Load type metallocene catalyst and preparation method thereof

A metallocene catalyst and metallocene compound technology are applied in the field of supported metallocene catalysts and their preparation, which can solve the problems of low catalytic activity and achieve the effects of high catalytic activity and stable structure.

Active Publication Date: 2013-08-14
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] The purpose of the present invention is to overcome the problem that the catalytic activity of the supported metallocene catalyst of the prior art is still low, and a kind of highly active supported metallocene catalyst is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Load type metallocene catalyst and preparation method thereof
  • Load type metallocene catalyst and preparation method thereof
  • Load type metallocene catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] According to the preparation method of the present invention, the types of the carrier, methylaluminoxane and metallocene compound have been described above and will not be repeated here.

[0039] The method of loading methylaluminoxane and metallocene compound on the carrier can be various loading methods known in the art, such as dipping and spraying. The method of impregnation can make the solution more fully enter the pores on the carrier, so impregnation is preferred in the present invention.

[0040] The method for preparing the above-mentioned supported metallocene catalyst of the present invention further comprises heating the carrier at a temperature of 300-500°C for 5-20 hours under the protection of an inert gas before loading methylaluminoxane .

[0041] The method for preparing the above-mentioned supported metallocene catalyst of the present invention, for example: may comprise the following steps:

[0042] (1) Thermal activation step, calcining the carrie...

Embodiment 1

[0050] This example is used to illustrate the supported metallocene catalyst and its preparation method according to the present invention.

[0051] 1) The rod-shaped mesoporous material SBA-15 (commercially purchased from Changchun Jilin University High-tech Co., Ltd., the length of the rod is 30-100 microns, and its pore structure parameters are shown in Table 1) was calcined at 400 ° C for 10 hour (thermal activation), remove hydroxyl group and residual moisture, obtain the rod-shaped mesoporous material after thermal activation;

[0052] 2) Transfer 0.4 g of the thermally activated rod-shaped mesoporous material to a 250 ml glass reactor fully replaced by nitrogen, add 10 ml of refined toluene, methyl aluminoxane (MAO, commercially available from Albemarle, USA) 0.47 g of auxiliary agent was stirred at 50° C. for 4 hours. After completion, wash three times with 20 ml of hexane, and finally dry the solid with nitrogen to obtain an alkylaluminoxane / SBA-15 complex carrier (M...

experiment Embodiment 1

[0062] This experimental example is used to illustrate the catalytic activity of the supported catalyst according to the present invention.

[0063] In a 2-liter stainless steel autoclave, replace three times with nitrogen and ethylene respectively, then add 200 milliliters of hexane solvent, raise the temperature of the kettle to 80 ° C, then add the remaining 800 milliliters of hexane solvent, with the addition of hexane, Add 2 ml of 1 mol / L triethylaluminum (TEA) hexane solution, then add 61.7 mg of SBA-15-YIN-1, feed ethylene to raise and maintain the pressure to 1.0 MPa, and react at 70°C for 1 hour . After the end of the polymerization reaction, the polyethylene particle powder was collected and weighed to obtain 68 grams. The efficiency of the catalyst was 1102gPE / (gcat h) (that is, 2.0×10 7 gPE / (mol Zr h)), bulk density (BD) is 0.285g / ml, melt index: MI 2.16 = 0.0001 g / 10 min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a load type metallocene catalyst, which is characterized by comprising a carrier, and a metallocene compound and methylaluminoxane which are on the carrier, wherein the carrier is SBA-15, the metallocene compound has a structure shown by the formula 1, M is one of titanium, zirconium and hafnium, and X is halogen. The load type metallocene catalyst provided by the invention has a stable structure and high catalytic activity. The formula 1 is shown in the accompanying drawing.

Description

technical field [0001] The invention relates to a supported metallocene catalyst and a preparation method thereof. Background technique [0002] The development and application of metallocene catalysts is another major breakthrough in the field of olefin polymerization catalysts after the traditional Ziegler-Natta catalysts. Due to the large amount of methylaluminoxane (MAO) required to achieve high activity of homogeneous metallocene catalysts, the production cost is high, and the obtained polymer has no particle shape, it cannot be used in the widely used slurry method or gas phase polymerization process. use. Moreover, the activity of the metallocene catalyst is very high, and it is prone to localized polymerization at a faster rate during the polymerization reaction, which in turn leads to detonation. [0003] An effective way to solve the above problems is to carry out loading treatment on soluble metallocene catalysts. At present, there are many reports on the suppo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F4/6592C08F4/02C08F10/00C08F10/02
Inventor 谢伦嘉郭顺亢宇邱波王洪涛刘长城赵思源姜健准
Owner CHINA PETROLEUM & CHEM CORP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com