Aluminum ferric sulfate water purifier and preparation method thereof

A technology of aluminum ferric sulfate and water purifying agent, which is applied in the direction of flocculation/sedimentation water/sewage treatment, etc., can solve the problems of not achieving rapid water purification effect, poor solid-liquid separation effect, affecting water purification effect, etc., to achieve non-toxic Side effects, quick precipitation, quick effect

Active Publication Date: 2012-11-21
刘耀红
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, no oxidizing agent is added in the production process of the current water purifier, and ferrous iron cannot be converted into ferric iron. In the production process, inorganic polymers are formed, and other additives need to be added to form flocs during use. Fast water purification effect, and the solid-liquid separation effect is poor when used, and the water insoluble content is too high, which affects the water purification effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum ferric sulfate water purifier and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of aluminum sulfate ferric salt water purifier, comprising the following steps: a. taking the following raw materials in parts by weight: 200kg-240kg of hydrochloric acid with a concentration of 18%, 340kg-380kg of sulfuric acid with a concentration of 93%, and a concentration of 35 % phosphoric acid 30kg-50kg, aluminum powder 10kg-20kg, iron powder 14kg-18kg, calcium powder 50kg-60kg, calcium aluminate powder containing calcium aluminate 53%WT 140kg-160kg, hydrogen peroxide 2kg-4kg, water 240kg- 260kg; b.: a. take the following raw materials by weight: concentration is 18% hydrochloric acid, concentration is 93% sulfuric acid, concentration is 35% phosphoric acid, aluminum powder, iron powder, calcium powder, calcium aluminate is 53% WT calcium aluminate powder, hydrogen peroxide, water; b. first half of the water is added to the reactor, and then the concentration is 18% hydrochloric acid, the concentration is 93% sulfuric acid, calcium powder, and...

Embodiment 2

[0025] A preparation method of aluminum sulfate ferric salt water purifier, comprising the following steps: a. taking the following raw materials in parts by weight: 205kg-235kg of hydrochloric acid with a concentration of 18%, 350kg-370kg of sulfuric acid with a concentration of 93%, and a concentration of 35 % phosphoric acid 35kg-45kg, aluminum powder 12kg-18kg, iron powder 15kg-17kg, calcium powder 52kg-58kg, calcium aluminate powder containing calcium aluminate 53%WT 145kg-155kg, hydrogen peroxide 2.5kg-3.5kg, water 245kg-255kg; b. First add half of the water into the reactor, then add 18% hydrochloric acid, 93% sulfuric acid, calcium powder, 35% phosphoric acid, aluminum powder, iron powder, aluminum acid Calcium aluminate powder with 53% WT calcium and hydrogen peroxide are poured into the reaction kettle in turn, and stirred for 2.5-4 hours; c. Then add the remaining half of the water into the reaction kettle, and react for 7.5-9 hours while stirring; d. Obtain aluminu...

Embodiment 3

[0027] A kind of preparation method of aluminum sulfate ferric salt water purifying agent, comprises the following steps: a. take by weight following raw material: concentration is 18% hydrochloric acid 220kg, concentration is 93% sulfuric acid 355kg, concentration is 35% phosphoric acid 40kg , aluminum powder 15kg, iron powder 16kg, calcium powder 55kg, the concentration is 53% calcium aluminate powder 150kg, hydrogen peroxide 3kg, water 250kg; b. 93% sulfuric acid, calcium powder, phosphoric acid with a concentration of 35%, aluminum powder, iron powder, calcium aluminate powder containing 53% WT calcium aluminate and hydrogen peroxide are poured into the reaction kettle in turn, stirred for 3 hours; c. Add the remaining half of the water into the reaction kettle, and react for 8 hours while stirring; d. Prepare the aluminum iron sulfate water purifying agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum ferric sulfate water purifier and a preparation method thereof. The aluminum ferric sulfate water purifier is prepared from the following components in parts by weight: 200-240 parts of hydrochloric acid with concentration of 18 percent, 340-380 parts of sulfuric acid with concentration of 93 percent, 30-50 parts of phosphoric acid with concentration of 35 percent, 10-20 parts of aluminum powder, 14-18 parts of iron powder, 50-60 parts of calcium powder, 140-160 parts of calcium aluminate powder containing 53 percent by weight of calcium aluminate, 2-4 parts of hydrogen peroxide and 240-260 parts of water. The aluminum ferric sulfate water purifier has certain killing power for some bacteria and viruses adverse to growth of biochemical bacteria in sewage. When the biochemical bacteria are in a sleep state, the biochemical bacteria can quickly revive by using the aluminum ferric sulfate water purifier; and the aluminum ferric sulfate water purifier has a stronger sterilization effect, so that the biochemical efficiency can be effectively increased and the water quality is changed in a short time.

Description

technical field [0001] The invention belongs to the field of water purifying agents, in particular to an aluminum iron sulfate water purifying agent, and also relates to a preparation method of the water purifying agent. Background technique [0002] Aluminum and iron polymer inorganic polymer water purifiers are a new type of chemical industry researched and developed from the 1970s to the 1990s, which has played a great role in improving people's quality of life and improving the environment. There are many types of water purifiers, and the production processes are different. However, no oxidizing agent is added in the production process of the current water purifier, and ferrous iron cannot be converted into ferric iron. In the production process, inorganic polymers are formed, and other additives need to be added to form flocs during use. Fast water purification effect, and the solid-liquid separation effect is poor when used, and the water insoluble content is too high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/52
Inventor 刘耀红
Owner 刘耀红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com