Glue cushion sizing material containing liquid-phase disperse white carbex mixture and preparation method and application thereof

A liquid phase dispersion and white carbon black technology, which is applied in transportation and packaging, tire parts, rolling resistance optimization, etc., can solve the problems of increased tread hysteresis loss, decreased heat generation performance, and poor durability performance

Active Publication Date: 2012-11-07
ZHONGCE RUBBER GRP CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally speaking, the use of carbon black with a high specific surface area in pursuit of wear in the tread of all-steel truck tires will inevitably increase the hysteresis loss of the tread, reduce the heat generation performance, and deteriorate the durability performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glue cushion sizing material containing liquid-phase disperse white carbex mixture and preparation method and application thereof
  • Glue cushion sizing material containing liquid-phase disperse white carbex mixture and preparation method and application thereof
  • Glue cushion sizing material containing liquid-phase disperse white carbex mixture and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Centrifugal concentration of natural rubber latex and silica slurry

[0069] A. Preparation of slurry

[0070] A component

[0071] formula

Composition (%)

Silica slurry (25% content)

85.47

water

13.33

Si69

0.66

stabilizer

0.410

Anti-settling agent

0.020

Dispersant

0.103

[0072] B component

[0073] formula

Composition (%)

Concentrated Natural Rubber Latex

56.31

stabilizer

0.54

water

43.15

[0074] Each was stirred at 1500~2500rpm for 2~5 minutes.

[0075] B. Mix and stir, slowly add component A to component B while stirring at a high speed, the mass ratio of component A to component B is 0.8:1, the stirring speed is 2000~6000rpm, and stir for 10 minutes.

[0076] C. Slowly add 0.3kg of glacial acetic acid to the mixture and solidify instantly.

[0077] D. Press filtration, press on the press, squeeze out...

Embodiment 2

[0084] Using fresh glue and silica paste collected directly from rubber trees

[0085] A. Preparation of slurry

[0086] A component

[0087] formula

Composition (%)

Silica slurry (25% content)

85.47

water

13.33

Si69

0.66

stabilizer

0.410

Anti-settling agent

0.020

Dispersant

0.103

[0088] B component

[0089] formula

Composition (%)

fresh glue

99.056

stabilizer

0.944

water

[0090] Each was stirred at 1500~2500rpm for 2~5 minutes.

[0091] B. Mix and stir, slowly add component A to component B while stirring at a high speed, the mass ratio of component A to component B is 1:1, the stirring speed is 2000~6000rpm, and stir for 10 minutes.

[0092] C. Slowly add 0.3kg of glacial acetic acid to the mixture and solidify instantly.

[0093] D. Press filtration, press on the press, squeeze out part of the liquid, and rec...

Embodiment 3~5

[0100] The pad rubber compound containing the liquid-phase dispersed silica latex mixture, the rubber compound comprises the components in the following table by weight, wherein the comparative example is formed by mixing natural rubber and carbon black, and examples 3 to 5 are The liquid-phase dispersed silica latex mixture obtained in Example 1 or Example 2 (represented by LNSC in the table) is mixed with or without adding natural rubber and carbon black.

[0101]

[0102]

[0103] The pad rubber compound containing the liquid-phase dispersed silica latex mixture of the above-mentioned embodiments 3 ~ 5 is prepared by mixing according to the following method:

[0104] (1) Plasticizing section

[0105] Add liquid-phase dispersed white carbon black latex mixture, stearic acid, nano-zinc oxide, microcrystalline wax, anti-aging agent RD and anti-aging agent 4020, the rotor speed is 45rpm, press the lump and keep it at 140°C, lift the lump and open the feeding door to exhau...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of a tire rubber sizing material, in particular to a glue cushion sizing material and a preparation method and application of the glue cushion sizing material. The glue cushion sizing material containing liquid-phase disperse white carbex mixture is prepared by plasticating and mixing the following components by weight of 50-100 parts of the liquid-phase disperse white carbex mixture, 0-80 parts of nature rubber, 0-30 parts of carbon black, 1.0-3.0 parts of high aromatic hydrocarbon oil, 0.80-1.50 parts of stearic acid, 6.5-8.5 parts of zinc oxide, 2.0-4.0 parts of antiager 4020, 0.60-1.0 part of antiager RD, 1.0-3.0 parts of 204 resin, 3.0-4.5 parts of infusible sulphur OT20, 1.0-2.5 parts of vulcanization accelerator, 0.90-1.50 parts of hardness increasing reinforcing agent 9010 and 0.3-2.0 parts of accelerator D. The glue cushion sizing material adopts the white carbon black to completely or partially replace carbon black to reduce rolling resistance of a tire, improve anti-slippery and wear-resisting properties and produce energy-saving and environment-friendly tires.

Description

technical field [0001] The invention relates to the field of tire rubber compound production, in particular to a cushion rubber compound and its preparation method and application. Background technique [0002] Natural rubber is widely used in tire industry and rubber industry because of its excellent physical and mechanical properties. Due to the extremely high molecular weight of natural rubber (the average molecular weight is about 700,000), using traditional dry mixing, the natural rubber must first be masticated (by mechanical force and high temperature degradation to reduce the molecular weight) and then added in the mechanical shearing process. Required carbon black, white carbon black and other activators, antioxidants, vulcanizing agents. In this process, the macromolecules of natural rubber are severely damaged, so that the strong wear performance decreases. To make up for the decline in strength and wear. Designers traditionally use a large number of hard carbo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L7/02C08K13/06C08K3/36C08K3/04C08K5/09C08K3/22C08K3/06B60C1/00
CPCY02T10/862Y02T10/86
Inventor 楼齐淼徐新建洪佳金振涣
Owner ZHONGCE RUBBER GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com