A nickel-based alloy, alloy powder technology, applied in welding medium, welding equipment, metal processing equipment and other directions, can solve problems such as poor effect, and achieve the effect of improving service life and good workmanship
Active Publication Date: 2015-04-01
TIANJIN ZHUJIN METAL SURFACE ENG MATERIALTECH DEV
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Corrosion-resistant nickel-based alloys have many patents in the world, such as Hastelloy C276, Inconel 625, etc., which are used in drilling tools for oil and gas wells with high sulfur content in my country, but the effect is still not good
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] A corrosion-resistant nickel-based alloy surfacing powder, calculated in % by weight, is composed of the following components:
[0017] Cr 20 Mo 10 Co 6 Zr 0.5 RE 0.5 Mn 1 Si 2
[0018] B 1.5 Ni balance Impurity content 0.05
Embodiment 2
[0020] A corrosion-resistant nickel-based alloy surfacing powder, calculated in % by weight, is composed of the following components:
[0021] Cr 24 Mo 12 Co 7 Zr 0.8 RE 0.8 Mn 1.2 Si 2.3
[0022] B 1.8 Ni balance Impurity content 0.05
Embodiment 3
[0024] A corrosion-resistant nickel-based alloy surfacing powder, calculated in % by weight, is composed of the following components:
[0025] Cr 28 Mo 14 Co 8 Zr l RE 1 Mn 1.5 Si 2.5
[0026] B 2 Ni balance Impurity content 0.05
[0027] In Examples 1, 2 and 3, Ni:Co is 5:1-10:1; Cr:Mo is 2:1; in the process of making alloy powder, Mn, Zr and RE are added one by one in this order.
[0028] The corrosion-resistant nickel-based alloy surfacing powder of the invention is prepared by smelting in an induction heating furnace and a high-purity nitrogen atomization method. The powder morphology is silver-gray, and the spherical particle powder has good fluidity (14s / 50g) and high bulk density (4.6g / cm2). 3 ), the oxygen content is ≤500PPM, and the preferable particle size range is 212-20μm.
[0029] The comparison test results of Example 2 of the corrosion-resistant nickel-based alloy surfacing powder of the present invention and Hastelloy C276 and Inconel 625 alloys in the same ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a corrosion-resistant nickel-base alloy overlay welding powder which comprises the following components in percentage by weight: 20-28% of Cr, 10-14% of Mo, 6-8% of Co, 1-1.5% of Mn, 0.5-1% of Zr, 0.5-1% of Re, 2-2.5% of Si, 1.5-2% of B, at most 0.05% of impurity and the balance of Ni. Due to the adoption of the technical scheme, the strong corrosion resistance of the prepared nickel-base alloy overlay welding powder is much better than that of any existing other alloy powder in the patent at home and abroad; and the corrosion-resistant nickel-base alloy overlay welding powder is suitable for plasma arc overlay welding, has favorable laser cladding processibility, completely satisfies the requirement of corrosion resistance for sulfur-containing high oil gas well drilling tools, and greatly prolongs the service life of the drilling tool.
Description
technical field [0001] The invention belongs to the technical field of metal alloy powder for surface coating, in particular to a corrosion-resistant nickel-based alloy surfacing powder. Background technique [0002] In the existing environment of sulfide-containing oil and gas wells, the drilling tools are very prone to sulfide stress corrosion. With the increase of the concentration of NaCl in the drilling fluid and other acidic substances, the corrosion rate will be significantly accelerated, and the H 2 S, CO 2 The corrosion of drilling tools by , molten salt, etc. is mutually promoting. Corrosion-resistant nickel-based alloys have many patents in the world, such as Hastelloy C276, Inconel 625, etc., which are used in drilling tools for oil and gas wells with high sulfur content in my country, but the effect is still poor. In order to prolong the service life of the drilling tool, the anti-corrosion coating material on the surface of the drilling tool developed by the ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/03B23K35/32
Inventor 钱铸
Owner TIANJIN ZHUJIN METAL SURFACE ENG MATERIALTECH DEV