Termination adhesive tape and manufacture method thereof

A technology for terminating tapes and production methods, applied in the directions of adhesives, adhesive types, film/sheet adhesives, etc., can solve the problems of corrosion, complex production process, high cost, and achieve good electrolyte resistance. Simple production process and beautiful appearance

Inactive Publication Date: 2011-11-23
东莞市苏粤电子包装材料有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in the production process of lithium-ion batteries, ordinary adhesive tape is used to fix and insulate the tabs and termination parts of lithium-ion batteries. The adhesive tape includes: a base tape and a rubber-type glue layer on the base tape. The adhesive tape has the following disadvantages Disadvantages: high cost, complex manufacturing process, the process has three procedures: primer, back coating, top coating; degumming, poor adhesion, discoloration, and corrosion after three days of immersion in the electrolyte, which cannot fully meet the needs of lithium batteries. Application requirements of battery manufacturers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Termination adhesive tape and manufacture method thereof
  • Termination adhesive tape and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The present invention will be further described below in conjunction with specific embodiments and accompanying drawings.

[0022] refer to figure 1 As shown, this embodiment of the present invention includes a base tape 1 and a glue layer 2 disposed on the base tape 1 .

[0023] The above-mentioned glue layer 2 is an acrylic glue layer, and the specific raw materials and weight of the acrylic glue layer in the present embodiment are:

[0024] Butyl acrylate 3 kg;

[0025] Vinyl acetate 9 kg;

[0026] 52 kg of ethyl acetate;

[0027] 28 kg of isooctyl acrylate;

[0028] Hydroxyethyl methacrylate 1.5 kg;

[0029] Acrylic acid 2 kg;

[0030] 3 kg of toluene;

[0031] Benzoyl Peroxide 0.3 kg.

[0032] An appropriate amount of green pigment and 1.2 kg of polycyanoisolate are added to the acrylic glue layer.

[0033] The steps of the method for making the above-mentioned termination tape are as follows:

[0034] A. Make acrylic glue;

[0035] Use 3 kilograms of to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of adhesive tapes, and particularly relates to a termination adhesive tape and a manufacture method thereof. The termination adhesive tape comprises a base tape and a glue layer located on the base tape, wherein the glue layer is an acrylic glue layer, which is composed of the following raw materials in parts by weight: 1-5 parts of butyl acrylate, 5-12 parts of vinyl acetate, 40-60 parts of ethyl acetate, 20-35 parts of iso-octyl acrylate, 0.5-2 parts of hydroxyethyl methacrylate, 1-3 parts of acrylic acid, 2-4 parts of toluene and 0.1-0.4 part of benzoyl peroxide. The manufacture method sequentially comprises the following steps: A. preparing the acrylic glue: titrating toluene-dissolved benzoyl peroxide used as an initiator to a mixed solution of butyl acrylate, vinyl acetate, ethyl acetate, iso-octyl acrylate, hydroxyethyl methacrylate and acrylic acid at the temperature of 80 DEG C, and ensuring the titration time of 2 hours and self-reaction time of 2.5 hours; and B. applying the acrylic glue on the base tape, sequentially drying, cooling and coiling. The termination adhesive tape provided by the invention has the advantages of low cost, beautiful appearance, simple manufacture process and good electrolyte resistance.

Description

Technical field: [0001] The invention relates to the technical field of adhesive tapes, in particular to a termination adhesive tape and a manufacturing method thereof. Background technique: [0002] Lithium-ion batteries have the advantages of high voltage, high specific energy, many cycle times, and long storage time. They are not only widely used in portable electronic devices such as mobile phones, digital cameras, and laptop computers, but also widely used in electric vehicles, In terms of large and medium-sized electric equipment such as electric bicycles and electric tools, the safety requirements for lithium-ion batteries are getting higher and higher. At present, in the production process of lithium-ion batteries, ordinary adhesive tape is used to fix and insulate the tabs and termination parts of lithium-ion batteries. The adhesive tape includes: a base tape and a rubber-type glue layer on the base tape. The adhesive tape has the following disadvantages Disadvanta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J133/08C08F220/18C08F218/08C08F220/28C08F220/06H01M2/08
CPCY02E60/12Y02E60/10
Inventor 陈鹏
Owner 东莞市苏粤电子包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products