethanol dropwise under the condition of water bath cooling, and control the temperature not to exceed 35°C with the rate of addition. Melamine, after stirring, remove excessive chlorohydrin (recycling) and a small amount of low boiling point by distillation under reduced pressure, cool and filter to obtain colorless liquid methyl tris (2-chloroethoxy) silane, product yield 95% . Its decomposition temperature is 235±5°C, and its flash point (open cup) is 195±5°C. Density is 1.333 (20°C), refractive index n D 25 = 1.4558.

Embodiment 3

[0019] Example 3 In a 200ml four-neck flask equipped with a stirrer, a thermometer, a dropping funnel, a reflux condenser and a hydrogen chloride absorption device connected to the mouth of the condenser, add 0.2mol (29.9g) methyltrichlorosilane, Then add 0.72mol (58g) of chloroethanol dropwise under the condition of cooling in a water bath, and control the temperature by the rate of addition to not exceed 35°C. After dropping, the temperature is raised to 70°C for reflux for 4 hours. After the hydrogen chloride is released, the reaction is completed, and 1.0g of melamine is added After stirring evenly, excessive chloroethanol (recycled) and a small amount of low boiling point were removed by distillation under reduced pressure, cooled and filtered to obtain a colorless liquid methyl tris (2-chloroethoxy) silane, and the product yield was 97%. Its decomposition temperature is 235±5°C, and its flash point (open cup) is 195±5°C. Density is 1.333 (20°C), refractive index n D 25...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
decomposition temperatureaaaaaaaaaa
flash pointaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to a methyl tri(2-chloroethoxy) silane compound which is used as a silicon-halogen synergistic flame-retardant plasticizer and a preparation method thereof. The methyl tri(2-chloroethoxy) silane compound has the following structural formula: CH3Si(OCH2CH2Cl)3. The preparation method of the methyl tri(2-chloroethoxy) silane compound comprises the following steps: dropwise adding and stirring chloroethanol at a certain molar ratio to methyl trichlorosilane, carrying out a reaction on the chloroethanol and the methyl trichlorosilane for a certain time at a certain temperature, and purifying after finishing hydrogen chloride release and reaction to obtain methyl tri(2-chloroethoxy) silane. The methyl tri(2-chloroethoxy) silane can be used as the good flame-retardant plasticizer, and the process for producing the methyl tri(2-chloroethoxy) silane is simple, has low equipment investment and cost and is easy to realize industrial production.

Description

technical field [0001] The invention relates to a methyl tris(2-chloroethoxy)silane compound and a preparation method thereof. Methyltris(2-chloroethoxy)silane belongs to chlorine-containing organosilicon dual-element synergistic flame retardant and also has good plasticity, which is suitable as a flame retardant for polyvinyl chloride, polyurethane, epoxy resin, unsaturated resin, etc. For burning plasticizers. Background technique [0002] At present, the amount of synthetic polymer materials and plasticizers used for processing is huge. Since most polymer materials are extremely flammable and often cause fires, flame retardants have been developed rapidly. Today, the amount of flame retardant is the second largest additive after the amount of plasticizer. From the perspective of ease of use and the idea of ​​improving the utilization rate of chemical atoms, people always hope that the flame retardancy and plasticizing properties can be reflected in the same compound str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F7/18C08K5/5419
Inventor 王彦林周中凯龚菁
Owner 河南森远科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com