Nitriding salt for low-temperature salt-bath nitriding

A technology of salt bath nitriding and nitriding salt, applied in the field of nitriding salt, which can solve the problems of high applicable temperature of nitriding base salt and unsuitability for low temperature treatment, etc., and achieve the effect of good wear resistance and corrosion resistance of workpieces

Inactive Publication Date: 2012-11-28
SICHUAN UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current salt bath nitriding treatment technology has the following disadvantages: the nitriding base salt is suitable for a relatively high temperature, generally between 520 and 600°C, and is not suitable for low temperature treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitriding salt for low-temperature salt-bath nitriding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The present embodiment 1 nitride salt is composed of the following components by weight: CO (NH 2 ) 2 55%, K 2 CO 3 12%, Na 2 CO 3 6%, Li 2 CO 3 6%, NaCl 10.5%, KCl 10.5%. This embodiment 1 is suitable for use under the nitriding process condition of 450°C, and the nitriding salt bath environment is stable. The metallographic results of nitrided K55 steel are as follows: figure 1 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nitriding salt for low-temperature salt-bath nitriding, which comprises the following components in percentage by weight: 45 to 55 percent of CO(NH2)2, 5 to 15 percent of K2CO3, 3 to 15 percent of Na2CO3, 3 to 15 percent of Li2CO3, 5 to 15 percent of NaCl and 5 to 15 percent of KCl. When the nitriding salt is used, the temperature for common salt-bath nitriding is lowered, and the use temperature range of the conventional nitriding salts is raised. In addition, the nitriding salt also has the advantages that: the deformation of a process workpiece is small; the equipment is simple; environment-friendly operation is realized; and the like.

Description

technical field [0001] The invention relates to a nitriding salt applied to the low-temperature salt bath nitriding process. Background technique [0002] The salt bath nitriding process technology is also called soft nitriding technology. The active nitrogen atoms generated by the decomposition of cyanate radicals penetrate into the workpiece, forming an iron compound layer and a diffusion layer on the surface of the workpiece, thereby improving the wear resistance of iron-based materials. properties, corrosion resistance and fatigue strength. Therefore, salt bath nitriding has been widely used in production practice. However, the currently used salt bath nitriding treatment technology has the following shortcomings: the applicable temperature of nitriding base salt is relatively high, generally between 520 and 600 °C, which is not suitable for low temperature treatment. SUMMARY OF THE INVENTION [0003] The purpose of the invention is to overcome the high applicable te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C8/50
Inventor 王均熊计张太平
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com